In order to evaluate the accumulative of tensile strain in the process of fatigue failure, the digital image correlation（DIC） method was utilized to characterize the tensile strain development of asphalt mixtures in...In order to evaluate the accumulative of tensile strain in the process of fatigue failure, the digital image correlation（DIC） method was utilized to characterize the tensile strain development of asphalt mixtures in the indirect tensile（IDT）fatigue test. Three typical hot mix asphalt（HMA） mixtures with varying nominal maximum aggregate sizes were tested at four stress levels. During the tests, a digital camera was mounted to capture the displacement/strain fields on the surface of the specimen by recording the real-time change of speckle position. The results indicate that the vertical deformation curve can barely evaluate the fatigue performance accurately due to the non-negligible local deflection near the loading point. However, based on the analysis of strain fields,the optimal fatigue cracking zone is determined as a 40mm×40mm rectangle in the middle of the specimens. Also, a reasonable fatigue model based on the tensile strain curves calculated by DIC is proposed to predict the fatigue lives of asphalt mixtures.展开更多
文摘In order to evaluate the accumulative of tensile strain in the process of fatigue failure, the digital image correlation（DIC） method was utilized to characterize the tensile strain development of asphalt mixtures in the indirect tensile（IDT）fatigue test. Three typical hot mix asphalt（HMA） mixtures with varying nominal maximum aggregate sizes were tested at four stress levels. During the tests, a digital camera was mounted to capture the displacement/strain fields on the surface of the specimen by recording the real-time change of speckle position. The results indicate that the vertical deformation curve can barely evaluate the fatigue performance accurately due to the non-negligible local deflection near the loading point. However, based on the analysis of strain fields,the optimal fatigue cracking zone is determined as a 40mm×40mm rectangle in the middle of the specimens. Also, a reasonable fatigue model based on the tensile strain curves calculated by DIC is proposed to predict the fatigue lives of asphalt mixtures.