Using low-cost FePO4·2H2O as iron source,Na2FePO4F/C composite is prepared by alcohol-assisted ball milling and solid-state reaction method.The XRD pattern of Na2FePO4F/C composite demonstrates sharp peaks,indica...Using low-cost FePO4·2H2O as iron source,Na2FePO4F/C composite is prepared by alcohol-assisted ball milling and solid-state reaction method.The XRD pattern of Na2FePO4F/C composite demonstrates sharp peaks,indicating high crystalline and phase purity.The SEM and TEM images reveal that diameter of the spherical-like Na2FePO4F/C particles ranges from 50 to 300 nm,and HRTEM image shows that the surface of Na2FePO4F/C composite is uniformly coated by carbon layer with a average thickness of about 3.6 nm.The carbon coating constrains the growth of the particles and effectively reduces the agglomeration of nanoparticles.Using lithium metal as anode,the composite delivers a discharge capacities of 102.8,96.4 and 90.3 mA·h/g at rates of 0.5C,1C and 2C,respectively.After 100 cycles at 0.5C,a discharge capacity of 98.9 mA·h/g is maintained with capacity retention of 96.2%.The Li+diffusion coefficient(D)of Na2FePO4F/C composite is calculated as 1.71×10^–9 cm^2/s.This study reveals that the simple solid state reaction could be a practical and effective synthetic route for the industrial production of Na2FePO4F/C material.展开更多
A promising preparation method for lithium hexafluorophosphate(LiPF6)was introduced.Phosphorus pentafluoride(PF5) was first prepared using CaF2 and P2O5 at 280℃for 3 h.LiPF6 was synthesized in acetonitrile solvent by...A promising preparation method for lithium hexafluorophosphate(LiPF6)was introduced.Phosphorus pentafluoride(PF5) was first prepared using CaF2 and P2O5 at 280℃for 3 h.LiPF6 was synthesized in acetonitrile solvent by LiF and PF5 at room temperature(20-30℃)for 4 h.The synthesized LiPF6 was characterized by infrared spectrometry and X-ray diffraction(XRD). Atomic absorption and ion chromatography results show that the purity of synthesized LiPF6 reaches 99.98%.Thermal stability of self-synthesized LiPF6 was analyzed by differential thermal analysis and thermogravimetry.The results indicate that the self-synthesized LiPF6 has higher purity,lower impurity contents and better thermal stability than the commercial LiPF6.展开更多
基金Projects(51472211,51502256)supported by the National Natural Science Foundation of ChinaProjects(2016GK4005,2016GK4030)supported by the Strategic New Industry of Hunan Province,ChinaProject(13C925)supported by the Research Foundation of Education Bureau of Hunan Province,China
文摘Using low-cost FePO4·2H2O as iron source,Na2FePO4F/C composite is prepared by alcohol-assisted ball milling and solid-state reaction method.The XRD pattern of Na2FePO4F/C composite demonstrates sharp peaks,indicating high crystalline and phase purity.The SEM and TEM images reveal that diameter of the spherical-like Na2FePO4F/C particles ranges from 50 to 300 nm,and HRTEM image shows that the surface of Na2FePO4F/C composite is uniformly coated by carbon layer with a average thickness of about 3.6 nm.The carbon coating constrains the growth of the particles and effectively reduces the agglomeration of nanoparticles.Using lithium metal as anode,the composite delivers a discharge capacities of 102.8,96.4 and 90.3 mA·h/g at rates of 0.5C,1C and 2C,respectively.After 100 cycles at 0.5C,a discharge capacity of 98.9 mA·h/g is maintained with capacity retention of 96.2%.The Li+diffusion coefficient(D)of Na2FePO4F/C composite is calculated as 1.71×10^–9 cm^2/s.This study reveals that the simple solid state reaction could be a practical and effective synthetic route for the industrial production of Na2FePO4F/C material.
基金Project(2007CB613607)supported by the National Basic Research Program of China
文摘A promising preparation method for lithium hexafluorophosphate(LiPF6)was introduced.Phosphorus pentafluoride(PF5) was first prepared using CaF2 and P2O5 at 280℃for 3 h.LiPF6 was synthesized in acetonitrile solvent by LiF and PF5 at room temperature(20-30℃)for 4 h.The synthesized LiPF6 was characterized by infrared spectrometry and X-ray diffraction(XRD). Atomic absorption and ion chromatography results show that the purity of synthesized LiPF6 reaches 99.98%.Thermal stability of self-synthesized LiPF6 was analyzed by differential thermal analysis and thermogravimetry.The results indicate that the self-synthesized LiPF6 has higher purity,lower impurity contents and better thermal stability than the commercial LiPF6.