Oleic acid (denoted as OA) surface-caped lanthanum borate nanorods, abbreviated as OA/LaBO3·H2O, were prepared via hydrothermal method. The microstructures of the as-prepared OA/LaBO3·H2O nanorods were chara...Oleic acid (denoted as OA) surface-caped lanthanum borate nanorods, abbreviated as OA/LaBO3·H2O, were prepared via hydrothermal method. The microstructures of the as-prepared OA/LaBO3·H2O nanorods were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques. The friction and wear properties of OA/LaBO3·H2O nanorods in rapeseed oil were evaluated with a four-ball tribo-tester. The results show that the as-prepared OA/LaBO3·H2O nanorods are hydrophobic and display nanorods morphology with uniform diameter of about 50 nm and length of up to 500 nm. In the meantime, OA/LaBO3·H2O nanorods can obviously improve the anti-wear and friction-reducing capacities of rapeseed oil, and the optimal anti-wear and friction-reducing properties of rapeseed oil were obtained at an OA/LaBO3·H2O content of 1% (mass fraction).展开更多
A BN-containing additive,the boron and nitrogen modified rapeseed oil (abbreviated as BNR),was prepared by chemical modification of rapeseed oil with boric and nitrous compounds.The friction and wear performances of t...A BN-containing additive,the boron and nitrogen modified rapeseed oil (abbreviated as BNR),was prepared by chemical modification of rapeseed oil with boric and nitrous compounds.The friction and wear performances of the AZ91D magnesium alloy against the GCr15 bearing steel under lubrication of rapeseed oil containing BNR were evaluated on a SRV tribotester.The topography and chemical species of the worn surfaces of magnesium alloy were analyzed by a scanning electron microscope (SEM) and an X-ray photoelectron spectroscope (XPS),respectively.The test results indicated that the friction and wear of the magnesium alloy-steel tribomates could be effectively reduced by incorporating BNR into the rapeseed oil lubricant.The friction coefficients and the wear scars of magnesium alloy decreased with an increasing content of BNR.The surface lubricated with the BNR-doped rapeseed oil demonstrated less wear as compared with that lubricated with neat rapeseed oil.The enhanced anti-wear and friction-reducing abilities of rapeseed oil provided by BNR in the lubrication of magnesium alloy against steel were ascribed to the formation of a composite boundary lubrication film due to the strong adsorption of BNR and rapeseed oil onto the lubricated surfaces and their tribochemical reactions with magnesium alloy.展开更多
The work described in this paper is part of the European Project IBIOLAB, trying to find suitable metalworking fluids based on vegetable oils, such us High Oleic Sunflower Oil （HOSO）. In this paper, the performance ...The work described in this paper is part of the European Project IBIOLAB, trying to find suitable metalworking fluids based on vegetable oils, such us High Oleic Sunflower Oil （HOSO）. In this paper, the performance of the newly developed IBIOLAB water based formulations supplied by SOGELUB and LUBRIX is analyzed and compared with reference Mineral and Synthetic cutting fluids Innovative characterization tests at laboratory scale （3 ball abrasion tests, grinding simulation tests, Tapping torque test） in real grinding machines in combination with advanced characterization techniques （residual stress measurements monitored by RX to predict formation of cracks）, have been used for screening the performance of the emulsions.展开更多
基金Project(50975282)supported by the National Natural Science Foundation of China
文摘Oleic acid (denoted as OA) surface-caped lanthanum borate nanorods, abbreviated as OA/LaBO3·H2O, were prepared via hydrothermal method. The microstructures of the as-prepared OA/LaBO3·H2O nanorods were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques. The friction and wear properties of OA/LaBO3·H2O nanorods in rapeseed oil were evaluated with a four-ball tribo-tester. The results show that the as-prepared OA/LaBO3·H2O nanorods are hydrophobic and display nanorods morphology with uniform diameter of about 50 nm and length of up to 500 nm. In the meantime, OA/LaBO3·H2O nanorods can obviously improve the anti-wear and friction-reducing capacities of rapeseed oil, and the optimal anti-wear and friction-reducing properties of rapeseed oil were obtained at an OA/LaBO3·H2O content of 1% (mass fraction).
基金the financial support from the National Natural Science Foundation of China (project No. 50975282)
文摘A BN-containing additive,the boron and nitrogen modified rapeseed oil (abbreviated as BNR),was prepared by chemical modification of rapeseed oil with boric and nitrous compounds.The friction and wear performances of the AZ91D magnesium alloy against the GCr15 bearing steel under lubrication of rapeseed oil containing BNR were evaluated on a SRV tribotester.The topography and chemical species of the worn surfaces of magnesium alloy were analyzed by a scanning electron microscope (SEM) and an X-ray photoelectron spectroscope (XPS),respectively.The test results indicated that the friction and wear of the magnesium alloy-steel tribomates could be effectively reduced by incorporating BNR into the rapeseed oil lubricant.The friction coefficients and the wear scars of magnesium alloy decreased with an increasing content of BNR.The surface lubricated with the BNR-doped rapeseed oil demonstrated less wear as compared with that lubricated with neat rapeseed oil.The enhanced anti-wear and friction-reducing abilities of rapeseed oil provided by BNR in the lubrication of magnesium alloy against steel were ascribed to the formation of a composite boundary lubrication film due to the strong adsorption of BNR and rapeseed oil onto the lubricated surfaces and their tribochemical reactions with magnesium alloy.
文摘The work described in this paper is part of the European Project IBIOLAB, trying to find suitable metalworking fluids based on vegetable oils, such us High Oleic Sunflower Oil （HOSO）. In this paper, the performance of the newly developed IBIOLAB water based formulations supplied by SOGELUB and LUBRIX is analyzed and compared with reference Mineral and Synthetic cutting fluids Innovative characterization tests at laboratory scale （3 ball abrasion tests, grinding simulation tests, Tapping torque test） in real grinding machines in combination with advanced characterization techniques （residual stress measurements monitored by RX to predict formation of cracks）, have been used for screening the performance of the emulsions.