Spinel-type manganese-cobalt oxides have been regarded as important class of electrocatalysts for oxygen reduction reaction(ORR).However,they are usually synthesized through oxidation-precipitation under aqueous ammon...Spinel-type manganese-cobalt oxides have been regarded as important class of electrocatalysts for oxygen reduction reaction(ORR).However,they are usually synthesized through oxidation-precipitation under aqueous ammonia and then crystallization at high temperature(150–180℃),which not only increases the energy consumption but also induces the growth of particles that is unfavorable for ORR.Herein,through a facile precipitation-dehydration method,ultrasmall spinel manganese-cobalt oxide nanoparticles(~5 nm)homogeneously dispersed on conductive carbon black(MnxCo3-xO4/C)were fabricated at low temperature(60℃).And the bimetallic composite oxide(Mn1.5Co1.5O4/C)with cubic spinel structure and high Mn content exhibits remarkable enhancement of ORR activity and stability compared with single metal oxide(both Mn3O4/C and Co3O4/C).The essential reason for the enhancement of activity can be attributed to the presence of the mixed Mn^3+ and Mn^4+ cations in Mn1.5Co1.5O4/C.Moreover,the ORR activity of Mn1.5Co1.5O4/C is comparable to that of commercial 20 wt% Pt/C,and the relative current density only decreases 1.4% after 12 h test,exceeding that of Pt/C and most reported manganese-cobalt oxide electrocatalysts.展开更多
文摘Spinel-type manganese-cobalt oxides have been regarded as important class of electrocatalysts for oxygen reduction reaction(ORR).However,they are usually synthesized through oxidation-precipitation under aqueous ammonia and then crystallization at high temperature(150–180℃),which not only increases the energy consumption but also induces the growth of particles that is unfavorable for ORR.Herein,through a facile precipitation-dehydration method,ultrasmall spinel manganese-cobalt oxide nanoparticles(~5 nm)homogeneously dispersed on conductive carbon black(MnxCo3-xO4/C)were fabricated at low temperature(60℃).And the bimetallic composite oxide(Mn1.5Co1.5O4/C)with cubic spinel structure and high Mn content exhibits remarkable enhancement of ORR activity and stability compared with single metal oxide(both Mn3O4/C and Co3O4/C).The essential reason for the enhancement of activity can be attributed to the presence of the mixed Mn^3+ and Mn^4+ cations in Mn1.5Co1.5O4/C.Moreover,the ORR activity of Mn1.5Co1.5O4/C is comparable to that of commercial 20 wt% Pt/C,and the relative current density only decreases 1.4% after 12 h test,exceeding that of Pt/C and most reported manganese-cobalt oxide electrocatalysts.