Studies on texture and microstructure evolution in hot extruded Al 6061 aluminium alloy reinforced with uncoated and nickel coated SiC p were carried out by electron backscattered diffraction technique.Textures of bot...Studies on texture and microstructure evolution in hot extruded Al 6061 aluminium alloy reinforced with uncoated and nickel coated SiC p were carried out by electron backscattered diffraction technique.Textures of both the alloy and its composite with nickel coated SiC p do exhibit strong β fiber with its axis parallel to the direction of extrusion.In addition to the dominant cube texture（001） 100,fully recrystallized grains with partially equiaxed structure have been observed in the alloy reinforced with uncoated SiC p.The recrystallization texture of this composite can be attributed to the particle stimulated nucleation（PSN） due to the presence of SiC p with size less than 5 μm.Under these conditions,the low value of Zener-Hollomon,Z（～1012s-1） confirms that PSN is one of the dominant mechanisms for recrystallization and is governed by formation of deformation zone rather than stored energy.展开更多
基金granting financial assistance to carry out this work which is a part of research project No.SR/S3/ME/019/2004-SERC
文摘Studies on texture and microstructure evolution in hot extruded Al 6061 aluminium alloy reinforced with uncoated and nickel coated SiC p were carried out by electron backscattered diffraction technique.Textures of both the alloy and its composite with nickel coated SiC p do exhibit strong β fiber with its axis parallel to the direction of extrusion.In addition to the dominant cube texture（001） 100,fully recrystallized grains with partially equiaxed structure have been observed in the alloy reinforced with uncoated SiC p.The recrystallization texture of this composite can be attributed to the particle stimulated nucleation（PSN） due to the presence of SiC p with size less than 5 μm.Under these conditions,the low value of Zener-Hollomon,Z（～1012s-1） confirms that PSN is one of the dominant mechanisms for recrystallization and is governed by formation of deformation zone rather than stored energy.