Au/3DOM（three-dimensionally ordered macroporous） Al2O3 and Au/CeO2/3DOM Al2O3 were prepared using a reduction-deposition method and characterized using scanning electron microscopy,N2 adsorption-desorption,X-ray dif...Au/3DOM（three-dimensionally ordered macroporous） Al2O3 and Au/CeO2/3DOM Al2O3 were prepared using a reduction-deposition method and characterized using scanning electron microscopy,N2 adsorption-desorption,X-ray diffraction,transmission electron microscopy,ultraviolet-visible spectroscopy,temperature-programmed hydrogen reduction,and X-ray photoelectron spectroscopy.Au nanoparticles of similar sizes were well dispersed and supported on the inner walls of uniform macropores.The norminal Au loading is 2%.Al-Ce-O solid solution in CeO2/3DOM Al2O3 catalysts can be formed due to the incorporation of Al^3＋ ions into the ceria lattice,which causes the creation of extrinsic oxygen vacancies.The extrinsic oxygen vacancies improved the oxygen-transport properties.The strong metal-support interactions between Au and CeO2 increased the amount of active oxygen on the Au nanoparticle surfaces,and this promoted soot oxidation.The activities of the Au-based catalysts were higher than those of the supports（Al2O3 or CeO2/3DOM Al2O3） at low temperature.Au/CeO2/3DOM Al2O3 had the highest catalytic activity for soot combustion,with T（10）,T（50）,and T（90） values of 273,364,and 412℃,respectively.展开更多
基金supported by the National Natural Science Foundation of China (21477146,21303263)the National High Technology Research and Development Program of China (863 Program,2015AA034603)+2 种基金Beijing Nova Program (Z141109001814072)the Specialized Research Fund for the Doctoral Program of Higher Education of China (20130007120011)the Science Foundation of China University of Petroleum-Beijing (YJRC-2013-13,2462013BJRC003)~~
文摘Au/3DOM（three-dimensionally ordered macroporous） Al2O3 and Au/CeO2/3DOM Al2O3 were prepared using a reduction-deposition method and characterized using scanning electron microscopy,N2 adsorption-desorption,X-ray diffraction,transmission electron microscopy,ultraviolet-visible spectroscopy,temperature-programmed hydrogen reduction,and X-ray photoelectron spectroscopy.Au nanoparticles of similar sizes were well dispersed and supported on the inner walls of uniform macropores.The norminal Au loading is 2%.Al-Ce-O solid solution in CeO2/3DOM Al2O3 catalysts can be formed due to the incorporation of Al^3＋ ions into the ceria lattice,which causes the creation of extrinsic oxygen vacancies.The extrinsic oxygen vacancies improved the oxygen-transport properties.The strong metal-support interactions between Au and CeO2 increased the amount of active oxygen on the Au nanoparticle surfaces,and this promoted soot oxidation.The activities of the Au-based catalysts were higher than those of the supports（Al2O3 or CeO2/3DOM Al2O3） at low temperature.Au/CeO2/3DOM Al2O3 had the highest catalytic activity for soot combustion,with T（10）,T（50）,and T（90） values of 273,364,and 412℃,respectively.