Plasma electrolytic oxidation(PEO) of brass was carried out in aluminate electrolytes with the addition of NaH2PO4(S1) and Na2SiO3(S2), respectively, with the aim to investigate the effect of additives on the coating ...Plasma electrolytic oxidation(PEO) of brass was carried out in aluminate electrolytes with the addition of NaH2PO4(S1) and Na2SiO3(S2), respectively, with the aim to investigate the effect of additives on the coating formation and corrosion resistance. For the PEO in S1 electrolyte, a mixed layer of AlPO4and Al2O3is formed at the initial stage, which leads to fast plasma discharges and formation of black coatings with the compositions of Al2O3,CuO, Cu2O and ZnO. However, in S2 electrolyte, plasma discharges are delayed and the coatings show a reddish color due to more Cu2O. Mott-Schottky tests show that the S1 coatings are p-type semiconductors;while the S2 coatings can be adjusted between n-type and p-type. Potentiodynamic polarization and electrochemical impedance spectroscopy(EIS) tests show that the PEO treatment can significantly improve the corrosion resistance of brass, with protection efficiency up to 91.50% and the largest charge transfer resistance of 59.95 kΩ·cm^(2) for the S1 coating.展开更多
A systematic study was conducted on current efficiency （CE）, corrosion and structural changes in SnO2-based inert anodes （made of 96wt%SnO2＋2wt%Sb2O3＋2wt%CuO） on a laboratory Hall-Heroult aluminium cell. The inf...A systematic study was conducted on current efficiency （CE）, corrosion and structural changes in SnO2-based inert anodes （made of 96wt%SnO2＋2wt%Sb2O3＋2wt%CuO） on a laboratory Hall-Heroult aluminium cell. The influence of operating parameters and electrolyte composition on the CE and corrosion process were evaluated. The CE was found to be more than 90% and catastrophic corrosion took place at low percent of Al2O3, high percent of LiF, low cryolite ratio and high current densities. From all the structural changes that took place in the SnO2-based inert anodes, we assumed that the most important contribution was due to the migration of CuO towards the outer limits of the constituent grains of SnO2 based ceramic. The complex process occurred during the formation of various phases and their sintering ability both directly depended on Cu/Sb molar ratio.展开更多
基金supported by the National Natural Science Foundation of China (No. 51671084)the Postgraduate Scientific Research Innovation Project of Hunan Province, China (No. QL20210092)。
文摘Plasma electrolytic oxidation(PEO) of brass was carried out in aluminate electrolytes with the addition of NaH2PO4(S1) and Na2SiO3(S2), respectively, with the aim to investigate the effect of additives on the coating formation and corrosion resistance. For the PEO in S1 electrolyte, a mixed layer of AlPO4and Al2O3is formed at the initial stage, which leads to fast plasma discharges and formation of black coatings with the compositions of Al2O3,CuO, Cu2O and ZnO. However, in S2 electrolyte, plasma discharges are delayed and the coatings show a reddish color due to more Cu2O. Mott-Schottky tests show that the S1 coatings are p-type semiconductors;while the S2 coatings can be adjusted between n-type and p-type. Potentiodynamic polarization and electrochemical impedance spectroscopy(EIS) tests show that the PEO treatment can significantly improve the corrosion resistance of brass, with protection efficiency up to 91.50% and the largest charge transfer resistance of 59.95 kΩ·cm^(2) for the S1 coating.
文摘A systematic study was conducted on current efficiency （CE）, corrosion and structural changes in SnO2-based inert anodes （made of 96wt%SnO2＋2wt%Sb2O3＋2wt%CuO） on a laboratory Hall-Heroult aluminium cell. The influence of operating parameters and electrolyte composition on the CE and corrosion process were evaluated. The CE was found to be more than 90% and catastrophic corrosion took place at low percent of Al2O3, high percent of LiF, low cryolite ratio and high current densities. From all the structural changes that took place in the SnO2-based inert anodes, we assumed that the most important contribution was due to the migration of CuO towards the outer limits of the constituent grains of SnO2 based ceramic. The complex process occurred during the formation of various phases and their sintering ability both directly depended on Cu/Sb molar ratio.