Nickel-based superalloys with and without Co by partial replacement of W were prepared using double vacuum melting.A comparison of the oxidation in air and hot corrosion behaviors under molten 75 wt.%Na2 SO4+25 wt.%Na...Nickel-based superalloys with and without Co by partial replacement of W were prepared using double vacuum melting.A comparison of the oxidation in air and hot corrosion behaviors under molten 75 wt.%Na2 SO4+25 wt.%NaCl at 900℃were systematically investigated.The results showed that partial replacement of W with Co promoted the formation of chromia scale and consequently decreased the oxidation rate.Besides,the addition of Co also retarded the internal oxidation/nitridation of Al and consequently promoted the growth of Al_(2) O3 scale,which further decreased the scaling rate and improved the adhesion of scale.Moreover,the addition of Co also further improved the hot corrosion resistance under molten Na2 SO4-NaCl salts.展开更多
基金financial supports from the Natural Science Foundation of Shandong Province,China(No.ZR2019MEE107)Shandong Jiaotong University“Climbing”Research Innovation Team Program,China(No.SDJTC1802)PhD Scientific Research Foundation of Shandong Jiaotong University,China(No.BS2018005)。
文摘Nickel-based superalloys with and without Co by partial replacement of W were prepared using double vacuum melting.A comparison of the oxidation in air and hot corrosion behaviors under molten 75 wt.%Na2 SO4+25 wt.%NaCl at 900℃were systematically investigated.The results showed that partial replacement of W with Co promoted the formation of chromia scale and consequently decreased the oxidation rate.Besides,the addition of Co also retarded the internal oxidation/nitridation of Al and consequently promoted the growth of Al_(2) O3 scale,which further decreased the scaling rate and improved the adhesion of scale.Moreover,the addition of Co also further improved the hot corrosion resistance under molten Na2 SO4-NaCl salts.