To obtain porous alumina ceramic with high strength,a novel gelcasting system based on 2-hydroxyethyl methacrylate(HEMA)dissolved in tert-butyl alcohol(TBA)was developed.The polymerization of the HEMA-TBA gelcasting s...To obtain porous alumina ceramic with high strength,a novel gelcasting system based on 2-hydroxyethyl methacrylate(HEMA)dissolved in tert-butyl alcohol(TBA)was developed.The polymerization of the HEMA-TBA gelcasting system,the thermal behavior of obtained green body,and the microstructures and mechanical properties of the sintered bodies were investigated by rheometer,TG-DSC,SEM and bending strength testing,respectively.The results show that,(1)10 mg/mL of the initiator(benzoyl peroxide)is the optimal amount for polymerization of this gelscasting system at 25 ℃;(2)The alumina suspension of the HEMA-TBA gelcasting system showing shear-thinning behavior is sufficiently low for gelcasting process;(3)The bending strength of porous alumina ceramic samples,whose porosities range from 42% to 56%,is from(8±0.5)to(91±4.5)MPa.展开更多
基金Project(51202296) supported by the National Natural Science Foundation of China
文摘To obtain porous alumina ceramic with high strength,a novel gelcasting system based on 2-hydroxyethyl methacrylate(HEMA)dissolved in tert-butyl alcohol(TBA)was developed.The polymerization of the HEMA-TBA gelcasting system,the thermal behavior of obtained green body,and the microstructures and mechanical properties of the sintered bodies were investigated by rheometer,TG-DSC,SEM and bending strength testing,respectively.The results show that,(1)10 mg/mL of the initiator(benzoyl peroxide)is the optimal amount for polymerization of this gelscasting system at 25 ℃;(2)The alumina suspension of the HEMA-TBA gelcasting system showing shear-thinning behavior is sufficiently low for gelcasting process;(3)The bending strength of porous alumina ceramic samples,whose porosities range from 42% to 56%,is from(8±0.5)to(91±4.5)MPa.