The effect of rolling processing on the microstructure,electrochemical property and anti-corrosion property of Al-Mg-Sn-Bi-Ga-In alloy anode in alkaline solution(80℃,Na2SnO3+5 mol/L NaOH)was analyzed by the chronopot...The effect of rolling processing on the microstructure,electrochemical property and anti-corrosion property of Al-Mg-Sn-Bi-Ga-In alloy anode in alkaline solution(80℃,Na2SnO3+5 mol/L NaOH)was analyzed by the chronopotentiometry (E-T curves),hydrogen collection tests and modern microstructure analysis.The results show that when the rolling temperature is 370℃,the electrochemical activity of Al anode decreases gradually with the increase of pass deformation in rolling,while the anti-corrosion property is improved in the beginning and then declined rapidly.When the pass deformation of rolling is 40%,the Al anode has good electrochemical activity as good as the anti-corrosion property and with the increase of rolling temperature,both electrochemical activity and anti-corrosion property of Al anode increase first and then decrease.When the rolling temperature is 420 ℃,the aluminum alloy anode has the most negative electrode potential of about-1.521 V(vs Hg/HgO)and the lowest hydrogen evolution rate of 0.171 6 mL/(min·cm2).The optimum comprehensive performance of Al alloy anode is obtained.展开更多
基金Project(50721003) supported by the Creative Research Group of National Natural Science Foundation of China
文摘The effect of rolling processing on the microstructure,electrochemical property and anti-corrosion property of Al-Mg-Sn-Bi-Ga-In alloy anode in alkaline solution(80℃,Na2SnO3+5 mol/L NaOH)was analyzed by the chronopotentiometry (E-T curves),hydrogen collection tests and modern microstructure analysis.The results show that when the rolling temperature is 370℃,the electrochemical activity of Al anode decreases gradually with the increase of pass deformation in rolling,while the anti-corrosion property is improved in the beginning and then declined rapidly.When the pass deformation of rolling is 40%,the Al anode has good electrochemical activity as good as the anti-corrosion property and with the increase of rolling temperature,both electrochemical activity and anti-corrosion property of Al anode increase first and then decrease.When the rolling temperature is 420 ℃,the aluminum alloy anode has the most negative electrode potential of about-1.521 V(vs Hg/HgO)and the lowest hydrogen evolution rate of 0.171 6 mL/(min·cm2).The optimum comprehensive performance of Al alloy anode is obtained.