Rutting is one of the most damages in the asphalt surfaces for the orthotropic steel bridge decks. With Hamburg wheel tracking device, the suitable test conditions for Gussasphalt in Germany are pointed out, the high ...Rutting is one of the most damages in the asphalt surfaces for the orthotropic steel bridge decks. With Hamburg wheel tracking device, the suitable test conditions for Gussasphalt in Germany are pointed out, the high temperature behaviour of Gussasphalt with different binders are tested and compared. The polymer modified binder has higher resistance stability to rutting. The retained time and mixed frequency have obvious effects on Gussasphalt behaviour during Gussasphalt retained period.展开更多
Using a Hamburg wheel-track test device, the resistance to rutting of Gussasphalt is tested and compared. Gussasphalt with hard bitumen has good resistance to rutting. The related resistance abilities to cracking at ...Using a Hamburg wheel-track test device, the resistance to rutting of Gussasphalt is tested and compared. Gussasphalt with hard bitumen has good resistance to rutting. The related resistance abilities to cracking at low temperature of Gussasphalt are tested and compared through flexural experiments and the composite structure fatigue test with temperature dropping. Gussasphalt with high performance polymer modified bitumen has a longer fatigue life and a lower breaking temperature; they can be used in the future surfaces for steel bridge decks in Germany.展开更多
In this paper,organic montmorillonite(OMMT)was added into crumb rubber modified asphalt(CRMA)to improve its high temperature performance,anti-aging performance and storage stability.The effects of different OMMT conte...In this paper,organic montmorillonite(OMMT)was added into crumb rubber modified asphalt(CRMA)to improve its high temperature performance,anti-aging performance and storage stability.The effects of different OMMT content on properties of CRMA were studied.The rutting factor obtained by dynamic shear rheological(DSR)test was adopted to evaluate the high-temperature performance.The creep stiffness and m value determined by the bending beam rheometer(BBR)test were employed to evaluate the low-temperature performance.The softening point,ductility,rutting factor before and after rolling thin film ovens test(RTFOT)and pressure aging vessel test(PAV)were compared to characterize the aging properties.Moreover,the segregation test after being reserved for 48 h and 7 d was conducted,and the softening point and rutting factor of upper and lower layers of segregation pipe were adopted to evaluate the storage stability.The results indicated that the high-temperature performance and anti-aging performance were developed with the increasing content of OMMT,while the low-temperature performance deteriorated.The storage stability was improved with the increasing content of OMMT before the content exceeded 4%,after which the storage stability declined.Taking account of all factors,it is suggested that the optimum content of OMMT is 3%−4%.展开更多
文摘Rutting is one of the most damages in the asphalt surfaces for the orthotropic steel bridge decks. With Hamburg wheel tracking device, the suitable test conditions for Gussasphalt in Germany are pointed out, the high temperature behaviour of Gussasphalt with different binders are tested and compared. The polymer modified binder has higher resistance stability to rutting. The retained time and mixed frequency have obvious effects on Gussasphalt behaviour during Gussasphalt retained period.
文摘Using a Hamburg wheel-track test device, the resistance to rutting of Gussasphalt is tested and compared. Gussasphalt with hard bitumen has good resistance to rutting. The related resistance abilities to cracking at low temperature of Gussasphalt are tested and compared through flexural experiments and the composite structure fatigue test with temperature dropping. Gussasphalt with high performance polymer modified bitumen has a longer fatigue life and a lower breaking temperature; they can be used in the future surfaces for steel bridge decks in Germany.
基金Projects(51838001,51878070,51908069)supported by the National Natural Science Foundation of China。
文摘In this paper,organic montmorillonite(OMMT)was added into crumb rubber modified asphalt(CRMA)to improve its high temperature performance,anti-aging performance and storage stability.The effects of different OMMT content on properties of CRMA were studied.The rutting factor obtained by dynamic shear rheological(DSR)test was adopted to evaluate the high-temperature performance.The creep stiffness and m value determined by the bending beam rheometer(BBR)test were employed to evaluate the low-temperature performance.The softening point,ductility,rutting factor before and after rolling thin film ovens test(RTFOT)and pressure aging vessel test(PAV)were compared to characterize the aging properties.Moreover,the segregation test after being reserved for 48 h and 7 d was conducted,and the softening point and rutting factor of upper and lower layers of segregation pipe were adopted to evaluate the storage stability.The results indicated that the high-temperature performance and anti-aging performance were developed with the increasing content of OMMT,while the low-temperature performance deteriorated.The storage stability was improved with the increasing content of OMMT before the content exceeded 4%,after which the storage stability declined.Taking account of all factors,it is suggested that the optimum content of OMMT is 3%−4%.