A facile and efficient method has been developed for microencapsulation of metal oxide nanoparticles in polyurea via interfacial polymerization of toluene-2,4-diisocyanate and H20 through the atomizing emulsification ...A facile and efficient method has been developed for microencapsulation of metal oxide nanoparticles in polyurea via interfacial polymerization of toluene-2,4-diisocyanate and H20 through the atomizing emulsification approach. The resultant microcapsules were well-shaped and uniform sphere with diameter ranging from 2 to 6 um. Thermogravimetry （TG） and differential scanning calorimetry （DSC） curves revealed that the microcapsules showed good thermal stability （no decomposition observed under 245℃）. Besides, the microencapsulated TiC2 has been used as an efficient catalyst for photocatalytic degradation of methyl orange. Furthermore, the photocatalysis of immobilized TiC2 could be enhanced by introducing UV absorbing agent to the wall of microcapsules.展开更多
A stable silica sol with 3-5 nm in diameter, which can form homogeneous film without crack, was prepared and characterized. Then, the inorganic-organic hybrid aqueous dispersion composed of such a silica sol and an em...A stable silica sol with 3-5 nm in diameter, which can form homogeneous film without crack, was prepared and characterized. Then, the inorganic-organic hybrid aqueous dispersion composed of such a silica sol and an emulsion of styrene （St） and acrylate （Ac） copolymer was prepared and the hybrid effect between the silica sol and poly（St-co-Ac） was observed by Fourier transform infra-red （FT-IR） spectroscope. The toughness of the film prepared by this kind of hybrid aqueous dispersion was excellent, as it was enhanced appreciably by commixing with a small amount of poly（St-co-Ac） emulsion. Some amino-polysiloxane modified hybrid aqueous dispersions were also prepared and the properties of the modified dispersions and their films were investigated. The experimental results showed that the film prepared with such an amino-polysiloxane modified hybrid dispersion exhibited excellent hydrophobicity and low surface energy after heat treatment for 1.5 h, during which the formation of the graft copolymer was observed. The surface energy of this film decreases as a result of the enrichment of siloxane segments on the film surface.展开更多
Polydimethylsiloxane （PDMS）, tetraethoxysilane （TEOS）, ethyl alcohol （EtOH） and deionized water were main raw materials to prepare silicone-modified hybrid thin films using sol-gel method. The effect of the cont...Polydimethylsiloxane （PDMS）, tetraethoxysilane （TEOS）, ethyl alcohol （EtOH） and deionized water were main raw materials to prepare silicone-modified hybrid thin films using sol-gel method. The effect of the contents of H2O and PDMS on thin films was studied. When the volume ratio of H20 to TEOS is 0.5, the optimum quality of thin films is obtained. And the gelation time is affected slightly by H20 content. Uniform thin films are obtained when the volume ratio of PDMS to TEOS is 0.2. Yet, the sol would be inactive in 6 d. Various properties of thin films were studied, including hardness, adhesive quality, hydrophobic property, corrosion protection property, and abrasion resistance. Test results show that the pencil hardness is generally 3-6 H, and adhesive quality achieves the highest standard of 0. When the sintering temperature is below 400℃, the contact angle is about 95° and hydrophobic films are obtained. The abrasion resistance of thin films is better than that of aluminum alloy when the sintering temperature is higher than 300℃. And the excellent corrosion protective effect is obtained by single-layer coating when the sintering temperature is higher than 400℃.展开更多
The ultra fine (<200 nm) inorganic solids (BS) were separated from bitumen which was washed by toluene and centrifugated at 2000 rpm. The result of PAS FTIR and image of TEM showed that the structure of BS particle...The ultra fine (<200 nm) inorganic solids (BS) were separated from bitumen which was washed by toluene and centrifugated at 2000 rpm. The result of PAS FTIR and image of TEM showed that the structure of BS particles was smiliar to that of kaolinite clay. On the surface of BS, both toluene insoluble organic matter and structural OH group are detected at the same time. The surface characteristics imparted a bi-wettable nature to the BS. As a result, the BS is able to stabilize fine water emulsion in the bitumen phase. The organic matter associated with BS is a possible factor of the fouling on catalyst and equipment.展开更多
A poly (St-co-BA) latex was successfully synthesized by using an organic-inorganic hybrid compound (OIHC), an aliphatic carboxylate sodium/nano-silica composite, as the emulsifier, and investigated by particle size an...A poly (St-co-BA) latex was successfully synthesized by using an organic-inorganic hybrid compound (OIHC), an aliphatic carboxylate sodium/nano-silica composite, as the emulsifier, and investigated by particle size analyzer, transmission electron microscope (TEM), optical contact angle measurement (OCA) and dynamic mechanical analyzer (DMA). It was found that the protective agent, sodium polyacrylate (PA),could obviously improve the polymerization stability and the functional monomer, glycidyl methacrylate (GMA), could enhance the store stability of the latex. The particle size of poly(St-co-BA) latex decreased and then leveled off as OIHC content increased. TEM shows that the prepared polymers were actually organic-inorganic nanocomposites, and these films have better waterproof property than those prepared by traditional poly(St-co-BA) latex or organic silicone modified poly(St-co-BA) latex. The nanocomposite polymer has much higher glass transition temperature than organic silicone modified poly(St-co-BA) polymer containing the same organic silicone content.展开更多
基金Supported by the National Natural Science Foundation of China （20576045） and the Program for New Century Excellent Talents in University （NCET-06-740）.
