The title compound Mn 3(BTC) 2(DMF) 4 (BTC=1,3,5-benzenetricarboxylic acid,DMF=dimethyl formamide) was synthesized under the mild conditions and its crystal structure was determined by single crystal X-ray diffraction...The title compound Mn 3(BTC) 2(DMF) 4 (BTC=1,3,5-benzenetricarboxylic acid,DMF=dimethyl formamide) was synthesized under the mild conditions and its crystal structure was determined by single crystal X-ray diffraction. The compound crystallizes in the monoclinic system and belongs to space group P2 1/c with a =1.787 6(4) nm, b =1.179 7(2) nm, c =1.884 8(4) nm, β =116.35(3)°, V = 3.561 9(12) nm 3, Z =4, D c=7.413 Mg/m 3, M r=871.43, μ =5.081 mm -1 , F (000)=8 082, R = 0.045 6 , wR =0.106 3. Its structure reveals that each asymmetric unit of the title polymer contains three Mn(Ⅱ) ions,six BTC and four DMF ligands. The coordination of BTC ligands with Mn(Ⅱ) ions forms a 3D infinite framework having helical chains composed with 2 1 axes and about 0.6 nm× 0.8 nm channels along the [100] direction.展开更多
The title compound [Zn3（BTC）2（H2O）3]n（BTC=1,3,5-benzenetricarboxylic acid） was synthesized under mild conditions and its crystal structure was determined by single crystal X-ray diffraction. The compound crystal...The title compound [Zn3（BTC）2（H2O）3]n（BTC=1,3,5-benzenetricarboxylic acid） was synthesized under mild conditions and its crystal structure was determined by single crystal X-ray diffraction. The compound crystallizes in the cubic system and belongs to space group Fm-3m with a=2.662 6（3） nm ,V=18.877（4） nm 3,Z=16,Dc=1.51 g/cm 3,Mr=664.4,μ=0.198 mm -1 , F（000）=852 ,R=0.062 5,wR=0.129 4. Its structure reveals that the title polymer is composed of dimeric zinc tetracarboxylate units,with a short Zn-Zn internuclear separation of 0.295 0（4） nm. The coordination of BTC ligands with Zn ions forms a 3D infinite framework with about 1.117 4 nm×1.327 4 nm pores along the [001],[100] and [010] direction. [WT5HZ]展开更多
文摘The title compound Mn 3(BTC) 2(DMF) 4 (BTC=1,3,5-benzenetricarboxylic acid,DMF=dimethyl formamide) was synthesized under the mild conditions and its crystal structure was determined by single crystal X-ray diffraction. The compound crystallizes in the monoclinic system and belongs to space group P2 1/c with a =1.787 6(4) nm, b =1.179 7(2) nm, c =1.884 8(4) nm, β =116.35(3)°, V = 3.561 9(12) nm 3, Z =4, D c=7.413 Mg/m 3, M r=871.43, μ =5.081 mm -1 , F (000)=8 082, R = 0.045 6 , wR =0.106 3. Its structure reveals that each asymmetric unit of the title polymer contains three Mn(Ⅱ) ions,six BTC and four DMF ligands. The coordination of BTC ligands with Mn(Ⅱ) ions forms a 3D infinite framework having helical chains composed with 2 1 axes and about 0.6 nm× 0.8 nm channels along the [100] direction.
文摘The title compound [Zn3（BTC）2（H2O）3]n（BTC=1,3,5-benzenetricarboxylic acid） was synthesized under mild conditions and its crystal structure was determined by single crystal X-ray diffraction. The compound crystallizes in the cubic system and belongs to space group Fm-3m with a=2.662 6（3） nm ,V=18.877（4） nm 3,Z=16,Dc=1.51 g/cm 3,Mr=664.4,μ=0.198 mm -1 , F（000）=852 ,R=0.062 5,wR=0.129 4. Its structure reveals that the title polymer is composed of dimeric zinc tetracarboxylate units,with a short Zn-Zn internuclear separation of 0.295 0（4） nm. The coordination of BTC ligands with Zn ions forms a 3D infinite framework with about 1.117 4 nm×1.327 4 nm pores along the [001],[100] and [010] direction. [WT5HZ]
