Ba0.95Ce0.9Y0.1O3－α solid electrolyte was prepared by high temperature solid state reaction. The electrochemical oxygen permeation (oxygen pumping) rates and oxide ion transport number in this electrolyte were detec...Ba0.95Ce0.9Y0.1O3－α solid electrolyte was prepared by high temperature solid state reaction. The electrochemical oxygen permeation (oxygen pumping) rates and oxide ion transport number in this electrolyte were detected in the temperature of 600～ 1000℃ . It was found that this electrolyte exhibited the oxide ion conduction with the oxide ion transport number of 0.3～ 0.5.展开更多
BaxCe0.8Y0.2O3-α(x=1.03,1,0.98) solid electrolyte samples show a single phase of orthorhombic perovskite of BaCeO3. The oxide ion conduction and transport number were detected in the temperature of 600～1000℃by elec...BaxCe0.8Y0.2O3-α(x=1.03,1,0.98) solid electrolyte samples show a single phase of orthorhombic perovskite of BaCeO3. The oxide ion conduction and transport number were detected in the temperature of 600～1000℃by electrochemical oxygen permeation (oxygen pumping), and compared with the results from the oxygen concentration cell. The relation between the ingredient of Ba and oxide ion conduction was also researched. It was found that these electrolytes exhibited the mixed oxide ionic and electronic hole conduction under the experimental temperature and oxygen gas. The oxide ion transport numbers are 0.1～0.6, which are close to the results of the oxygen concentration cell. They increase as the decrease of Ba content in the samples.展开更多
文摘Ba0.95Ce0.9Y0.1O3－α solid electrolyte was prepared by high temperature solid state reaction. The electrochemical oxygen permeation (oxygen pumping) rates and oxide ion transport number in this electrolyte were detected in the temperature of 600～ 1000℃ . It was found that this electrolyte exhibited the oxide ion conduction with the oxide ion transport number of 0.3～ 0.5.
文摘BaxCe0.8Y0.2O3-α(x=1.03,1,0.98) solid electrolyte samples show a single phase of orthorhombic perovskite of BaCeO3. The oxide ion conduction and transport number were detected in the temperature of 600～1000℃by electrochemical oxygen permeation (oxygen pumping), and compared with the results from the oxygen concentration cell. The relation between the ingredient of Ba and oxide ion conduction was also researched. It was found that these electrolytes exhibited the mixed oxide ionic and electronic hole conduction under the experimental temperature and oxygen gas. The oxide ion transport numbers are 0.1～0.6, which are close to the results of the oxygen concentration cell. They increase as the decrease of Ba content in the samples.