Functionalized graphene nano-sheets(FGN) of 0.01%-0.05%(mass fraction) were added to produce FGN-cement composites in the form of mortars. Flow properties, mechanical properties and microstructure of the cementitious ...Functionalized graphene nano-sheets(FGN) of 0.01%-0.05%(mass fraction) were added to produce FGN-cement composites in the form of mortars. Flow properties, mechanical properties and microstructure of the cementitious material were then investigated. The results indicate that the addition of FGN decreases the fluidity slightly and improves mechanical properties of cement-based composites significantly. The highest strength is obtained with FGN content of 0.02% where the flexural strength and compressive strength at 28 days are 12.917 MPa and 52.42 MPa, respectively. Besides, scanning electron micrographs show that FGN can regulate formation of massive compact cross-linking structures and thermo gravimetric analysis indicates that FGN can accelerate the hydration reaction to increase the function of the composite effectively.展开更多
Invading track of chloride ions and chloride ion distribution rule in cement-based materials were investigated by partially soaking in 3.5% （mass fraction） NaCl solution and fully immerging in 3.5% and 5.0% （mass f...Invading track of chloride ions and chloride ion distribution rule in cement-based materials were investigated by partially soaking in 3.5% （mass fraction） NaCl solution and fully immerging in 3.5% and 5.0% （mass fraction） NaC1 solution, respectively, and relevant invading mechanisms were discussed. Results indicate that under full immerging condition, the invading track of chloride ions in cement mortar is similar to beeline that is vertical to chloride ion invading direction, and chloride ion content decreases rapidly with the increase of chloride ion invading depth. Under partial soaking condition, the invading track of chloride ion in cement mortar is similar to the shape of concave parabola, and chloride ion content decreases slowly along the lengthway direction of cement mortar samples in the distance of 20-80 mm from the bottom. Lots of chloride ions accumulate in cement mortar surface layer under the effect of capillary rise and evaporation and then invade cement mortar by diffusion effect. Under partial soaking condition, cement mortar is distinguished by four areas, i.e., immerging area, wet area, crystallization area and dry area.展开更多
基金Project(51102035)supported by the National Natural Science Foundation of China
文摘Functionalized graphene nano-sheets(FGN) of 0.01%-0.05%(mass fraction) were added to produce FGN-cement composites in the form of mortars. Flow properties, mechanical properties and microstructure of the cementitious material were then investigated. The results indicate that the addition of FGN decreases the fluidity slightly and improves mechanical properties of cement-based composites significantly. The highest strength is obtained with FGN content of 0.02% where the flexural strength and compressive strength at 28 days are 12.917 MPa and 52.42 MPa, respectively. Besides, scanning electron micrographs show that FGN can regulate formation of massive compact cross-linking structures and thermo gravimetric analysis indicates that FGN can accelerate the hydration reaction to increase the function of the composite effectively.
基金Project(50678174) supported by the National Natural Science Foundation of China
文摘Invading track of chloride ions and chloride ion distribution rule in cement-based materials were investigated by partially soaking in 3.5% （mass fraction） NaCl solution and fully immerging in 3.5% and 5.0% （mass fraction） NaC1 solution, respectively, and relevant invading mechanisms were discussed. Results indicate that under full immerging condition, the invading track of chloride ions in cement mortar is similar to beeline that is vertical to chloride ion invading direction, and chloride ion content decreases rapidly with the increase of chloride ion invading depth. Under partial soaking condition, the invading track of chloride ion in cement mortar is similar to the shape of concave parabola, and chloride ion content decreases slowly along the lengthway direction of cement mortar samples in the distance of 20-80 mm from the bottom. Lots of chloride ions accumulate in cement mortar surface layer under the effect of capillary rise and evaporation and then invade cement mortar by diffusion effect. Under partial soaking condition, cement mortar is distinguished by four areas, i.e., immerging area, wet area, crystallization area and dry area.