泡沫铅对VRLA电池负极活性物质结构及性能影响

The surface morphology and composition of negative active material (NAM) both on the cast grid and on lead foam grid at the state of charge and discharge, in valve-regulated lead acid (VRLA) battery, were characterized by SEM and XRD, respectively. Moreover, the specific surface area and electrochemical impedance of the negative active material for both negative electrode grids were studied by chronoamperometry and EIS.The result indicates that after lots of cycles, compared with the cast grid, the sponge lead of the lead foam negative plate is smaller; the specific surface area increases by about 16%; the residual PbSO4 on the surface of the electrode is less at the state of charge. At the state of discharge, PbSO4 crystals on the surface of the negative plate of lead foam are smaller, and the specific surface area increases to 209%. EIS analysis shows that compared with the negative plate of cast grid, no matter what state the negative plate of lead foam is at, the electrochemical impedance of the material is lower.

泡沫铅对VRLA电池性能的影响

以泡沫铜为基体,采用电沉积铅制备泡沫铅板栅,并将其作为阀控密封铅酸电池的负极集流体,组装成负极限容的实验电池。对实验电池进行了充放电性能测试,结果表明:在20h、10h、5h和2h率放电情况下,泡沫铅电池与铸造板栅电池相比,质量比容量分别提高了23%、36%、35%和44%,活性物质利用率分别提高了5 03%、9 86%、8 79%和9 60%。

铅酸电池泡沫铅板栅材料的研究进展

阐述了铅酸电池泡沫铅板栅材料的制备方法及研究进展。重点介绍了泡沫铅板栅的结构、性能指标及对铅酸电池电化学性能的影响,展望了铅酸电池泡沫铅板栅材料的发展前景。

卷绕铅酸电池泡沫铅负极电化学行为的研究(英文)

以泡沫铅作为负极集流体制备了卷绕VRLA电池。采用计时电流法、循环伏安曲线、电化学阻抗谱和充放电实验研究了泡沫铅负极的电化学行为,结果表明:泡沫铅负极的真实表面积比铅箔负极的大,因此泡沫铅负极具有较低的过电势,并且不论是在怎样的放电状态下,泡沫铅负极的电化学反应电阻较小;与铅箔负极相比,在10、5和2小时率放电状态下,泡沫铅负极的质量比容量分别增加25.9%,30.0%和48.2%。此外,SEM观察显示,泡沫铅负极表面活性物质为更加细小的晶体颗粒和具有更高的孔率。

泡沫铅的制备及预制块的研究

对渗流铸造法制备泡沫铅及其关键———预制块的制备过程进行了实验研究。着重考察了预制块的粒径、松装密度、烧结温度、烧结时间和预制块组分间的配比五个因素对预制块孔隙率的影响 ,并采用渗流铸造法成功地制备出孔隙率为 4 3 .6%～ 73 .6%的泡沫铅 ,得到了泡沫铅的孔隙率与孔径 (取决于预制块的粒径 )之间的关系。

高性能铅酸电池用泡沫铅电沉积制备研究

研究了泡沫铅的电沉积过程,考察了铅离子浓度、氟硼酸浓度、硼酸浓度、添加剂、阴极表观电流密度及温度等因素对电流效率和泡沫铅产物质量的影响。确定了最佳工艺条件为:铅离子质量浓度115g/L,氟硼酸质量浓度35g/L,硼酸质量浓度25g/L,添加剂蛋白胨质量浓度1.0g/L,阴极表观电流密度300A/m2,温度25℃。经扫描电镜分析所得泡沫铅产物孔隙率高,表面平整,且为三维开孔结构,可作为高性能铅酸电池电极材料。

泡沫铅的制备、性能及应用研究的现状

介绍了泡沫铅材料的主要制备方法——渗流铸造法、粉体发泡法和电沉积法。阐述了泡沫铅用作铅酸电池板栅材料在提高活性物质利用率等方面的性能和应用研究情况。

泡沫铅板栅对VRLA电池充电接受能力的影响

以泡沫铅和铸造板栅为负极集流体,组装阀控铅酸(VRLA)蓄电池,并进行充放电循环测试,结果表明:在填涂相同的负极活性物质条件下,泡沫铅VRLA电池不仅负极活性物质利用率、容量高,并且充电接受能力好.对放电态的两种板栅负极分别进行循环伏安(CV)、电化学阻抗(EIS)测试和SEM观察,并采用计时安培法测量了两种负极的真实表面积.结果表明,放电态泡沫铅负极的氧化峰的峰值电势较负,还原峰的峰值电势略正,泡沫铅负极氧化峰、还原峰的峰值电流更大,放电态的泡沫铅负极的电化学反应电阻小,真实表面积大,活性物质中的PbSO4结晶颗粒较小,表明泡沫铅有利于提高VRLA电池的充电接受能力.

