Al_(0.1)CoCrFeNi高熵合金在准静态扭转下的微观组织和力学性能

将Al_(0.1)CoCrFeNi高熵合金进行准静态扭转加载,利用X射线衍射分析仪、扫描电镜、电子背散射衍射、纳米压痕以及准静态拉伸实验,研究了扭转后试样的梯度微结构和力学性能。除了晶粒细化,高熵合金的梯度微结构还包括位错及孪晶亚结构的梯度分布,即含量从中心到边缘不断增加。准静态拉伸实验表明,由于梯度微结构和较高的加工硬化能力,扭转后的拉伸板可显著提高拉伸强度,同时保持良好的塑性。因此,梯度应变、额外的加工硬化能力和背应力效应实现了强度和塑性的协调变形。此外,纳米压痕硬度沿径向不断增加,同样呈现明显的梯度分布,其强化机制主要归因于细晶强化和加工硬化。

Microstructure and ablation behavior of Zr-based ultra-high-temperature gradient composites

To obtain high-performance Zr-based ultra-high-temperature composites,Zr-based ultra-high-temperature gradient composites were prepared by changing the laying method of the infiltrant via reactive melt infiltration.The effects of different infiltrant laying methods on the microstructure and ablative properties of Zr-based ultrahigh-temperature gradient composites were investigated.The results showed that the gradient structure of the Zr-based ultrahigh-temperature gradient composites differed when the composition ratio of the infiltrant was changed.When the thicknesses of the Zr/Mo/Si layers were 6/4/12 mm and 8/2/12 mm,the SiMoZrC solid solution content in the samples increased and decreased along the infiltration direction,respectively.The gradient samples were ablated in an oxyacetylene flame at 3000°C for 40 s.The ablation resistance of the sample was the highest when the infiltrant was a powder and the thickness of the Zr/Mo/Si layer was 6/4/12 mm.

Microstructure of TA2/TA15 graded structural material by laser additive manufacturing process

TA2/TA15 graded structural material（GSM） was fabricated by the laser additive manufacturing（LAM） process. The chemical composition, microstructure and micro-hardness of the as-deposited GSM were investigated. The results show that the TA2 part of exhibiting near-equiaxed grains was Widmanst？tten α-laths microstructure. The TA15 part containing large columnar grains was fine basket-weave microstructure. The graded zone was divided into four deposited layers with 3000 μm in thickness. As the distance from the TA2 part increases, the alloy element contents and the β phase volume fraction increase, the α phase volume fraction decreases and the microstructure shows the evolution from Widmanst？tten α-laths to basket-weave α-laths gradually. The micro-hardness increases from the TA2 part to the TA15 part due to the solid solution strengthening and grain boundary strengthening.

Microstructural evolution and mechanical properties of Ti-5Al-5Mo-5V-3Cr alloy by heat treatment with continuous temperature gradient

A new high throughput heat-treatment method with a continuous temperature gradient between 600 and 700 ？C was utilized on the Ti-5553 alloy（Ti-5 Al-5 Mo-5 V-3 Cr, mass fraction, %）. The temperature gradient was induced by the variation of the axial section of sample, which was heated by the direct current. The variation of continuous cooling rates on the treated sample was realized by using the end quenching method. The microstructural evolution and mechanical properties under different heat treatment conditions were evaluated. The results show that the pseudo-spinodal decomposition of the alloy occurs at（617±1） ？C, and the size of the precipitated α phase is around 300 nm. Moreover, the highest microhardness is obtained after the heat treatment at the pseudo-spinodal decomposition temperature for 4 h. These indicate that the high throughput method is efficient and fast to determine the phase transformation temperature and corresponding microstructural evolution of alloys.

Microstructure and mechanical properties of TA15/TC11 graded structural material by wire arc additive manufacturing process

A graded structural material(GSM)with a material transition from TA15 to TC11 was fabricated by wire arc additive manufacturing(WAAM)method.The grain morphology,chemical composition,microstructure and mechanical properties of the as-deposited GSM were all characterized to investigate their variations along the deposition direction.The results indicate that from TA15 to TC11,the grain size decreases and a transition from columnar grains to equiaxed grains occurs.The content of alloy element alters greatly within a short distance,and the width of the mutation zone is 800μm.Both TA15 and TC11 regions exhibit basketweave microstructure withα-phase andβ-phase.However,during the transition from TA15 to TC11,theα-lath becomes fine,which leads to an increase in microhardness.The tensile test shows that the bonding strength at the interface is higher than the longitudinal strength of TA15,and the lateral elongation at the interface is higher than that of TA15 and TC11.