The semi-solid slurry of AZ91 D magnesium alloy was prepared by gas bubbling process.The effect of processing parameters,including gas flow rate,cooling rate and stirring end temperature,on microstructure of AZ91 D se...The semi-solid slurry of AZ91 D magnesium alloy was prepared by gas bubbling process.The effect of processing parameters,including gas flow rate,cooling rate and stirring end temperature,on microstructure of AZ91 D semi-solid slurry was investigated.With increasing the gas flow rate from 0 to 5 L/min,the average size of primary α-Mg particles decreases from 119.1 to77.2μm and the average shape factor increases continuously from 0.1 to 0.596.The formation of non-dendritic primary α-Mg particles during gas bubbling is the result of combined effects of dendrite fragmentation and copious nucleation.With increasing the cooling rate from 3.6 to 14.6℃/min,the average particle size of primary α-Mg phase decreases from 105.0 to 68.1μm while the average shape factor peaks at 9.1℃/min.Both high and low cooling rates can induce dendritic growth of primary α-Mg particles.Changing the stirring end temperature from 590 to 595℃ has little effect on the average size and shape factor of primary α-Mg particles in AZ91 D semi-solid slurry.The insensitivity of semi-solid microstructures to the stirring end temperature is attributed to the sufficient quantity of primary particles formed in the melt.展开更多
A system for in vitro investigation of ultrasound contrast agent＇s enhancement effect is presented and evaluated. It includes the digital B-mode ultrasound scanner Belson3000A, the tissue-mimicking ultrasound phantom...A system for in vitro investigation of ultrasound contrast agent＇s enhancement effect is presented and evaluated. It includes the digital B-mode ultrasound scanner Belson3000A, the tissue-mimicking ultrasound phantoms and the software which is used for image quantitative analysis. The linear range, optimal settings and repeatability of the system are assessed and explored by scanning the ultrasound phantoms with different reflective intensities. The measurements are performed under an acoustic power from 4.8 to 12.3 mW, the scanner centre frequency is 3.5 MH and the gain setting is 50 dB. Both a self-made surfactant encapsulated microbubble and a commercial ultrasound contrast agent are scanned. The results show that the pixel intensity of ultrasonic images increases with the increase in the sound power, and for the stronger reflective phantoms of more particles, the increasing trend is much more evident. The system is optimal for evaluating the microbubble contrast agents＇ enhancement effects. It presents a simple, effective and real-time means for characterizing the enhancement ability of microbubbles.展开更多
基金Project(51275295)supported by the National Natural Science Foundation of ChinaProjects(20120073120011,20130073110052)supported by the Research Fund for the Doctoral Program of Higher Education of China
文摘The semi-solid slurry of AZ91 D magnesium alloy was prepared by gas bubbling process.The effect of processing parameters,including gas flow rate,cooling rate and stirring end temperature,on microstructure of AZ91 D semi-solid slurry was investigated.With increasing the gas flow rate from 0 to 5 L/min,the average size of primary α-Mg particles decreases from 119.1 to77.2μm and the average shape factor increases continuously from 0.1 to 0.596.The formation of non-dendritic primary α-Mg particles during gas bubbling is the result of combined effects of dendrite fragmentation and copious nucleation.With increasing the cooling rate from 3.6 to 14.6℃/min,the average particle size of primary α-Mg phase decreases from 105.0 to 68.1μm while the average shape factor peaks at 9.1℃/min.Both high and low cooling rates can induce dendritic growth of primary α-Mg particles.Changing the stirring end temperature from 590 to 595℃ has little effect on the average size and shape factor of primary α-Mg particles in AZ91 D semi-solid slurry.The insensitivity of semi-solid microstructures to the stirring end temperature is attributed to the sufficient quantity of primary particles formed in the melt.
基金The National Basic Research Program of China (973Program) (No.2006CB933206)the National Natural Science Foundation of China(No.50872021,60725101)
文摘A system for in vitro investigation of ultrasound contrast agent＇s enhancement effect is presented and evaluated. It includes the digital B-mode ultrasound scanner Belson3000A, the tissue-mimicking ultrasound phantoms and the software which is used for image quantitative analysis. The linear range, optimal settings and repeatability of the system are assessed and explored by scanning the ultrasound phantoms with different reflective intensities. The measurements are performed under an acoustic power from 4.8 to 12.3 mW, the scanner centre frequency is 3.5 MH and the gain setting is 50 dB. Both a self-made surfactant encapsulated microbubble and a commercial ultrasound contrast agent are scanned. The results show that the pixel intensity of ultrasonic images increases with the increase in the sound power, and for the stronger reflective phantoms of more particles, the increasing trend is much more evident. The system is optimal for evaluating the microbubble contrast agents＇ enhancement effects. It presents a simple, effective and real-time means for characterizing the enhancement ability of microbubbles.