The localized micro-galvanic corrosion process and the kinetic information of Mg-(7,9)Al-1Fe-x Nd alloys were investigated by in situ observation under electrochemical control and in situ atomic force microscopy(AFM)i...The localized micro-galvanic corrosion process and the kinetic information of Mg-(7,9)Al-1Fe-x Nd alloys were investigated by in situ observation under electrochemical control and in situ atomic force microscopy(AFM)in an electrolyte environment.The results revealed that the formation of the Nd-rich phase in alloys resulted in a decrease in the Volta potential difference from~400 m V(AlFe3/α-Mg)to~220 mV(Nd-rich/α-Mg),reducing the corrosion products around the cathodic phase and corrosion current density of the microscale area.The addition of Nd significantly improved the corrosion resistance,mainly due to the suppression of the micro-galvanic corrosion between the second phases and substrate.Finally,the corrosion mechanism of Mg-(7,9)Al-1Fe-x Nd alloys was discussed based on in situ observations and electrochemical results.展开更多
The evolution of mechanical properties,localized corrosion resistance of a high purity Al-Zn-Mg-Cu alloy during non-isothermal aging(NIA)was investigated by hardness test,electrical conductivity test,tensile test,inte...The evolution of mechanical properties,localized corrosion resistance of a high purity Al-Zn-Mg-Cu alloy during non-isothermal aging(NIA)was investigated by hardness test,electrical conductivity test,tensile test,intergranular corrosion test,exfoliation corrosion test,slow strain rate tensile test and electrochemical test,and the mechanism has been discussed based on microstructure examination by optical microscopy,electron back scattered diffraction,scanning electron microscopy and scanning transmission electron microscopy.The NIA treatment includes a heating stage from 40℃to 180℃with a rate of 20℃/h and a cooling stage from 180℃to 40℃with a rate of 10℃/h.The results show that the hardness and strength increase rapidly during the heating stage of NIA since the increasing temperature favors the nucleation and the growth of strengthening precipitates and promotes the transformation of Guinier-Preston(GPI)zones toη'phase.During the cooling stage,the sizes ofη'phase increase with a little change in the number density,leading to a further slight increase of the hardness and strength.As NIA proceeds,the corroded morphology in the alloy changes from a layering feature to a wavy feature,the maximum corrosion depth decreases,and the reason has been analyzed based on the microstructural and microchemical feature of precipitates at grain boundaries and subgrain boundaries.展开更多
On May 12, 2008, a magnitude 8.0 earthquake hit Wenchuan County, Sichuan Province resulted in great loss of life and properties.Besides, abundant landslides and slope failures were triggered in the most seriously hit ...On May 12, 2008, a magnitude 8.0 earthquake hit Wenchuan County, Sichuan Province resulted in great loss of life and properties.Besides, abundant landslides and slope failures were triggered in the most seriously hit areas and caused disastrous damages to infrastructures and public facilities.Moreover, abundant unstable slopes caused by the quake have the potential to cause damages for a considerable long period of time.The variety of these slopes and the corresponding treatments are connected with the topographical and geological conditions of the sites.It is decided to document and identify some of these major slope instabilities caused by the earthquake and their treatments.The paper shows the condition of a road in Dujiangyan through in situ explorations.The case history showed significant implications to the reconstruction of the quake-hit regions and future disaster prevention and management works.展开更多
基金financial support from the National Natural Science Foundation of China(No.51961026)。
文摘The localized micro-galvanic corrosion process and the kinetic information of Mg-(7,9)Al-1Fe-x Nd alloys were investigated by in situ observation under electrochemical control and in situ atomic force microscopy(AFM)in an electrolyte environment.The results revealed that the formation of the Nd-rich phase in alloys resulted in a decrease in the Volta potential difference from~400 m V(AlFe3/α-Mg)to~220 mV(Nd-rich/α-Mg),reducing the corrosion products around the cathodic phase and corrosion current density of the microscale area.The addition of Nd significantly improved the corrosion resistance,mainly due to the suppression of the micro-galvanic corrosion between the second phases and substrate.Finally,the corrosion mechanism of Mg-(7,9)Al-1Fe-x Nd alloys was discussed based on in situ observations and electrochemical results.
基金Project(202302AB080024)supported by the Department of Science and Technology of Yunnan Province,China。
文摘The evolution of mechanical properties,localized corrosion resistance of a high purity Al-Zn-Mg-Cu alloy during non-isothermal aging(NIA)was investigated by hardness test,electrical conductivity test,tensile test,intergranular corrosion test,exfoliation corrosion test,slow strain rate tensile test and electrochemical test,and the mechanism has been discussed based on microstructure examination by optical microscopy,electron back scattered diffraction,scanning electron microscopy and scanning transmission electron microscopy.The NIA treatment includes a heating stage from 40℃to 180℃with a rate of 20℃/h and a cooling stage from 180℃to 40℃with a rate of 10℃/h.The results show that the hardness and strength increase rapidly during the heating stage of NIA since the increasing temperature favors the nucleation and the growth of strengthening precipitates and promotes the transformation of Guinier-Preston(GPI)zones toη'phase.During the cooling stage,the sizes ofη'phase increase with a little change in the number density,leading to a further slight increase of the hardness and strength.As NIA proceeds,the corroded morphology in the alloy changes from a layering feature to a wavy feature,the maximum corrosion depth decreases,and the reason has been analyzed based on the microstructural and microchemical feature of precipitates at grain boundaries and subgrain boundaries.
基金supported by the 973 Program of China (Grant No. 2008CB425803the Open Fund of the Key Laboratory of Marine Geology and Environment, China Academy of Sciences (Grant No. MGE2008KG04)the Open Fund of the Key Laboratory of Mountain Hazards and Surface Process, CAS.
文摘On May 12, 2008, a magnitude 8.0 earthquake hit Wenchuan County, Sichuan Province resulted in great loss of life and properties.Besides, abundant landslides and slope failures were triggered in the most seriously hit areas and caused disastrous damages to infrastructures and public facilities.Moreover, abundant unstable slopes caused by the quake have the potential to cause damages for a considerable long period of time.The variety of these slopes and the corresponding treatments are connected with the topographical and geological conditions of the sites.It is decided to document and identify some of these major slope instabilities caused by the earthquake and their treatments.The paper shows the condition of a road in Dujiangyan through in situ explorations.The case history showed significant implications to the reconstruction of the quake-hit regions and future disaster prevention and management works.