The alkaline leaching of arsenic (As2O3) by Na2S, together with its precipitation by Fe2(SO4)3 was studied. Response surface methodology based on central composite design was employed to quantify and qualify the effec...The alkaline leaching of arsenic (As2O3) by Na2S, together with its precipitation by Fe2(SO4)3 was studied. Response surface methodology based on central composite design was employed to quantify and qualify the effect of pertinent factors and to develop statistical models for optimization purposes. Based on the obtained results, 89% of arsenic is removed from the dust under following optimum predicted conditions: Na2S concentration of 100 g/L and solid to liquid ratio of 0.163 g/mL at 80 °C. It is found that solid to liquid ratio and Na2S concentration are the significant factors influencing the leaching process. In the precipitation process, more than 99.93% of arsenic from the leaching solution is removed in the form of amorphous ferric arsenate, at pH 4.8 when Fe3+ to arsenic and H2O2 to arsenic molar ratios are set at 5:1 and 4:1, respectively. Also, Fe3+ to arsenic ratio and pH are the most significant factors, and the interaction between these terms is significant.展开更多
Conventionally, multiple reference frame(MRF) method and sliding mesh(SM) method are used in the simulation of stirred tanks, however, both methods have limitations. In this study, a hybrid immersed-boundary(IB)techni...Conventionally, multiple reference frame(MRF) method and sliding mesh(SM) method are used in the simulation of stirred tanks, however, both methods have limitations. In this study, a hybrid immersed-boundary(IB)technique is developed in a finite difference context for the numerical simulation of stirred tanks. IBs based on Lagrangian markers and solid volume fractions are used for moving and stationary boundaries, respectively, to achieve optimal efficiency and accuracy. To cope with the high computational cost in the simulation of stirred tanks, the technique is implemented on computers with hybrid architecture where central processing units(CPUs) and graphics processing units(GPUs) are used together. The accuracy and efficiency of the present technique are first demonstrated in a relatively simple case, and then the technique is applied to the simulation of turbulent flow in a Rushton stirred tank with large eddy simulation(LES). Finally the proposed methodology is coupled with discrete element method(DEM) to accomplish particle-resolved simulation of solid suspensions in small stirred tanks. It demonstrates that the proposed methodology is a promising tool in simulating turbulent flow in stirred tanks with complex geometries.展开更多
In this research work, extraction and purification of germanium from zinc leach residues(ZLR) were investigated. The results of ICP, XRF, and atomic adsorption spectroscopy(AAS) tests show that contents of germanium, ...In this research work, extraction and purification of germanium from zinc leach residues(ZLR) were investigated. The results of ICP, XRF, and atomic adsorption spectroscopy(AAS) tests show that contents of germanium, iron, lead, and zinc within the leaching residue were 105×10^(-6), 3.53%, 10.35%, and 8.8%, respectively. XRD results indicate that the main minerals were in different forms of sulfates(CaSO_4·2H_2O, PbSO_4 and ZnSO_4·6H__2O), silicate(SiO_2), and oxide(Fe_2O_3). Dissolution of leaching filter cake was carried out using 5 parameters and each in 4 levels(acid concentration, temperature, time, liquid-to-solid ratio, and stirring speed) by Taguchi method(L_(16)), and then optimization of the effective parameters by response surface method. Under optimum conditions, zinc and germanium dissolution efficiencies were 88.71% and 8%, respectively. Leaching tests with sulfuric acid(added di-ammonium oxalate monohydrate) and hydrochloric acid(HCl) on the residues obtained from previous-stage sulfuric acid dissolution, yielded germanium and iron recoveries of 83%, 88%, 40%, and 90%, respectively. Thus, leaching experiment with sulfuric acid(added di-ammonium oxalate monohydrate) was superior to that with hydrochloric acid due to high and low extraction amounts of germanium and iron, respectively. Precipitation experiments revealed that germanium purification with tannic acid presented a better result compared to sodium hydroxide and ammonia. Under optimum conditions, contents of germanium and iron in the solution after precipitation were 0.1505% and 14.7% with precipitation yields of 91% and 52%, respectively.展开更多
Based on the existing form of Zn2 Si O4 in willemite, the chemical precipitation method was used to synthesize Zn2 Si O4.Through the orthogonal experimentation, the reaction conditions of melten Na OH decomposing Zn2 ...Based on the existing form of Zn2 Si O4 in willemite, the chemical precipitation method was used to synthesize Zn2 Si O4.Through the orthogonal experimentation, the reaction conditions of melten Na OH decomposing Zn2 Si O4 were optimized, and the optimal experimental conditions include reaction temperature of 400 °C, reaction time of 4 h, and alkaline-to-ore molar ratio of 20:1.Based on the optimized experiment, on-line detection for the alkali leaching was made by using Raman spectroscopy; XRD was used to analyze the structure of water leaching residue, to explore the reaction mechanism of Na OH decomposing Zn2 Si O4. The results show that during the reaction process, the Si — O bond in Si O4 is destroyed, and the Na OH inserts itself into the silicate lattice,producing an immediate Na2 Zn Si O4 product. After the alkali leaching process, Zn2+ can be separated from the Si O4 array, which can be released out of the silicate in the form of ZnO.展开更多
文摘The alkaline leaching of arsenic (As2O3) by Na2S, together with its precipitation by Fe2(SO4)3 was studied. Response surface methodology based on central composite design was employed to quantify and qualify the effect of pertinent factors and to develop statistical models for optimization purposes. Based on the obtained results, 89% of arsenic is removed from the dust under following optimum predicted conditions: Na2S concentration of 100 g/L and solid to liquid ratio of 0.163 g/mL at 80 °C. It is found that solid to liquid ratio and Na2S concentration are the significant factors influencing the leaching process. In the precipitation process, more than 99.93% of arsenic from the leaching solution is removed in the form of amorphous ferric arsenate, at pH 4.8 when Fe3+ to arsenic and H2O2 to arsenic molar ratios are set at 5:1 and 4:1, respectively. Also, Fe3+ to arsenic ratio and pH are the most significant factors, and the interaction between these terms is significant.
