Characterization of microstructure and strain response in Ti-6Al-4V plasma welding deposited material by combined EBSD and in-situ tensile test

Additive layer manufacturing （ALM） of aerospace grade titanium components shows great promise in supplying a cost-effective alternative to the conventional production routes. Complex microstructures comprised of columnar remnants of directionally solidifiedβ-grains, with interior inhabited by colonies of finerα-plate structures, were found in samples produced by layered plasma welding of Ti-6Al-4V alloy. The application of in-situ tensile tests combined with rapid offline electron backscatter diffraction （EBSD） analysis provides a powerful tool for understanding and drawing qualitative correlations between microstructural features and deformation characteristics. Non-uniform deformation occurs due to a strong variation in strain response between colonies and across columnar grain boundaries. Prismatic and basal slip systems are active, with the prismatic systems contributing to the most severe deformation through coarse and widely spaced slip lines. Certain colonies behave as microstructural units, with easy slip transmission across the entire colony. Other regions exhibit significant deformation mismatch, with local build-up of strain gradients and stress concentration. The segmentation occurs due to the growth morphology and variant constraints imposed by the columnar solidification structures through orientation relationships, interface alignment and preferred growth directions. Tensile tests perpendicular to columnar structures reveal deformation localization at columnar grain boundaries. In this work connections are made between the theoretical macro- and microstructural growth mechanisms and the observed microstructure of the Ti-6Al-4V alloy, which in turn is linked to observations during in-situ tensile tests.

Corrosion behavior of Mg−Li alloys:A review

It has been known that the lack of excellent corrosion resistance is the key problem restricting the wide application of Mg−Li alloys.Based on a quantity of literature about corrosion behavior of Mg−Li alloys,this review elaborates the factors affecting the corrosion behavior of Mg−Li alloys and the processing methods for improving corrosion resistance.The corrosion characteristics of Mg−Li alloys are described firstly.Then,it is explained that the grain size,orientation,second phase,and surface film strongly influence corrosion performance,which can be tailored by alloying,plastic deformation,and heat treatment.Further in-depth discussion about the corrosion mechanisms for Mg−Li alloys was also presented.Finally,important points of improving corrosion resistance are suggested.

Prediction of grain scale plasticity of NiTi shape memory alloy based on crystal plasticity finite element method

Grain scale plasticity of NiTi shape memory alloy(SMA)during uniaxial compression deformation at 400℃was investigated through two-dimensional crystal plasticity finite element simulation and corresponding analysis based on the obtained orientation data.Stress and strain distributions of the deformed NiTi SMA samples confirm that there exhibits a heterogeneous plastic deformation at grain scale.Statistically stored dislocation(SSD)density and geometrically necessary dislocation(GND)density were further used in order to illuminate the microstructure evolution during uniaxial compression.SSD is responsible for sustaining plastic deformation and it increases along with the increase of plastic strain.GND plays an important role in accommodating compatible deformation between individual grains and thus it is correlated with the misorientation between neighboring grains,namely,a high GND density corresponds to large misorientation between grains and a low GND density corresponds to small misorientation between grains.

Microstructure and mechanical properties evolution of 65Cu-35Zn brass tube during cyclic rotating−bending process

The cyclic rotating−bending(CRB)processes under different deformation conditions were carried out to refine the microstructure and improve the mechanical properties of the 65Cu−35Zn brass tubes.The microstructure and the mechanical properties in the axial direction of the tubes after the CRB process were studied with the OM,EBSD and conventional tensile test.To obtain the accumulated effective plastic strain of the tube during the CRB process,the FEM simulation was also executed.The results show that the average grain size decreases with the increase of rotation time at RT,and with the decrease of bending angle at 200℃.With the increase of accumulated effective plastic strain during the CRB process,the reduction rate of average grain size of the brass tube increases,the tensile strength of the brass tube increases in wave shape and the elongation increases first and then sharply decreases.