To understand the effect of steam curing temperature on the hydrate and microstructure of hardened cement paste,several measuring methods including X-ray diffraction(XRD),atomic absorption spectroscopy(ASS),ion chroma...To understand the effect of steam curing temperature on the hydrate and microstructure of hardened cement paste,several measuring methods including X-ray diffraction(XRD),atomic absorption spectroscopy(ASS),ion chromatography,conductivity meter,alternating-current impedance spectroscopy and nuclear magnetic resonance(NMR)are employed to investigate the hydration characteristics,pore solution composition and conductivity,resistivity and pore structure during the steam curing process.Experimental results show that steam curing promotes the hydration process,greatly raises the resistivity,and decreases the porosity of specimen at early age.Compared with being treated at 45℃,higher temperature leads to a fast decomposition of ettringite at initial stage of the constant temperature treatment period,which improves the relative content and ionic activity of the conductive ions in pore solution.Furthermore,the number of pores larger than 200 nm increases significantly,which reduces the resistivity of the hardened cement paste.Cement paste treated at 45℃ has a more stable and denser microstructure with less damages.展开更多
AC impedance spectroscopy in pure room temperature ionic liquids （RTILs） and RTIL-water mixture was measured at the temperature of range from 30 ℃ down to -30 ℃. The cations of RTILs are N,N-diethyl-N-methyl-N-（2...AC impedance spectroscopy in pure room temperature ionic liquids （RTILs） and RTIL-water mixture was measured at the temperature of range from 30 ℃ down to -30 ℃. The cations of RTILs are N,N-diethyl-N-methyl-N-（2-methoxyethyl） ammonium （[DEME]）, 1-ethyl-3-methylimidazolium （[C2mim]） and l-butyl-3-methylimidazolium （[Camim]）, the anions are tetrafluoroborate （[BF4]） and bis（trifluoromethanesulfonyl）imide （[TFSI]）. In all pure RTILs, there are two kinds of local minima in real part of the AC impedance Zreal. By adding water to [DEME][BF4] （0 mol% 〈 x 〈 94 mol%） at room temperature, the local minimum value at higher frequency decreased remarkably at the fixed frequency with increasing water concentration. Above 94 mol% H20, a quite different profile of the AC impedance spectroscopy was obtained. In addition to Zreal. temperature dependence of an imaginary part of the impedance Zimag had an isosbestic point below 94 mol%. The isosbestic point disappeared above 94 mol%. The isosbestic point in Zing reveals an interaction between [DEME][BFa] and H2O.展开更多
基金Projects(U1534207,11790283,51878583)supported by the National Natural Science Foundation of China。
文摘To understand the effect of steam curing temperature on the hydrate and microstructure of hardened cement paste,several measuring methods including X-ray diffraction(XRD),atomic absorption spectroscopy(ASS),ion chromatography,conductivity meter,alternating-current impedance spectroscopy and nuclear magnetic resonance(NMR)are employed to investigate the hydration characteristics,pore solution composition and conductivity,resistivity and pore structure during the steam curing process.Experimental results show that steam curing promotes the hydration process,greatly raises the resistivity,and decreases the porosity of specimen at early age.Compared with being treated at 45℃,higher temperature leads to a fast decomposition of ettringite at initial stage of the constant temperature treatment period,which improves the relative content and ionic activity of the conductive ions in pore solution.Furthermore,the number of pores larger than 200 nm increases significantly,which reduces the resistivity of the hardened cement paste.Cement paste treated at 45℃ has a more stable and denser microstructure with less damages.
文摘AC impedance spectroscopy in pure room temperature ionic liquids （RTILs） and RTIL-water mixture was measured at the temperature of range from 30 ℃ down to -30 ℃. The cations of RTILs are N,N-diethyl-N-methyl-N-（2-methoxyethyl） ammonium （[DEME]）, 1-ethyl-3-methylimidazolium （[C2mim]） and l-butyl-3-methylimidazolium （[Camim]）, the anions are tetrafluoroborate （[BF4]） and bis（trifluoromethanesulfonyl）imide （[TFSI]）. In all pure RTILs, there are two kinds of local minima in real part of the AC impedance Zreal. By adding water to [DEME][BF4] （0 mol% 〈 x 〈 94 mol%） at room temperature, the local minimum value at higher frequency decreased remarkably at the fixed frequency with increasing water concentration. Above 94 mol% H20, a quite different profile of the AC impedance spectroscopy was obtained. In addition to Zreal. temperature dependence of an imaginary part of the impedance Zimag had an isosbestic point below 94 mol%. The isosbestic point disappeared above 94 mol%. The isosbestic point in Zing reveals an interaction between [DEME][BFa] and H2O.