文摘A facile and efficient method has been developed for microencapsulation of metal oxide nanoparticles in polyurea via interfacial polymerization of toluene-2,4-diisocyanate and H20 through the atomizing emulsification approach. The resultant microcapsules were well-shaped and uniform sphere with diameter ranging from 2 to 6 um. Thermogravimetry （TG） and differential scanning calorimetry （DSC） curves revealed that the microcapsules showed good thermal stability （no decomposition observed under 245℃）. Besides, the microencapsulated TiC2 has been used as an efficient catalyst for photocatalytic degradation of methyl orange. Furthermore, the photocatalysis of immobilized TiC2 could be enhanced by introducing UV absorbing agent to the wall of microcapsules.
基金Supported by Science and Technology Commission of Shanghai Municipality (No. 0212nm008).
文摘A stable silica sol with 3-5 nm in diameter, which can form homogeneous film without crack, was prepared and characterized. Then, the inorganic-organic hybrid aqueous dispersion composed of such a silica sol and an emulsion of styrene （St） and acrylate （Ac） copolymer was prepared and the hybrid effect between the silica sol and poly（St-co-Ac） was observed by Fourier transform infra-red （FT-IR） spectroscope. The toughness of the film prepared by this kind of hybrid aqueous dispersion was excellent, as it was enhanced appreciably by commixing with a small amount of poly（St-co-Ac） emulsion. Some amino-polysiloxane modified hybrid aqueous dispersions were also prepared and the properties of the modified dispersions and their films were investigated. The experimental results showed that the film prepared with such an amino-polysiloxane modified hybrid dispersion exhibited excellent hydrophobicity and low surface energy after heat treatment for 1.5 h, during which the formation of the graft copolymer was observed. The surface energy of this film decreases as a result of the enrichment of siloxane segments on the film surface.
基金supported partly by the School of Mechanical,Electronic and Control Engineering,Beijing Jiaotong university,China
文摘Polydimethylsiloxane （PDMS）, tetraethoxysilane （TEOS）, ethyl alcohol （EtOH） and deionized water were main raw materials to prepare silicone-modified hybrid thin films using sol-gel method. The effect of the contents of H2O and PDMS on thin films was studied. When the volume ratio of H20 to TEOS is 0.5, the optimum quality of thin films is obtained. And the gelation time is affected slightly by H20 content. Uniform thin films are obtained when the volume ratio of PDMS to TEOS is 0.2. Yet, the sol would be inactive in 6 d. Various properties of thin films were studied, including hardness, adhesive quality, hydrophobic property, corrosion protection property, and abrasion resistance. Test results show that the pencil hardness is generally 3-6 H, and adhesive quality achieves the highest standard of 0. When the sintering temperature is below 400℃, the contact angle is about 95° and hydrophobic films are obtained. The abrasion resistance of thin films is better than that of aluminum alloy when the sintering temperature is higher than 300℃. And the excellent corrosion protective effect is obtained by single-layer coating when the sintering temperature is higher than 400℃.
基金Financially supported by the Opening Fund of National Key Laboratory of State Heavy Oil University of Petroleum+1 种基金 Beijing (2003-04) and the Scientific Research Foundation (SRF) for the Returned Overseas Chinese Scholars (ROCS) State Education Minis
文摘The ultra fine (<200 nm) inorganic solids (BS) were separated from bitumen which was washed by toluene and centrifugated at 2000 rpm. The result of PAS FTIR and image of TEM showed that the structure of BS particles was smiliar to that of kaolinite clay. On the surface of BS, both toluene insoluble organic matter and structural OH group are detected at the same time. The surface characteristics imparted a bi-wettable nature to the BS. As a result, the BS is able to stabilize fine water emulsion in the bitumen phase. The organic matter associated with BS is a possible factor of the fouling on catalyst and equipment.
基金Supported by the National "863" Project (No. 2001 AA 320206)and Shanghai Nano Special Foundation(No. 0120nm034).
文摘A poly (St-co-BA) latex was successfully synthesized by using an organic-inorganic hybrid compound (OIHC), an aliphatic carboxylate sodium/nano-silica composite, as the emulsifier, and investigated by particle size analyzer, transmission electron microscope (TEM), optical contact angle measurement (OCA) and dynamic mechanical analyzer (DMA). It was found that the protective agent, sodium polyacrylate (PA),could obviously improve the polymerization stability and the functional monomer, glycidyl methacrylate (GMA), could enhance the store stability of the latex. The particle size of poly(St-co-BA) latex decreased and then leveled off as OIHC content increased. TEM shows that the prepared polymers were actually organic-inorganic nanocomposites, and these films have better waterproof property than those prepared by traditional poly(St-co-BA) latex or organic silicone modified poly(St-co-BA) latex. The nanocomposite polymer has much higher glass transition temperature than organic silicone modified poly(St-co-BA) polymer containing the same organic silicone content.