For the resource utilization of the solid waste coking sulfur paste and the improvement of performance of the asphalt mixture,a method for preparing modified asphalt mixture with coking sulfur paste modifier(CSPM)is h...For the resource utilization of the solid waste coking sulfur paste and the improvement of performance of the asphalt mixture,a method for preparing modified asphalt mixture with coking sulfur paste modifier(CSPM)is herein proposed.Compared with the matrix asphalt mixture,the Marshall stability of the 30%CSPM modified asphalt mixture increased by 38.3%,the dynamic stability increased by nearly one time(reaching 1847.5 times/mm),the splitting strength ratio increased by 39.3%while the splitting tensile strength decreased by 11.7%.After curing,the performance of the CSPM modified asphalt mixture was further improved.The results show that CSPM improved the high temperature stability and water damage resistance of the asphalt mixture,and the low-temperature anti-cracking performance of that was slightly reduced.Chemical analysis of asphalt binders shows that a little sulfur reacted with asphalt to produce polysulfide compounds(R-Sx-R′),and a part of sulfur existed in the form of crystalline sulfur which was further increased after curing.The presence of crystalline sulfur as an inorganic filler is the key point for improving the high temperature stability and water resistance performance of modified asphalt mixture.展开更多
Mesocarbon microbeads （MCMB） were prepared from coal tar pitch modified by phenolic resin and from the same pitch modified by phenolic resin and hexamethylenetetramine at 440℃ for lh. By investigating the morpholog...Mesocarbon microbeads （MCMB） were prepared from coal tar pitch modified by phenolic resin and from the same pitch modified by phenolic resin and hexamethylenetetramine at 440℃ for lh. By investigating the morphology of mesophase spheres and the structure of the MCMB carbonized at 1000℃ for lh using scanning electron microscope （SEM） and XRD, it was found that phenolic resin accelerated the formation and coalescence of mesophase spheres. Some of the obtained MCMB were hi- or tri-spheres with the distorted microtextural carbon layers. Hexamethylenetetramine in the pitch modified by phenolic resin accelerated the condensation of phenolic resin and consequently expedited the combination of mesophase spheres, which was proved by the formation of some tetra-spheres. Owing to the cross-linkage of the additives, MCMB with complex structure were obtained.展开更多
It is studied that reactivity of petroleum catalytic slurry （PCS） and coal with Fe catalyst in 1 L autoclave, the fol- lowing is mainly discussed, coal conversion and asphalt properties, especially related with petr...It is studied that reactivity of petroleum catalytic slurry （PCS） and coal with Fe catalyst in 1 L autoclave, the fol- lowing is mainly discussed, coal conversion and asphalt properties, especially related with petroleum cracking slurry （PCS） properties. The results show that co-processing conversion and asphalt yield increase with the increase of PCS ratio. PCS prop- erties have important effect on coal conversion and asphalt properties. One kind of PCS shows negative effect on coal conver- sion. High aromatic PCS can lead to high ductility asphalt with good colloid properties. Coal and the PCS can lead to a strong matching effect.展开更多
基金Project(201703D321006)supported by the Shanxi Provincial Key Research and Development Project(Social Development),China。
文摘For the resource utilization of the solid waste coking sulfur paste and the improvement of performance of the asphalt mixture,a method for preparing modified asphalt mixture with coking sulfur paste modifier(CSPM)is herein proposed.Compared with the matrix asphalt mixture,the Marshall stability of the 30%CSPM modified asphalt mixture increased by 38.3%,the dynamic stability increased by nearly one time(reaching 1847.5 times/mm),the splitting strength ratio increased by 39.3%while the splitting tensile strength decreased by 11.7%.After curing,the performance of the CSPM modified asphalt mixture was further improved.The results show that CSPM improved the high temperature stability and water damage resistance of the asphalt mixture,and the low-temperature anti-cracking performance of that was slightly reduced.Chemical analysis of asphalt binders shows that a little sulfur reacted with asphalt to produce polysulfide compounds(R-Sx-R′),and a part of sulfur existed in the form of crystalline sulfur which was further increased after curing.The presence of crystalline sulfur as an inorganic filler is the key point for improving the high temperature stability and water resistance performance of modified asphalt mixture.
基金Supported by the National Natural Science Foundation of China (No.50172034).
文摘Mesocarbon microbeads （MCMB） were prepared from coal tar pitch modified by phenolic resin and from the same pitch modified by phenolic resin and hexamethylenetetramine at 440℃ for lh. By investigating the morphology of mesophase spheres and the structure of the MCMB carbonized at 1000℃ for lh using scanning electron microscope （SEM） and XRD, it was found that phenolic resin accelerated the formation and coalescence of mesophase spheres. Some of the obtained MCMB were hi- or tri-spheres with the distorted microtextural carbon layers. Hexamethylenetetramine in the pitch modified by phenolic resin accelerated the condensation of phenolic resin and consequently expedited the combination of mesophase spheres, which was proved by the formation of some tetra-spheres. Owing to the cross-linkage of the additives, MCMB with complex structure were obtained.
文摘It is studied that reactivity of petroleum catalytic slurry （PCS） and coal with Fe catalyst in 1 L autoclave, the fol- lowing is mainly discussed, coal conversion and asphalt properties, especially related with petroleum cracking slurry （PCS） properties. The results show that co-processing conversion and asphalt yield increase with the increase of PCS ratio. PCS prop- erties have important effect on coal conversion and asphalt properties. One kind of PCS shows negative effect on coal conver- sion. High aromatic PCS can lead to high ductility asphalt with good colloid properties. Coal and the PCS can lead to a strong matching effect.