The Ni-Cr alloy electrodepositing technology on iron substrate in the chlorid-sulfate solution and the impacts of main processing parameters on coating composition were studied. The optimal Ni-Cr alloy electrodepositi...The Ni-Cr alloy electrodepositing technology on iron substrate in the chlorid-sulfate solution and the impacts of main processing parameters on coating composition were studied. The optimal Ni-Cr alloy electrodepositing conditions are that the cathode current density is 16 A/dm^2,the plating solution temperature is 30℃ and the pH value is 2.5. The bright, compact coating gained under the optimal conditions has good cohesion and 24.1% Cr content. The results show that the coating is composed of crystalline, the average grain size is 82 nm and the higher the Cr content of coating, the larger the rigidity, and the higher the corrosion resistance. The rigidity of coating reaches 78.6(HR30T) and the passivation area broadens to 1.4 V when the Cr content of coating is 24.1%.展开更多
A total of 28 yeast strains were obtained from the sea sediment of Antarctica.According to the results of routine identi-fication and molecular characterization,the strains belonged to species of Yarrowia lipolytica,D...A total of 28 yeast strains were obtained from the sea sediment of Antarctica.According to the results of routine identi-fication and molecular characterization,the strains belonged to species of Yarrowia lipolytica,Debaryomyces hansenii,Rhodotorula slooffiae,Rhodotorula mucilaginosa,Sporidiobolus salmonicolor,Aureobasidium pullulans,Mrakia frigida and Guehomyces pullu-lans,respectively.The Antarctica yeasts have wide potential applications in biotechnology,for some of them can produce b-galactosidase and killer toxins.展开更多
基金Project (59674025) supported by the National Natural Science Foundation of China
文摘The Ni-Cr alloy electrodepositing technology on iron substrate in the chlorid-sulfate solution and the impacts of main processing parameters on coating composition were studied. The optimal Ni-Cr alloy electrodepositing conditions are that the cathode current density is 16 A/dm^2,the plating solution temperature is 30℃ and the pH value is 2.5. The bright, compact coating gained under the optimal conditions has good cohesion and 24.1% Cr content. The results show that the coating is composed of crystalline, the average grain size is 82 nm and the higher the Cr content of coating, the larger the rigidity, and the higher the corrosion resistance. The rigidity of coating reaches 78.6(HR30T) and the passivation area broadens to 1.4 V when the Cr content of coating is 24.1%.
基金supported by the Hi-Tech Researchand Development Program of China(863),the grant No. is 2006AA09Z403
文摘A total of 28 yeast strains were obtained from the sea sediment of Antarctica.According to the results of routine identi-fication and molecular characterization,the strains belonged to species of Yarrowia lipolytica,Debaryomyces hansenii,Rhodotorula slooffiae,Rhodotorula mucilaginosa,Sporidiobolus salmonicolor,Aureobasidium pullulans,Mrakia frigida and Guehomyces pullu-lans,respectively.The Antarctica yeasts have wide potential applications in biotechnology,for some of them can produce b-galactosidase and killer toxins.