Poly (EA-MAn-APTES)/silica hybrid materials were successfully prepared fromEthyl acrylate (EA), maleic anhydride (MAn) and tetraethoxysilane (TEOS) in the presence of acoupling agent 3-aminopropyltriethoxysilane (APTE...Poly (EA-MAn-APTES)/silica hybrid materials were successfully prepared fromEthyl acrylate (EA), maleic anhydride (MAn) and tetraethoxysilane (TEOS) in the presence of acoupling agent 3-aminopropyltriethoxysilane (APTES),by free-radical solution polymerization and insitu sol-gel process. The mass fraction of TEOS varied from 0 to 25%. The hybrid materials werecharacterized by the methods of FT-IR spectra, solvent extraction, scanning electron microscope (SEM), transmission electron microscope (TEM), differential scanning calorimetry (DSC) andthermogravimetric analysis (TGA) measuring apparatus to get their structures, gel contents,morphologies, particle sizes and thermal performances. The results show that the covalent bonds arebetween organic and inorganic phases, gel contents in the hybrid materials are much higher, theSiO_2 phase is well dispersed in the polymer matrix, silicon dioxide exist at nanoscale in thecomposites and have excellent thermal stability.展开更多
The organic gel-thermal reduction process was used for the preparation of ferromagnetic metal Ni, Co and Fe fine fibers from the raw materials of citric acid, lactic acid and metal salts. The structure, thermal decomp...The organic gel-thermal reduction process was used for the preparation of ferromagnetic metal Ni, Co and Fe fine fibers from the raw materials of citric acid, lactic acid and metal salts. The structure, thermal decomposition process and morphologies of the gel precursors and fibers derived from thermal reduction of these gel precursors were characterized by Fourier transform infrared spectroscopy, X-ray diffraction, thermo-gravimetric/differential scanning calorimetry and scanning electron microscopy. The results show that spinnability of gel largely depends on molecular structure of metal-carboxylate complex that is a linear-type structure formed in the gel. As a result, the gels exhibit a good spinnability. Metal Ni, Co and Fe fine fibers are featured with diameters of around 1 μm and a high aspect ratio up to 1×106.展开更多
Six preparation methods for polymeric organic-inorganic nanocomposites and their respective mechanisms and features are reviewed. The extraordinary properties of polymeric organic-inorganic nanocomposites are discusse...Six preparation methods for polymeric organic-inorganic nanocomposites and their respective mechanisms and features are reviewed. The extraordinary properties of polymeric organic-inorganic nanocomposites are discussed,and their potential applications are evaluated.展开更多
Room temperature ionic liquids(RTILs) are non-volatile organic salts. They may replace conventional coalescing agents in latex coating thus reducing volatile organic compounds(VOCs) emission as well as improving perfo...Room temperature ionic liquids(RTILs) are non-volatile organic salts. They may replace conventional coalescing agents in latex coating thus reducing volatile organic compounds(VOCs) emission as well as improving performance of latex coating products such as better thermal stability, conductivity, and antifouling property. The formation of latex coating containing RTILs can be achieved by encapsulation of RTILs inside particles via miniemulsion polymerization. In this study, the role of RTILs and its concentration on stability of miniemulsion during storage and polymerization were investigated. It has been found that, above a critical concentration(10 wt%), adding more RTILs to oil phase may weaken miniemulsion stability during storage as well as polymerization. Such observations were consistent with the zeta potential measurement for miniemulsions prepared at the similar conditions. The results obtained here would be a useful guideline for the development of new waterborne coating products with desirable functions and particle sizes.展开更多
Low-molecular-weight organogels(LMOG) have been attracting a surge interest in fabricating soft materials.Although the finding of the gelator molecules has been developed from serendipity to objective design,the achie...Low-molecular-weight organogels(LMOG) have been attracting a surge interest in fabricating soft materials.Although the finding of the gelator molecules has been developed from serendipity to objective design,the achievement of the gelator molecules still needs good design and tedious organic synthesis.In this paper,we proposed a simple and general mixing approach to get the organogel for nearly all the organic compounds and even soluble nanoparticles without any modification.We have designed a universal gelator molecule,which forms organogels with more than 40 kinds of organic solvents from aploar to polar solvents.More interestingly,when other organic compounds or even nanomaterials,which are soluble in certain organic solvents,are mixed with this gelator molecule,they can form organogels no matter whether the individual compounds could form organogel or not.This method is applicable to nearly all kinds of soluble organic compounds and opens an efficient and universal way to fabricate gel materials.展开更多
文摘Poly (EA-MAn-APTES)/silica hybrid materials were successfully prepared fromEthyl acrylate (EA), maleic anhydride (MAn) and tetraethoxysilane (TEOS) in the presence of acoupling agent 3-aminopropyltriethoxysilane (APTES),by free-radical solution polymerization and insitu sol-gel process. The mass fraction of TEOS varied from 0 to 25%. The hybrid materials werecharacterized by the methods of FT-IR spectra, solvent extraction, scanning electron microscope (SEM), transmission electron microscope (TEM), differential scanning calorimetry (DSC) andthermogravimetric analysis (TGA) measuring apparatus to get their structures, gel contents,morphologies, particle sizes and thermal performances. The results show that the covalent bonds arebetween organic and inorganic phases, gel contents in the hybrid materials are much higher, theSiO_2 phase is well dispersed in the polymer matrix, silicon dioxide exist at nanoscale in thecomposites and have excellent thermal stability.
