The viscoplastic friction and nanostructure formation mechanism of laser-clad Co-based coating were studied by rotary friction between laser-clad Co-Cr-Ni-Mo coating and WC-Co rod.The friction coefficient,friction int...The viscoplastic friction and nanostructure formation mechanism of laser-clad Co-based coating were studied by rotary friction between laser-clad Co-Cr-Ni-Mo coating and WC-Co rod.The friction coefficient,friction interface temperature and axial displacement—time curves during rotary friction process were measured.The results showed that all the curves firstly experienced rising stage and then steady stage.The rising stage corresponded to sliding friction while the steady stage corresponded to viscoplastic friction.After viscoplastic friction processing,three typical zones of viscoplastic deformation zone,thermo-mechanically affected zone,and original laser-clad zone can be observed successively from the friction surface to the interior.The viscoplastic deformation significantly crushed the network M23C7 phase in original laser-clad zone and made it dispersively distributed with equiaxial shape and in nano-scale.The viscoplastic zone,in width of 37-131 μm,is mainly characterized by refined M23C7 and α-Co phase with grain size bellow 50 nm,and even a small quantity of amorphous.Thus,the hardness of viscoplastic zone about HV997 was improved compared with the hardness of original laser-clad zone about HV600.展开更多
Nanoparticles monolayer formation by spin coating is considered to be a simple, fast and inexpensive nanopatteming technique However, the parameters that govern the overall growth process in this technique are not com...Nanoparticles monolayer formation by spin coating is considered to be a simple, fast and inexpensive nanopatteming technique However, the parameters that govern the overall growth process in this technique are not completely quantified and techniques for the controlled and continuous growth of close packed monolayer particle arrays without defects need to be developed. In this paper, an ordered particle array formation process is analyzed theoretically, employing material flux balance and parti- cle-subjected forces balance, based on the film thickness model of spin coating and evaporation rate law. A series of experi- ments were conducted using silica particle suspensions with various particle volume fractions and different spin speeds. The results show that the spin speed should match the particle volume fraction to meet the requirements of material flux and particles movement in order to obtain a close packed monolayer film. The formation mechanism of fabrication defects involving particle agglomeration and uncontrollable voids were analyzed qualitatively based on crystal growth theory, and validation experiments were performed. The formation of highly uniform close-packed monolayer films was demonstrated and the condi- tion requirements for achieving monolayer nanoparticles array with good quality presented.展开更多
基金Project(51101126) supported by the National Natural Science Foundation of ChinaProjects(20110491684,2012T50817) supported by the China Postdoctoral Science FoundationProject(20110942K) supported by the Open Fund of State Key Laboratory of Powder Metallurgy,China
文摘The viscoplastic friction and nanostructure formation mechanism of laser-clad Co-based coating were studied by rotary friction between laser-clad Co-Cr-Ni-Mo coating and WC-Co rod.The friction coefficient,friction interface temperature and axial displacement—time curves during rotary friction process were measured.The results showed that all the curves firstly experienced rising stage and then steady stage.The rising stage corresponded to sliding friction while the steady stage corresponded to viscoplastic friction.After viscoplastic friction processing,three typical zones of viscoplastic deformation zone,thermo-mechanically affected zone,and original laser-clad zone can be observed successively from the friction surface to the interior.The viscoplastic deformation significantly crushed the network M23C7 phase in original laser-clad zone and made it dispersively distributed with equiaxial shape and in nano-scale.The viscoplastic zone,in width of 37-131 μm,is mainly characterized by refined M23C7 and α-Co phase with grain size bellow 50 nm,and even a small quantity of amorphous.Thus,the hardness of viscoplastic zone about HV997 was improved compared with the hardness of original laser-clad zone about HV600.
基金supported by the National Natural Science Foundation of China(Grant Nos.51375381,51575427 and 51675422)the 2015 Overall Planning Innovation Project Foundation of Shaanxi Province(Grant No.2015KTCQ01-36)
文摘Nanoparticles monolayer formation by spin coating is considered to be a simple, fast and inexpensive nanopatteming technique However, the parameters that govern the overall growth process in this technique are not completely quantified and techniques for the controlled and continuous growth of close packed monolayer particle arrays without defects need to be developed. In this paper, an ordered particle array formation process is analyzed theoretically, employing material flux balance and parti- cle-subjected forces balance, based on the film thickness model of spin coating and evaporation rate law. A series of experi- ments were conducted using silica particle suspensions with various particle volume fractions and different spin speeds. The results show that the spin speed should match the particle volume fraction to meet the requirements of material flux and particles movement in order to obtain a close packed monolayer film. The formation mechanism of fabrication defects involving particle agglomeration and uncontrollable voids were analyzed qualitatively based on crystal growth theory, and validation experiments were performed. The formation of highly uniform close-packed monolayer films was demonstrated and the condi- tion requirements for achieving monolayer nanoparticles array with good quality presented.