Stable aqueous carbon inks,with graphene sheets(GSs)and carbon black(CB)as conductive fillers,are prepared by a simple one-pot ball-milling method.The asprepared composite ink with 10 wt%GSs shows optimized rheologica...Stable aqueous carbon inks,with graphene sheets(GSs)and carbon black(CB)as conductive fillers,are prepared by a simple one-pot ball-milling method.The asprepared composite ink with 10 wt%GSs shows optimized rheological properties(viscosity and thixotropy)for screen printing.The as-printed coatings based on the above ink are uniform and dense on a polyimide substrate,and exhibit a sandwich-type conductive three dimensional network at the microscale.The resistivity of the typical composite coating is as low as 0.23±0.01Ωcm(92±4Ωsq^-1,25μm),which is 30%as that of a pure CB coating(0.77±0.01Ωcm).It is noteworthy that the resistivity decreases to 0.18±0.01Ωcm(72±4Ωsq^-1,25μm)after a further rolling compression.The coating exhibits good mechanical flexibility,and the resistance slightly increases by 12%after 3000 bending cycles.With the CB/GSs composite coatings as a flexible conductor,fascinating luminescent bookmarks and membrane switches were fabricated,demonstrating the tremendous potential of these coatings in the commercial production of flexible electronics and devices.展开更多
基金supported by the Scientific and Technological Key Project of Shanxi Province (MC2016-04 and MC2016-08)Natural Science Foundation of Shanxi Province (201801D221156)+2 种基金DNL Cooperation Fund of CAS (DNL180308)Science and Technology Service Network Initiative of CAS (KFJ-STS-ZDTP-068)Youth Innovation Promotion Association of CAS
文摘Stable aqueous carbon inks,with graphene sheets(GSs)and carbon black(CB)as conductive fillers,are prepared by a simple one-pot ball-milling method.The asprepared composite ink with 10 wt%GSs shows optimized rheological properties(viscosity and thixotropy)for screen printing.The as-printed coatings based on the above ink are uniform and dense on a polyimide substrate,and exhibit a sandwich-type conductive three dimensional network at the microscale.The resistivity of the typical composite coating is as low as 0.23±0.01Ωcm(92±4Ωsq^-1,25μm),which is 30%as that of a pure CB coating(0.77±0.01Ωcm).It is noteworthy that the resistivity decreases to 0.18±0.01Ωcm(72±4Ωsq^-1,25μm)after a further rolling compression.The coating exhibits good mechanical flexibility,and the resistance slightly increases by 12%after 3000 bending cycles.With the CB/GSs composite coatings as a flexible conductor,fascinating luminescent bookmarks and membrane switches were fabricated,demonstrating the tremendous potential of these coatings in the commercial production of flexible electronics and devices.