基于7075铝合金时效强化机理分析的工艺优化

为了获得最佳的时效工艺和有效提升实验效率,以JMatPro仿真方法为基础,研究了7xxx系铝合金的时效强化机理,获得了铝合金的最佳时效工艺参数。通过JMatPro仿真得到时效过程中析出相的体积分数,获得了经典的JMAK动力学方程,再通过析出相长大模型得到时效过程中析出相的尺寸。然后,分别使用时效强化模型和JMatPro仿真方法计算时效后合金的强度,与时效强化模型相比,使用JMatPro仿真方法可以将合金强度峰值预测精度提高了0.72%;峰值时间预测精度提高了18.28%。最后,通过拟合JMatPro的仿真结果,获得了强度峰值、峰值时间与时效温度的关系表达式,为制定最佳的时效工艺参数提供指导。

Aging behavior and mechanical properties of 6013 aluminum alloy processed by severe plastic deformation

Structural features, aging behavior, precipitation kinetics and mechanical properties of a 6013 Al–Mg–Si aluminum alloy subjected to equal channel angular pressing （ECAP） at different temperatures were comparatively investigated with that in conventional static aging by quantitative X-ray diffraction （XRD） measurements, differential scanning calorimetry （DSC） and tensile tests. Average grain sizes measured by XRD are in the range of 66-112 nm while the average dislocation density is in the range of 1.20×10^14-1.70×10^14 m^-2 in the deformed alloy. The DSC analysis reveals that the precipitation kinetics in the deformed alloy is much faster as compared with the peak-aged sample due to the smaller grains and higher dislocation density developed after ECAP. Both the yield strength （YS） and ultimate tensile strength （UTS） are dramatically increased in all the ECAP samples as compared with the undeformed counterparts. The maximum strength appears in the samples ECAP treated at room temperature and the maximum YS is about 1.6 times that of the statically peak-aged sample. The very high strength in the ECAP alloy is suggested to be related to the grain size strengthening and dislocation strengthening, as well as the precipitation strengthening contributing from the dynamic precipitation during ECAP.

Experiments and modeling of double-peak precipitation hardening and strengthening mechanisms in Al-Zn-Mg alloy

The aim of the present work is to develop a model for simulating double-peak precipitation hardening kinetics in Al-Zn-Mg alloy with the simultaneous formation of different types of precipitates at elevated temperatures based on the modified Langer-Schwartz approach. The double aging peaks are present in the long time age-hardening curves of Al-Zn-Mg alloys. The physically-based model, while taking explicitly into account nucleation, growth, coarsening of the new phase precipitations and two strengthening mechanisms associated with particle-dislocation interaction （shearing and bypassing）, was used for the analysis of precipitates evolution and precipitation hardening during aging of Al-Zn-Mg alloy. Model predictions were compared with the measurements of Al-Zn-Mg alloy. The systematic and quantitative results show that the predicted hardness profiles of double peaks via adding a shape dependent parameter in the growth equation for growth and coarsening generally agree well with the measured ones. Two strengthening mechanisms associated with particle-dislocation interaction （shearing and bypassing） were considered operating simultaneously in view of the particle size-distribution. The transition from shearing to bypassing strengthening mechanism was found to occur at rather early stage of the particle growth. The bypassing was found to be the prevailing strengthening mechanism in the investigated alloys.

Microstructures and mechanical properties of BP/7A04 Al matrix composites

The microstructures and interface structures of basalt particle reinforced 7A04 Al matrix composites (BP/7A04 Al) were analyzed by using OM, TEM, SEM and EDS, and the mechanical properties of 7A04 Al alloy were compared with those of BP/7A04 Al matrix composites. The results show that the basalt particles are dispersed in the Al matrix and form a strong bonding interface with the Al matrix. SiO2 at the edge of the basalt particles is continuously replaced by Al2O3 formed in the reaction, forming a high-temperature reaction layer with a thickness of several tens of nanometers, and Al2O3 strengthens the bonding interface between basalt particles and Al matrix. The dispersed basalt particles promote the dislocation multiplication, vacancy formation and precipitation of the matrix, and the precipitated phases mainly consist of plate-like η(MgZn2) phase and bright white band-shaped or ellipsoidal T (Al2Mg3Zn3) phase. The bonding interface, high dislocation density and dispersion strengthening phase significantly improve the mechanical properties of the composites. The yield strength and ultimate tensile strength of BP/7A04 Al matrix composites are up to 665 and 699 MPa, which increase by 11.4% and 10.9% respectively compared with 7A04 Al alloy without basalt particles.

Effects of Cu content on microstructures and compressive mechanical properties of CNTs/Al-Cu composites

The carbon nanotubes(CNTs) reinforced Al-Cu matrix composites were prepared by hot pressing sintering and hot rolling, and the effects of Cu content on the interfacial reaction between Al and CNTs, the precipitation behavior of Cu-containing precipitates, and the resultant mechanical properties of the composites were systematically investigated. The results showed that the increase of Cu content can not only increase the number and size of Cu-containing precipitate generated during the composite fabrication processes, but also promote the interfacial reaction between CNTs and Al matrix, leading to the intensified conversion of CNTs into Al_(4)C_(3). As a result, the composite containing 1 wt.% Cu possesses the highest strength, elastic modulus and hardness among all composites, due to the maintenance of the original structure of CNTs. Moreover, the increase of Cu content can change the dominant strengthening mechanisms for the enhanced strength of the fabricated composites.

Strengthening mechanism of T8-aged Al-Cu-Li alloy with increased pre-deformation

The microstructure evolution and mechanical properties of a T8-aged Al-Cu-Li alloy with increased pre-deformation(0-15%) were investigated,revealing the microstructure-strength relationship and the intrinsic strengthening mechanism.The results show that increasing the pre-deformation levels remarkably improves the strength of the alloy but deteriorates its ductility.Dislocations introduced by pre-deformation effectively suppress the formation of Guinier-Preston(GP) zones and provide more nucleation sites for T1 precipitates.This leads to more intensive and finer T1 precipitates in the samples with higher pre-deformation levels.Simultaneously,the enhanced precipitation of T1 precipitates and inhibited formation of GP zones cause the decreases in number and sizes of θ′ precipitates.The quantitative descriptions of the strength contributions from different strengthening mechanisms reveal that strengthening contributions from T1 and θ′ precipitates decrease with increasing pre-deformation.The reduced diameters of T1 precipitates are primarily responsible for their weakened strengthening effects.Therefore,the improved strength of the T8-aged Al-Cu-Li alloy is mainly attributed to the stronger strain hardening from the increased pre-deformation levels.