Two CaCO3-based materials （limestone and clamshells） and steel slag were used as mineral admixtures in cement to produce ternary blends and their influences on hydration and portlandite formation were analyzed. Addi...Two CaCO3-based materials （limestone and clamshells） and steel slag were used as mineral admixtures in cement to produce ternary blends and their influences on hydration and portlandite formation were analyzed. Additionally, mechanical properties were determined. These properties were determined using X-ray diffraction and scanning electron microscopic/energy dispersive X-ray analytical techniques as well as applying methods specified by EN （European Standards） and ASTM （American Standards for Testing and Materials）. The portlandite （Ca（OH）E） content was considerably reduced from 36.9% of reference cement to between 13.79% and 15.5%. With the water demand and setting times of the cements containing up to 10%, admixtures did not change significantly. The mechanical tests results showed that ternary blends produced 2-day strengths higher than that specified by EN 197-1 and that blends containing up to 20% admixtures can be used to produce both Class 32.5N and 42.5N cements.展开更多
An experimental investigation was conducted to study the efficiency of thermal insulation of composite PCMs （phase change materials） produced by vacuum impregnation process between paraffin （PCMs） and fly ash part...An experimental investigation was conducted to study the efficiency of thermal insulation of composite PCMs （phase change materials） produced by vacuum impregnation process between paraffin （PCMs） and fly ash particles. DSC （differential scanning calorimeter） has been used to determine the thermal properties of latent heat of melting and heat capacity for composite PCMs. Vacuum impregnation pressure of 40 in.Hg, paraffin melting temperature of 90℃, vacuum time and impregnation time of paraffin of 30 min are the optimum condition of composite PCMs productions. The values of latent heat of melting and heat capacity are 74.00 J/g and 15.726 J/g.℃ for composite PCMs that produces by the optimum condition in vacuum impregnation process. Increasing the amount of composite PCMs replacing for cement in mortars causes the compressive strength, flexural strength and tensile strength reduction. Compressive strength, flexural strength and tensile strength of mortar with and without composite PCMs can be increased by the longer time of water curing for mortar specimens. Thermal conductivity （k） of mortar cement is reduced by increasing the amount of composite PCMs which replaced for cement in mortar plate compositions. Composite PCMs have the efficiency for thermal energy insulation when incorporated into the buildings. Therefore, this property of paraffin/fly ash composites PCMs can reduce the energy consumption for temperature control in the buildings.展开更多
文摘Two CaCO3-based materials （limestone and clamshells） and steel slag were used as mineral admixtures in cement to produce ternary blends and their influences on hydration and portlandite formation were analyzed. Additionally, mechanical properties were determined. These properties were determined using X-ray diffraction and scanning electron microscopic/energy dispersive X-ray analytical techniques as well as applying methods specified by EN （European Standards） and ASTM （American Standards for Testing and Materials）. The portlandite （Ca（OH）E） content was considerably reduced from 36.9% of reference cement to between 13.79% and 15.5%. With the water demand and setting times of the cements containing up to 10%, admixtures did not change significantly. The mechanical tests results showed that ternary blends produced 2-day strengths higher than that specified by EN 197-1 and that blends containing up to 20% admixtures can be used to produce both Class 32.5N and 42.5N cements.
文摘An experimental investigation was conducted to study the efficiency of thermal insulation of composite PCMs （phase change materials） produced by vacuum impregnation process between paraffin （PCMs） and fly ash particles. DSC （differential scanning calorimeter） has been used to determine the thermal properties of latent heat of melting and heat capacity for composite PCMs. Vacuum impregnation pressure of 40 in.Hg, paraffin melting temperature of 90℃, vacuum time and impregnation time of paraffin of 30 min are the optimum condition of composite PCMs productions. The values of latent heat of melting and heat capacity are 74.00 J/g and 15.726 J/g.℃ for composite PCMs that produces by the optimum condition in vacuum impregnation process. Increasing the amount of composite PCMs replacing for cement in mortars causes the compressive strength, flexural strength and tensile strength reduction. Compressive strength, flexural strength and tensile strength of mortar with and without composite PCMs can be increased by the longer time of water curing for mortar specimens. Thermal conductivity （k） of mortar cement is reduced by increasing the amount of composite PCMs which replaced for cement in mortar plate compositions. Composite PCMs have the efficiency for thermal energy insulation when incorporated into the buildings. Therefore, this property of paraffin/fly ash composites PCMs can reduce the energy consumption for temperature control in the buildings.
