Homogeneous(unseeded)precipitation of magnesium carbonate hydrates by the reaction of MgCl2 with Na2CO3 in supersaturated solutions between 273 and 363K was investigated.The compositions,morphologies and filtration ch...Homogeneous(unseeded)precipitation of magnesium carbonate hydrates by the reaction of MgCl2 with Na2CO3 in supersaturated solutions between 273 and 363K was investigated.The compositions,morphologies and filtration characteristics of the precipitates were studied in detail.The magnesium carbonate hydrates obtained at 313K and in the range of 343-363K showed good morphologies and filtration characteristics.Magnesium oxides(MgO)with high purity(97.6%-99.4%)were obtained by calcining magnesium carbonate hydrates at 1073K.展开更多
The selective precipitation of zinc from zinc-nickel sulfate solution with the Zn/Ni molar ratio of20:1was studied.Dropwise addition of0.5mol/L NaOH solution into the zinc-nickel sulfate solution containing0,0.01,0.02...The selective precipitation of zinc from zinc-nickel sulfate solution with the Zn/Ni molar ratio of20:1was studied.Dropwise addition of0.5mol/L NaOH solution into the zinc-nickel sulfate solution containing0,0.01,0.02,0.03and0.04mol/L ethylene diamine tetraacetate(EDTA)as a chelating agent was done.The equilibrium analysis of precipitation pathway was performed using Visual MINTEQ program.The equilibrium analysis showed that the presence of small amounts of EDTA can prevent nickel precipitation in alkaline conditions without any negative effect on zinc precipitation.On this basis,more than90%of zinc could be precipitated as a product with about50%Zn and only0.11%Ni at pH=9.0merely as a result of the presence of0.03mol/L EDTA in the solution.The stirring time of120min after precipitation was found to be essential for more complete separation.The X-ray diffraction studies on the precipitate revealed that the precipitated phase was Zn4(OH)6SO4.4H2O.展开更多
基金Supported by the National Natural Science Foundation of China （20876161） and the National Basic Research Program of China （2007CB613501, 2009CB219904）.
文摘Homogeneous(unseeded)precipitation of magnesium carbonate hydrates by the reaction of MgCl2 with Na2CO3 in supersaturated solutions between 273 and 363K was investigated.The compositions,morphologies and filtration characteristics of the precipitates were studied in detail.The magnesium carbonate hydrates obtained at 313K and in the range of 343-363K showed good morphologies and filtration characteristics.Magnesium oxides(MgO)with high purity(97.6%-99.4%)were obtained by calcining magnesium carbonate hydrates at 1073K.
文摘The selective precipitation of zinc from zinc-nickel sulfate solution with the Zn/Ni molar ratio of20:1was studied.Dropwise addition of0.5mol/L NaOH solution into the zinc-nickel sulfate solution containing0,0.01,0.02,0.03and0.04mol/L ethylene diamine tetraacetate(EDTA)as a chelating agent was done.The equilibrium analysis of precipitation pathway was performed using Visual MINTEQ program.The equilibrium analysis showed that the presence of small amounts of EDTA can prevent nickel precipitation in alkaline conditions without any negative effect on zinc precipitation.On this basis,more than90%of zinc could be precipitated as a product with about50%Zn and only0.11%Ni at pH=9.0merely as a result of the presence of0.03mol/L EDTA in the solution.The stirring time of120min after precipitation was found to be essential for more complete separation.The X-ray diffraction studies on the precipitate revealed that the precipitated phase was Zn4(OH)6SO4.4H2O.