Double-V butt TIG welding process was performed on two plates of AA6061-T6 using ER5356 filler. The microstructure,mechanical and nanomechanical properties of the joint were evaluated in as-welded and after post weld ...Double-V butt TIG welding process was performed on two plates of AA6061-T6 using ER5356 filler. The microstructure,mechanical and nanomechanical properties of the joint were evaluated in as-welded and after post weld heat treatment (PWHT) usingXRD, FESEM, EBSD, nanoindentation and tensile tests. The results show that PWHT led to microstructural recovery of the heataffected zone (HAZ) in addition to the appearance of β-phase (Al3Mg2) at the grain boundaries of weld zone. The hardness (Hnano) inall zones increased after PWHT while the elastic modulus (Enano) was improved from 69.93 GPa to 81 GPa in weld area. All resultsindicate that PWHT has created a homogenous microstructure in the weld zone in addition to outstanding improvement inmechanical properties for the weld zone which surpass the base metal.展开更多
基金the financial support for this study from the Malaysian Ministry of Higher Education(MOHE) through the Fundamental Research Grant Scheme and Exploratory Research Grant Scheme
文摘Double-V butt TIG welding process was performed on two plates of AA6061-T6 using ER5356 filler. The microstructure,mechanical and nanomechanical properties of the joint were evaluated in as-welded and after post weld heat treatment (PWHT) usingXRD, FESEM, EBSD, nanoindentation and tensile tests. The results show that PWHT led to microstructural recovery of the heataffected zone (HAZ) in addition to the appearance of β-phase (Al3Mg2) at the grain boundaries of weld zone. The hardness (Hnano) inall zones increased after PWHT while the elastic modulus (Enano) was improved from 69.93 GPa to 81 GPa in weld area. All resultsindicate that PWHT has created a homogenous microstructure in the weld zone in addition to outstanding improvement inmechanical properties for the weld zone which surpass the base metal.