In order to reasonably utilize the iron resources of copper slags, the smelting chlorination process was used to remove copper from copper slags. Higher holding temperature and O2 flow rate are beneficial to increasin...In order to reasonably utilize the iron resources of copper slags, the smelting chlorination process was used to remove copper from copper slags. Higher holding temperature and O2 flow rate are beneficial to increasing copper removal rate. However,the Cu2O mode is formed by the reaction of surplus O2 and CuCl with O2 flow rate increasing over 0.4 L/min, causing CuCl volatilization rate and copper removal rate to decrease. The resulting copper removal rate of 84.34% is obtained under the optimum conditions of holding temperature of 1573 K, residence time of 10 min, Ca Cl2 addition amount of 0.1(mass ratio of CaCl2 and the copper slag) and oxygen flow rate of 0.4 L/min. The efficient removal of copper from copper slags through chlorination is feasible.展开更多
The gas phase thermodynamic properties of 135 polychlorinated xanthones(PCXTs)are calculated using a combination of quantum mechanical computations performed with the Gaussian 03 program at the B3LYP/6-311G**level.It ...The gas phase thermodynamic properties of 135 polychlorinated xanthones(PCXTs)are calculated using a combination of quantum mechanical computations performed with the Gaussian 03 program at the B3LYP/6-311G**level.It is found that the chlorine substitution pattern strongly influences the thermodynamic properties of the compounds.The thermodynamic properties of congeners with the same number of chlorines also depend on the chlorine substitution pattern,especially for ortho-substituted congeners.PCXT congeners with one phenyl ring fully chlorinated are found to be the least stable among the analogues.The effect of the chlorine substitution pattern is quantitatively studied by considering the number and position of Cl atom substitution(NPCS).The results show that the NPCS model may be used to predict the thermodynamic properties for all 135 PCXT congeners. In addition,the values of molar heat capacities at constant pressure(cp,m)from 200 to 1000 K for PCXT congeners are calculated,and the temperature dependence relation of this parameter is obtained using the least-squares method.展开更多
基金Project(51204082)supported by the National Natural Science Foundation of ChinaProject(KKZ3201252011)supported by Talent Cultivation Project of Kunming University of Science and Technology,China
文摘In order to reasonably utilize the iron resources of copper slags, the smelting chlorination process was used to remove copper from copper slags. Higher holding temperature and O2 flow rate are beneficial to increasing copper removal rate. However,the Cu2O mode is formed by the reaction of surplus O2 and CuCl with O2 flow rate increasing over 0.4 L/min, causing CuCl volatilization rate and copper removal rate to decrease. The resulting copper removal rate of 84.34% is obtained under the optimum conditions of holding temperature of 1573 K, residence time of 10 min, Ca Cl2 addition amount of 0.1(mass ratio of CaCl2 and the copper slag) and oxygen flow rate of 0.4 L/min. The efficient removal of copper from copper slags through chlorination is feasible.
基金Supported by the National Natural Science Foundation of China （20977046, 20737001）.
文摘The gas phase thermodynamic properties of 135 polychlorinated xanthones(PCXTs)are calculated using a combination of quantum mechanical computations performed with the Gaussian 03 program at the B3LYP/6-311G**level.It is found that the chlorine substitution pattern strongly influences the thermodynamic properties of the compounds.The thermodynamic properties of congeners with the same number of chlorines also depend on the chlorine substitution pattern,especially for ortho-substituted congeners.PCXT congeners with one phenyl ring fully chlorinated are found to be the least stable among the analogues.The effect of the chlorine substitution pattern is quantitatively studied by considering the number and position of Cl atom substitution(NPCS).The results show that the NPCS model may be used to predict the thermodynamic properties for all 135 PCXT congeners. In addition,the values of molar heat capacities at constant pressure(cp,m)from 200 to 1000 K for PCXT congeners are calculated,and the temperature dependence relation of this parameter is obtained using the least-squares method.