A new composite two component grout comprised of modified urea-formaldehyde resin and cement was formulated to take account of the advantages and disadvantages of both the cement grout and the chem- ical grout. The ne...A new composite two component grout comprised of modified urea-formaldehyde resin and cement was formulated to take account of the advantages and disadvantages of both the cement grout and the chem- ical grout. The new grout is designed for water blocking by reinforcing as well as seepage control by bore grouting. The A component consists of a modified urea-formaldehyde resin A component, some cement, and some water. The B component is an alkaline coagulant. An orthogonal test of four factors at three lev- els showed that gel time increased with increased water content and with urea-formaldehyde resin con- tent. Gel time decreased at increased levels of alkaline coagulant. The A component of this new composite grout is stable over time. A mixed cross-over test showed that as the volume ratio of A to B increases the gel time falls at first but then increases. The solid strength decreases with increasing levels of the B com- ponent. The solid strength increases over time and becomes stable by the 28th day after mixing. The vis- cosity increases with increasing levels of resin A component. The increase is exponential and may be fit to： μ = 8.162e0.0286x.展开更多
基金the Graduate Developing Innovation Project of Jiangsu Province of China (No. CXZZ11-0306)the Major State Basic Research and Development Program of China (No.2007CB209400)
文摘A new composite two component grout comprised of modified urea-formaldehyde resin and cement was formulated to take account of the advantages and disadvantages of both the cement grout and the chem- ical grout. The new grout is designed for water blocking by reinforcing as well as seepage control by bore grouting. The A component consists of a modified urea-formaldehyde resin A component, some cement, and some water. The B component is an alkaline coagulant. An orthogonal test of four factors at three lev- els showed that gel time increased with increased water content and with urea-formaldehyde resin con- tent. Gel time decreased at increased levels of alkaline coagulant. The A component of this new composite grout is stable over time. A mixed cross-over test showed that as the volume ratio of A to B increases the gel time falls at first but then increases. The solid strength decreases with increasing levels of the B com- ponent. The solid strength increases over time and becomes stable by the 28th day after mixing. The vis- cosity increases with increasing levels of resin A component. The increase is exponential and may be fit to： μ = 8.162e0.0286x.