The Fe-based coatings in powder form were deposited on a steel type E335 by flame spraying technique.The effects of the post heat treatment on the microstructure and the mechanical properties of sprayed coatings were ...The Fe-based coatings in powder form were deposited on a steel type E335 by flame spraying technique.The effects of the post heat treatment on the microstructure and the mechanical properties of sprayed coatings were studied.Post heat treatment was conducted in a furnace in air at 623 K,823 K and 1023 K for 1 h and then cooled in air.The results showed that with the increase of annealing temperature,the microstructure of coating treated at 823 K and 1023 K had several changes as follows:the reduction of porosity,formation of carbides and oxides.It was found that the solid solution FCC(Fe,Ni),intermetallic compound AlFe3 and carbides[Fe,C]were the main phases for coatings as-sprayed and treated at 623 K and while iron carbide,molybdenum carbide and oxide as Fe3O4 became the main phases and reinforced the solid solution FCC(Fe,Ni)phase for annealed coatings at 823 K.However,it was observed the disappearance of molybdenum carbide and oxide Fe3O4 at 1023 K.The coating annealed at 823 K exhibited an excellent wear resistance than the as-sprayed and annealed coatings at 623 K and 1023 K and shows the lower wear rate than another coating treated or as sprayed.展开更多
Anodic coatings were prepared by micro-arc oxidation on AZ91HP magnesium alloys in a base solution containing 10 g/L NaOH and 12 g/L phytic acid with addition of 0-8 g/L sodium tungstate.The effects of sodium tungstat...Anodic coatings were prepared by micro-arc oxidation on AZ91HP magnesium alloys in a base solution containing 10 g/L NaOH and 12 g/L phytic acid with addition of 0-8 g/L sodium tungstate.The effects of sodium tungstate on the coating thickness, mass gain,surface morphology and corrosion resistance were studied by eddy current instrument,electronic scales,scanning electron microscope and immersion tester.With the addition of sodium tungstate,the electrolytic conductivity increases and the final voltage decreases.The sodium tungstate has a minor effect on the coating thickness,but lightens the coating color.With increasing sodium tungstate concentration,the size of micropores on the coatings is enlarged and the corrosion resistance of the anodized samples decreases.展开更多
文摘The Fe-based coatings in powder form were deposited on a steel type E335 by flame spraying technique.The effects of the post heat treatment on the microstructure and the mechanical properties of sprayed coatings were studied.Post heat treatment was conducted in a furnace in air at 623 K,823 K and 1023 K for 1 h and then cooled in air.The results showed that with the increase of annealing temperature,the microstructure of coating treated at 823 K and 1023 K had several changes as follows:the reduction of porosity,formation of carbides and oxides.It was found that the solid solution FCC(Fe,Ni),intermetallic compound AlFe3 and carbides[Fe,C]were the main phases for coatings as-sprayed and treated at 623 K and while iron carbide,molybdenum carbide and oxide as Fe3O4 became the main phases and reinforced the solid solution FCC(Fe,Ni)phase for annealed coatings at 823 K.However,it was observed the disappearance of molybdenum carbide and oxide Fe3O4 at 1023 K.The coating annealed at 823 K exhibited an excellent wear resistance than the as-sprayed and annealed coatings at 623 K and 1023 K and shows the lower wear rate than another coating treated or as sprayed.
基金Projects(GJJ08363,GJJ09573)supported by the Scientific Research Fund of Jiangxi Provincial Education Department,China
文摘Anodic coatings were prepared by micro-arc oxidation on AZ91HP magnesium alloys in a base solution containing 10 g/L NaOH and 12 g/L phytic acid with addition of 0-8 g/L sodium tungstate.The effects of sodium tungstate on the coating thickness, mass gain,surface morphology and corrosion resistance were studied by eddy current instrument,electronic scales,scanning electron microscope and immersion tester.With the addition of sodium tungstate,the electrolytic conductivity increases and the final voltage decreases.The sodium tungstate has a minor effect on the coating thickness,but lightens the coating color.With increasing sodium tungstate concentration,the size of micropores on the coatings is enlarged and the corrosion resistance of the anodized samples decreases.