The deformation zone of CONFORM extrusion was divided into primary gripping zone,gripping zone,conical expansion chamber zone,cylindrical zone and sizing zone of die,and corresponding force equilibrium equations were ...The deformation zone of CONFORM extrusion was divided into primary gripping zone,gripping zone,conical expansion chamber zone,cylindrical zone and sizing zone of die,and corresponding force equilibrium equations were established using the Slab method.The deformation force formulae of CONFORM machine at any wrapping angle with an expansion chamber were obtained.Experiment on pure aluminum and Al-5%Ti-1%B alloy was conducted on the CONFORM machine self-designed.The resistance to deformation of Al-5%Ti-1%B alloy at the deformation temperature of 400℃ and the strain rate of 3.07 s-1 was measured to be 50 MPa using Gleeble-1500 thermal simulation machine.The calculation results of deformation forces for CONFORM process with an expansion chamber for pure aluminum and Al-5%Ti-1%B alloy were given.The experimental CONFORM radial force is in agreement with the radial force obtained by theoretical formula.展开更多
To determine the extrusion force of pipe fabricated by continuous casting and extrusion (CASTEX) using an expansion combination die, the metallic expansion combination die was divided into diversion zone, expansion zo...To determine the extrusion force of pipe fabricated by continuous casting and extrusion (CASTEX) using an expansion combination die, the metallic expansion combination die was divided into diversion zone, expansion zone, flow dividing zone, welding chamber, and sizing zone, and the corresponding stress formulae in various zones were established using the slab method. The deformation zones of CASTEX groove were divided into liquid and semisolid zone, solid primary gripping zone, and solid gripping zone, and the formulae of pipe extrusion forces were established. Experiments were carried out on the self-designed CASTEX machine to obtain the aluminum pipe and measure its extrusion force using the expansion combination die. The experimental results of radial extrusion force for aluminum pipe are in good agreement with the calculated ones.展开更多
A continuous semisolid extending extrusion （CSEP） method was proposed. Temperature field and metal flow during continuous semisolid extending extrusion process of 6201 alloy tube were studied. During the process, th...A continuous semisolid extending extrusion （CSEP） method was proposed. Temperature field and metal flow during continuous semisolid extending extrusion process of 6201 alloy tube were studied. During the process, the temperature in the roll-shoe cavity decreases gradually, and the isothermal lines of the alloy deviate from the shoe side to the work roll side in the roll–shoe gap. Metal flow velocity decreases gradually from the surface of the work roll to the surface of the shoe. In the extrusion mould, alloy temperature decreases gradually from the entrance to the exit and from the center to the sidewall of the mould. The extending cavity is radially filled with the alloy. The flow lines in the tube corresponding to the centers of the splitflow orifices and the welding gaps are dense, and the corresponding harness values are high; there are 8 transitional bands between them. In order to prepare 6201 alloy tubes with good surface quality, the pouring temperature from 750 ℃ to 780 ℃ was suggested.展开更多
基金Projects(51034002,50974038,50274020) supported by the National Natural Science Foundation of China
文摘The deformation zone of CONFORM extrusion was divided into primary gripping zone,gripping zone,conical expansion chamber zone,cylindrical zone and sizing zone of die,and corresponding force equilibrium equations were established using the Slab method.The deformation force formulae of CONFORM machine at any wrapping angle with an expansion chamber were obtained.Experiment on pure aluminum and Al-5%Ti-1%B alloy was conducted on the CONFORM machine self-designed.The resistance to deformation of Al-5%Ti-1%B alloy at the deformation temperature of 400℃ and the strain rate of 3.07 s-1 was measured to be 50 MPa using Gleeble-1500 thermal simulation machine.The calculation results of deformation forces for CONFORM process with an expansion chamber for pure aluminum and Al-5%Ti-1%B alloy were given.The experimental CONFORM radial force is in agreement with the radial force obtained by theoretical formula.
基金Projects(51334006,50274020)supported by the National Natural Science Foundation of China
文摘To determine the extrusion force of pipe fabricated by continuous casting and extrusion (CASTEX) using an expansion combination die, the metallic expansion combination die was divided into diversion zone, expansion zone, flow dividing zone, welding chamber, and sizing zone, and the corresponding stress formulae in various zones were established using the slab method. The deformation zones of CASTEX groove were divided into liquid and semisolid zone, solid primary gripping zone, and solid gripping zone, and the formulae of pipe extrusion forces were established. Experiments were carried out on the self-designed CASTEX machine to obtain the aluminum pipe and measure its extrusion force using the expansion combination die. The experimental results of radial extrusion force for aluminum pipe are in good agreement with the calculated ones.
基金Projects (51034002, 50974038) supported by the National Natural Science Foundation of ChinaProject (132002) supported by the Fok Ying Tong Education FoundationProject (2011CB610405) supported by National Basic Research Program of China
文摘A continuous semisolid extending extrusion （CSEP） method was proposed. Temperature field and metal flow during continuous semisolid extending extrusion process of 6201 alloy tube were studied. During the process, the temperature in the roll-shoe cavity decreases gradually, and the isothermal lines of the alloy deviate from the shoe side to the work roll side in the roll–shoe gap. Metal flow velocity decreases gradually from the surface of the work roll to the surface of the shoe. In the extrusion mould, alloy temperature decreases gradually from the entrance to the exit and from the center to the sidewall of the mould. The extending cavity is radially filled with the alloy. The flow lines in the tube corresponding to the centers of the splitflow orifices and the welding gaps are dense, and the corresponding harness values are high; there are 8 transitional bands between them. In order to prepare 6201 alloy tubes with good surface quality, the pouring temperature from 750 ℃ to 780 ℃ was suggested.