Photocatalytic degradation of gaseous pollutants on Bi-based semiconductors under solar lightirradiation has attracted significant attention.However,their application in gaseous straight-chainalkane purification is st...Photocatalytic degradation of gaseous pollutants on Bi-based semiconductors under solar lightirradiation has attracted significant attention.However,their application in gaseous straight-chainalkane purification is still rare.Here,a series of Bi/BiOBr composites were solvothermally synthe-sized and applied in solar-light-driven photocatalytic degradation of gaseous n-hexane.The charac-terization results revealed that both increasing number of functional groups of alcohol solvent(from methanol and ethylene glycol to glycerol)and solvothermal temperature(from 160 and 180to 200℃)facilitated the in-situ formation of metallic Bi nanospheres on BiOBr nanoplates withexposed(110)facets.Meanwhile,chemical bonding between Bi and BiOBr was observed on theseexposed facets that resulted in the formation of surface oxygen vacancy.Furthermore,the synergis-tic effect of optimum surface oxygen vacancy on exposed(110)facets led to a high visible light re-sponse,narrow band gap,great photocurrent,low recombination rate of the charge carriers,andstrong·O2-and h*formation,all of which resulted in the highest removal efficiency of 97.4%within120 min of 15 ppmv of n-hexane on Bi/BiOBr.Our findings efficiently broaden the application ofBi-based photocatalysis technology in the purification of gaseous straight-chain pollutants emittedby the petrochemical industry.展开更多
In the present work,samples of Al-Si-Cu piston alloy after T6 heat treatment were exposed for 2 h at temperatures ranging from 400 to 550°C.The evolution of surface roughness and microstructure of the alloy durin...In the present work,samples of Al-Si-Cu piston alloy after T6 heat treatment were exposed for 2 h at temperatures ranging from 400 to 550°C.The evolution of surface roughness and microstructure of the alloy during thermal exposure was studied by combination methods of roughness profiles,optical and scanning electron microscopy as well as XRD analysis.It is found that the roughness and mass of the alloy increase with the raise of the thermal exposure temperature,and the increasing rates of them are slow as the exposure temperature is below 500°C,but accelerates abruptly when the temperature is higher than 500°C.The variation of surface roughness of the alloy is closely related to phase transformation and oxidation during the thermal exposure.展开更多
文摘Photocatalytic degradation of gaseous pollutants on Bi-based semiconductors under solar lightirradiation has attracted significant attention.However,their application in gaseous straight-chainalkane purification is still rare.Here,a series of Bi/BiOBr composites were solvothermally synthe-sized and applied in solar-light-driven photocatalytic degradation of gaseous n-hexane.The charac-terization results revealed that both increasing number of functional groups of alcohol solvent(from methanol and ethylene glycol to glycerol)and solvothermal temperature(from 160 and 180to 200℃)facilitated the in-situ formation of metallic Bi nanospheres on BiOBr nanoplates withexposed(110)facets.Meanwhile,chemical bonding between Bi and BiOBr was observed on theseexposed facets that resulted in the formation of surface oxygen vacancy.Furthermore,the synergis-tic effect of optimum surface oxygen vacancy on exposed(110)facets led to a high visible light re-sponse,narrow band gap,great photocurrent,low recombination rate of the charge carriers,andstrong·O2-and h*formation,all of which resulted in the highest removal efficiency of 97.4%within120 min of 15 ppmv of n-hexane on Bi/BiOBr.Our findings efficiently broaden the application ofBi-based photocatalysis technology in the purification of gaseous straight-chain pollutants emittedby the petrochemical industry.
基金Project(DLBF2018-KY-JS-066-J)supported by China North Engine Research InstituteProject(XAGDXJJ17008)supported by the Principal Fund of Xi’an Technological University,ChinaProjects(19JK0400,19JK0402)supported by the Education Fund of Shaanxi Province,China。
文摘In the present work,samples of Al-Si-Cu piston alloy after T6 heat treatment were exposed for 2 h at temperatures ranging from 400 to 550°C.The evolution of surface roughness and microstructure of the alloy during thermal exposure was studied by combination methods of roughness profiles,optical and scanning electron microscopy as well as XRD analysis.It is found that the roughness and mass of the alloy increase with the raise of the thermal exposure temperature,and the increasing rates of them are slow as the exposure temperature is below 500°C,but accelerates abruptly when the temperature is higher than 500°C.The variation of surface roughness of the alloy is closely related to phase transformation and oxidation during the thermal exposure.