Constant-current anodization of pure aluminum was carried out in non-corrosive capacitor working electrolytes to study the formation mechanism of nanopores in the anodic oxide films.Through comparative experiments,nan...Constant-current anodization of pure aluminum was carried out in non-corrosive capacitor working electrolytes to study the formation mechanism of nanopores in the anodic oxide films.Through comparative experiments,nanopores are found in the anodic films formed in the electrolytes after high-temperature storage(HTS)at 130°C for 240 h.A comparison of the voltage-time curves suggests that the formation of nanopores results from the decrease in formation efficiency of anodic oxide films rather than the corrosion of the electrolytes.FT-IR and UV spectra analysis shows that carboxylate and ethylene glycol in electrolytes can easily react by esterification at high temperatures.Combining the electronic current theory and oxygen bubble mold effect,the change in electrolyte composition could increase the electronic current in the anodizing process.The electronic current decreases the formation efficiency of anodic oxide films,and oxygen bubbles accompanying electronic current lead to the formation of nanopores in the dense films.The continuous electronic current and oxygen bubbles are the prerequisites for the formation of porous anodic oxides rather than the traditional field-assisted dissolution model.展开更多
The structure, separation principle and feasibility research for a new type of vehicle air filter called the high speed rotary positive air filter were described. The analysis of the experimental data showed that the ...The structure, separation principle and feasibility research for a new type of vehicle air filter called the high speed rotary positive air filter were described. The analysis of the experimental data showed that the principle and structure of it were feasible and it possessed high separation efficiency and great self cleaning ability. Compared with the conventional air filter it also has lower air intake loss. So it is worth further practical research.展开更多
[Objective] The deliver amount and deliver rate of heavy metal elements during smoking were studied, which could provide a reference for reducing the damage of cigarette products. [Method] Two pretreatment methodsof m...[Objective] The deliver amount and deliver rate of heavy metal elements during smoking were studied, which could provide a reference for reducing the damage of cigarette products. [Method] Two pretreatment methodsof microwave di- gestion and acid extraction were used to process the ash content, the total particu- late matter of mainstream smoke （TPM） and cigarette filter. Detection results of heavy metal elements were compared by the two methods. [Result] The microwave digestion method was better than acid solution extraction method on analysis of TPM, but presented disadvantages on analysis of ash and filter. Meanwhile, the migration amount and rate were studied and resultsshowed that most heavy metal elements were escaped along with sidestream smoke between 66.89% and 95.48%, and almost all Hg escaped through sidestream smoke. Other heavy metal elements, except Hg, were separately found in ash, TPM and filter. Cr, Ni, As and Se were mostly residual in ash, followed by TPM, and filter had the least, while Cd and Pb were just in the reverse order. Normally, 5% or less heavy metal elements were transferred to TPM, only a small part of which could reach 5%-10%. [Conclusion] Most of the heavy metal elements are taken by sidestream smoke, ash and filter, while the migration amounts to mainstream smoke are extremely low.展开更多
基金financially supported by the National Natural Science Foundation of China(Nos.51777097,51577093)。
文摘Constant-current anodization of pure aluminum was carried out in non-corrosive capacitor working electrolytes to study the formation mechanism of nanopores in the anodic oxide films.Through comparative experiments,nanopores are found in the anodic films formed in the electrolytes after high-temperature storage(HTS)at 130°C for 240 h.A comparison of the voltage-time curves suggests that the formation of nanopores results from the decrease in formation efficiency of anodic oxide films rather than the corrosion of the electrolytes.FT-IR and UV spectra analysis shows that carboxylate and ethylene glycol in electrolytes can easily react by esterification at high temperatures.Combining the electronic current theory and oxygen bubble mold effect,the change in electrolyte composition could increase the electronic current in the anodizing process.The electronic current decreases the formation efficiency of anodic oxide films,and oxygen bubbles accompanying electronic current lead to the formation of nanopores in the dense films.The continuous electronic current and oxygen bubbles are the prerequisites for the formation of porous anodic oxides rather than the traditional field-assisted dissolution model.
文摘The structure, separation principle and feasibility research for a new type of vehicle air filter called the high speed rotary positive air filter were described. The analysis of the experimental data showed that the principle and structure of it were feasible and it possessed high separation efficiency and great self cleaning ability. Compared with the conventional air filter it also has lower air intake loss. So it is worth further practical research.
文摘[Objective] The deliver amount and deliver rate of heavy metal elements during smoking were studied, which could provide a reference for reducing the damage of cigarette products. [Method] Two pretreatment methodsof microwave di- gestion and acid extraction were used to process the ash content, the total particu- late matter of mainstream smoke （TPM） and cigarette filter. Detection results of heavy metal elements were compared by the two methods. [Result] The microwave digestion method was better than acid solution extraction method on analysis of TPM, but presented disadvantages on analysis of ash and filter. Meanwhile, the migration amount and rate were studied and resultsshowed that most heavy metal elements were escaped along with sidestream smoke between 66.89% and 95.48%, and almost all Hg escaped through sidestream smoke. Other heavy metal elements, except Hg, were separately found in ash, TPM and filter. Cr, Ni, As and Se were mostly residual in ash, followed by TPM, and filter had the least, while Cd and Pb were just in the reverse order. Normally, 5% or less heavy metal elements were transferred to TPM, only a small part of which could reach 5%-10%. [Conclusion] Most of the heavy metal elements are taken by sidestream smoke, ash and filter, while the migration amounts to mainstream smoke are extremely low.