In several countries, the residual RHA （rice husk ash） has been produced in rice processing industries or in thermoelectric plants that use rice husk to generate heat and/or electrical energy, usually without burnin...In several countries, the residual RHA （rice husk ash） has been produced in rice processing industries or in thermoelectric plants that use rice husk to generate heat and/or electrical energy, usually without burning process control. This causes a reduction in the amorphous silica content of residual RHA, which distinguishes them from the RHA produced according to controlled burning process, which is totally amorphous and considered a highly reactive pozzolan. In this paper, the hydration products and the porous structure of binders paste were studied by replacing, in weight of 5%, 10% and 20% of Portland cement OPC （ordinary Portland cement）, by residual RHAs named A and B, which have high and low content of amorphous silica, respectively, using microstructure evaluation techniques as XRD （X-ray diffraction）, TG （thermogravimetric） tests and MIP （mercury intrusion porosimetry）. A reducing the size of the pores of the pastes was observed according to the increase of content replacement of RHA A and RHA B.展开更多
文摘In several countries, the residual RHA （rice husk ash） has been produced in rice processing industries or in thermoelectric plants that use rice husk to generate heat and/or electrical energy, usually without burning process control. This causes a reduction in the amorphous silica content of residual RHA, which distinguishes them from the RHA produced according to controlled burning process, which is totally amorphous and considered a highly reactive pozzolan. In this paper, the hydration products and the porous structure of binders paste were studied by replacing, in weight of 5%, 10% and 20% of Portland cement OPC （ordinary Portland cement）, by residual RHAs named A and B, which have high and low content of amorphous silica, respectively, using microstructure evaluation techniques as XRD （X-ray diffraction）, TG （thermogravimetric） tests and MIP （mercury intrusion porosimetry）. A reducing the size of the pores of the pastes was observed according to the increase of content replacement of RHA A and RHA B.