A series of macroporous silicates with zeolitic microporous frameworks have been successfully prepared by self assembly of discrete colloidal crystals of silicalite 1, titanium silicalite 1(TS 1) and ZSM 5 , using pol...A series of macroporous silicates with zeolitic microporous frameworks have been successfully prepared by self assembly of discrete colloidal crystals of silicalite 1, titanium silicalite 1(TS 1) and ZSM 5 , using polystyrene(PS) spheres as templates. The properties of these novel materials were characterized by means of XRD, IR, SEM, 29 Si MAS NMR and N 2 adsorption/desorption measurements. These materials show ordered spheroidal voids, which are interconnected in three dimensions through windows. The ordering of the macropores are mainly affected by the particle size of the colloidal zeolites. [WT5HZ]展开更多
A TiO2 photocatalyst is coated on the surface of a zeolite fly ash bead（ZFAB） to improve its dispersability and exposure degree in a cement system.The application of Ag particles in TiO2/ZFAB modified cementitious m...A TiO2 photocatalyst is coated on the surface of a zeolite fly ash bead（ZFAB） to improve its dispersability and exposure degree in a cement system.The application of Ag particles in TiO2/ZFAB modified cementitious materials is to further enhance the photocatalytic performance.Various Ag@TiO2/ZFAB modified cementitious specimens with different Ag dosages are prepared and the characteristics and photocatalytic performance of the prepared samples are investigated.It is observed that the multi-level pore structure of ZFAB can improve the exposure degree of TiO2 in a cement system and is also useful to enhance the photocatalytic efficiency.With an increment of the amounts of Ag particles in the TiO2/ZFAB modified cementitious samples,the photocatalytic activities increased first and then decreased.The optimal Ag@TiO2/ZFAB modified cementitious sample reveals the maximum reaction rate constant for degrading benzene（9.91×10^-3 min^-1）,which is approximately 3 and 10 times higher than those of TiO2/ZFAB and TiO2 modified samples,respectively.This suggests that suitable Ag particles coupled with a ZFAB carrier could effectively enhance the photocatalytic effects and use of TiO2 in a cement system.Thus,ZFAB as a carrier could provide a potential method for a high efficiency engineering application of TiO2 in the construction field.展开更多
文摘A series of macroporous silicates with zeolitic microporous frameworks have been successfully prepared by self assembly of discrete colloidal crystals of silicalite 1, titanium silicalite 1(TS 1) and ZSM 5 , using polystyrene(PS) spheres as templates. The properties of these novel materials were characterized by means of XRD, IR, SEM, 29 Si MAS NMR and N 2 adsorption/desorption measurements. These materials show ordered spheroidal voids, which are interconnected in three dimensions through windows. The ordering of the macropores are mainly affected by the particle size of the colloidal zeolites. [WT5HZ]
基金supported by the National Natural Science Foundation of China (51478370)the Engineering and Physical Sciences Research Council of UK–Natural Science Foundation of China (EPSRC-NSFC) International Joint Research Project (51461135005)~~
文摘A TiO2 photocatalyst is coated on the surface of a zeolite fly ash bead（ZFAB） to improve its dispersability and exposure degree in a cement system.The application of Ag particles in TiO2/ZFAB modified cementitious materials is to further enhance the photocatalytic performance.Various Ag@TiO2/ZFAB modified cementitious specimens with different Ag dosages are prepared and the characteristics and photocatalytic performance of the prepared samples are investigated.It is observed that the multi-level pore structure of ZFAB can improve the exposure degree of TiO2 in a cement system and is also useful to enhance the photocatalytic efficiency.With an increment of the amounts of Ag particles in the TiO2/ZFAB modified cementitious samples,the photocatalytic activities increased first and then decreased.The optimal Ag@TiO2/ZFAB modified cementitious sample reveals the maximum reaction rate constant for degrading benzene（9.91×10^-3 min^-1）,which is approximately 3 and 10 times higher than those of TiO2/ZFAB and TiO2 modified samples,respectively.This suggests that suitable Ag particles coupled with a ZFAB carrier could effectively enhance the photocatalytic effects and use of TiO2 in a cement system.Thus,ZFAB as a carrier could provide a potential method for a high efficiency engineering application of TiO2 in the construction field.