基金Projects(50474038 50674048) supported by the National Natural Science Foundation of China
文摘The organic gel-thermal reduction process was used for the preparation of ferromagnetic metal Ni, Co and Fe fine fibers from the raw materials of citric acid, lactic acid and metal salts. The structure, thermal decomposition process and morphologies of the gel precursors and fibers derived from thermal reduction of these gel precursors were characterized by Fourier transform infrared spectroscopy, X-ray diffraction, thermo-gravimetric/differential scanning calorimetry and scanning electron microscopy. The results show that spinnability of gel largely depends on molecular structure of metal-carboxylate complex that is a linear-type structure formed in the gel. As a result, the gels exhibit a good spinnability. Metal Ni, Co and Fe fine fibers are featured with diameters of around 1 μm and a high aspect ratio up to 1×106.
基金Supported by Phosphor Plan of Science Technology of Young Scientists of Shanghai(No.00QE14047).
文摘Six preparation methods for polymeric organic-inorganic nanocomposites and their respective mechanisms and features are reviewed. The extraordinary properties of polymeric organic-inorganic nanocomposites are discussed,and their potential applications are evaluated.
基金the Low Carbon Automation Manufacture Innovation Team 2011B81006 for the PhD studentshipNingbo Natural Science Foundation funding 2012A610094
文摘Room temperature ionic liquids(RTILs) are non-volatile organic salts. They may replace conventional coalescing agents in latex coating thus reducing volatile organic compounds(VOCs) emission as well as improving performance of latex coating products such as better thermal stability, conductivity, and antifouling property. The formation of latex coating containing RTILs can be achieved by encapsulation of RTILs inside particles via miniemulsion polymerization. In this study, the role of RTILs and its concentration on stability of miniemulsion during storage and polymerization were investigated. It has been found that, above a critical concentration(10 wt%), adding more RTILs to oil phase may weaken miniemulsion stability during storage as well as polymerization. Such observations were consistent with the zeta potential measurement for miniemulsions prepared at the similar conditions. The results obtained here would be a useful guideline for the development of new waterborne coating products with desirable functions and particle sizes.
基金supported by the National Natural Science Foundation of China (50673095 and 21021003)the Basic Research Development Program (2007CB808005 and 2009CB930802)the Fund of the Chinese Academy of Sciences
文摘Low-molecular-weight organogels(LMOG) have been attracting a surge interest in fabricating soft materials.Although the finding of the gelator molecules has been developed from serendipity to objective design,the achievement of the gelator molecules still needs good design and tedious organic synthesis.In this paper,we proposed a simple and general mixing approach to get the organogel for nearly all the organic compounds and even soluble nanoparticles without any modification.We have designed a universal gelator molecule,which forms organogels with more than 40 kinds of organic solvents from aploar to polar solvents.More interestingly,when other organic compounds or even nanomaterials,which are soluble in certain organic solvents,are mixed with this gelator molecule,they can form organogels no matter whether the individual compounds could form organogel or not.This method is applicable to nearly all kinds of soluble organic compounds and opens an efficient and universal way to fabricate gel materials.