基金Supported by the National Natural Science Foundation of China(21225628,51106168,11272312)the“Strategic Priority Research Program”of the Chinese Academy of Sciences(XDA07080000)
文摘Conventionally, multiple reference frame(MRF) method and sliding mesh(SM) method are used in the simulation of stirred tanks, however, both methods have limitations. In this study, a hybrid immersed-boundary(IB)technique is developed in a finite difference context for the numerical simulation of stirred tanks. IBs based on Lagrangian markers and solid volume fractions are used for moving and stationary boundaries, respectively, to achieve optimal efficiency and accuracy. To cope with the high computational cost in the simulation of stirred tanks, the technique is implemented on computers with hybrid architecture where central processing units(CPUs) and graphics processing units(GPUs) are used together. The accuracy and efficiency of the present technique are first demonstrated in a relatively simple case, and then the technique is applied to the simulation of turbulent flow in a Rushton stirred tank with large eddy simulation(LES). Finally the proposed methodology is coupled with discrete element method(DEM) to accomplish particle-resolved simulation of solid suspensions in small stirred tanks. It demonstrates that the proposed methodology is a promising tool in simulating turbulent flow in stirred tanks with complex geometries.
文摘In this research work, extraction and purification of germanium from zinc leach residues(ZLR) were investigated. The results of ICP, XRF, and atomic adsorption spectroscopy(AAS) tests show that contents of germanium, iron, lead, and zinc within the leaching residue were 105×10^(-6), 3.53%, 10.35%, and 8.8%, respectively. XRD results indicate that the main minerals were in different forms of sulfates(CaSO_4·2H_2O, PbSO_4 and ZnSO_4·6H__2O), silicate(SiO_2), and oxide(Fe_2O_3). Dissolution of leaching filter cake was carried out using 5 parameters and each in 4 levels(acid concentration, temperature, time, liquid-to-solid ratio, and stirring speed) by Taguchi method(L_(16)), and then optimization of the effective parameters by response surface method. Under optimum conditions, zinc and germanium dissolution efficiencies were 88.71% and 8%, respectively. Leaching tests with sulfuric acid(added di-ammonium oxalate monohydrate) and hydrochloric acid(HCl) on the residues obtained from previous-stage sulfuric acid dissolution, yielded germanium and iron recoveries of 83%, 88%, 40%, and 90%, respectively. Thus, leaching experiment with sulfuric acid(added di-ammonium oxalate monohydrate) was superior to that with hydrochloric acid due to high and low extraction amounts of germanium and iron, respectively. Precipitation experiments revealed that germanium purification with tannic acid presented a better result compared to sodium hydroxide and ammonia. Under optimum conditions, contents of germanium and iron in the solution after precipitation were 0.1505% and 14.7% with precipitation yields of 91% and 52%, respectively.
基金Project(2007CB613603)supported by the National Basic Research Program of ChinaProject(51204037)supported by the National Natural Science Foundation of China
文摘Based on the existing form of Zn2 Si O4 in willemite, the chemical precipitation method was used to synthesize Zn2 Si O4.Through the orthogonal experimentation, the reaction conditions of melten Na OH decomposing Zn2 Si O4 were optimized, and the optimal experimental conditions include reaction temperature of 400 °C, reaction time of 4 h, and alkaline-to-ore molar ratio of 20:1.Based on the optimized experiment, on-line detection for the alkali leaching was made by using Raman spectroscopy; XRD was used to analyze the structure of water leaching residue, to explore the reaction mechanism of Na OH decomposing Zn2 Si O4. The results show that during the reaction process, the Si — O bond in Si O4 is destroyed, and the Na OH inserts itself into the silicate lattice,producing an immediate Na2 Zn Si O4 product. After the alkali leaching process, Zn2+ can be separated from the Si O4 array, which can be released out of the silicate in the form of ZnO.