泡沫铅制备工艺研究

研究了电沉积法制备泡沫铅的工艺,以聚氨酯泡沫为基体,经脱脂-粗化-除膜-导电化处理后,先预镀铜然后再电沉积铅。在预镀铜过程中,考察了阴极电流密度、异极极距、镀液温度和电镀时间对电流效率和槽电压的影响,得到了最佳的镀铜工艺参数为:阴极电流密度3.0 A/dm2、异极极距3.5 cm、镀液温度为25℃、电镀时间35 min。在电沉积铅过程中,考察了铅离子浓度、氟硼酸浓度、添加剂、阴极电流密度及温度和时间等因素对电流效率、槽电压和泡沫铅产品质量的影响,确定了最佳工艺条件为:阴极表观电流密度3.0 A/dm2、镀液温度为25℃、电镀时间30～50 min。在优化条件下制备的泡沫铅镀层结晶细密、均匀,且韧性和光亮性都较好,孔隙率高,具有三维网状结构。

泡沫铅板栅的比表面积对铅酸电池性能的影响

本工作以聚氨酯泡沫为原材料,经玻璃炭化后制成的泡沫铅板栅具有比普通板栅高几十倍的比表面积。通过对聚氨酯泡沫基材孔数和正极泡沫板栅镀铅量的对比实验,优化筛选出聚氨酯泡沫基材孔数为15 PPI,正极板栅镀铅量为20 g的工艺方案。优选方案制成的泡沫铅正板栅比表面积为19.1 cm^2/cm^3,镀层厚度为39.1μm;相对的泡沫负板栅比表面积为33.1 cm^2/cm^3,镀层厚度为13.3μm。泡沫板栅具有提升活性物质利用率,提高铅酸电池比能量的特性,且制成的电动助力车电池大电流放电性能和循环寿命都能满足国家标准的要求。

铅精炼大极板工艺“泡沫铅”的产生及处理

分析了阳极板铸造过程中生成"泡沫铅"原因,及"泡沫铅"在铅电解生产中所造成的危害,通过对除铜操作工艺的调整、立模铸造温度的调整、立模浇铸速度的调整,最终不但彻底消除隐患,而且通过挖潜,提高了立模铸造的产能。

铅衣泡沫清洗液对介入辐射防护用品铅衣表面清洁效果的研究

目的:评估铅衣泡沫清洗液对介入辐射防护用品铅衣表面的清洁效果。方法:将宁波市第一医院介入诊疗中心2019年6月至2020年5月电生理组介入手术使用后的48件介入防护用品铅衣按照随机数字表法分成A组和B组,每组24件。A组采用铅衣泡沫清洗液清洁,B组采用37℃温水清洁,比较2种清洁方法的清洁效果。结果:2组介入辐射防护用品铅衣物体表面清洁合格率分别为91.67%和62.50%;清洁后2组介入辐射防护用品铅衣物体表面细菌菌落数分别为(1.71±0.22)cfu/cm^(2)和(4.08±0.33)cfu/cm^(2);2组介入辐射防护用品铅衣平均物体表面细菌减少率分别为83.80%和62.47%;2组每件介入辐射防护用品铅衣清洁平均耗时(10.36±1.07)min和(16.25±1.81)min, A组清洁方法清洁效果优于B组,差异有统计学意义(P<0.05)。结论:铅衣泡沫清洗液清洁效果优于37℃温水清洁效果,且耗时短,能有效提高工作人员清洁铅衣的效率且符合安全性能检测要求,适合介入辐射防护用品铅衣的日常维护清洁,可推广使用。

泡沫材料的最新研究进展

综述了泡沫铝、泡沫钛、泡沫硅和泡沫铅等材料的制备方法,以及如何控制材料的组成和孔隙率来制备不同性能的材料,重点介绍了这些泡沫材料在汽车工业、人体植入材料、光学材料、微电子、计算机和铅酸电池等方面表现出来的优异性能,并展望其广阔的市场前景。

铅蓄电池板栅材料的研究发展现状

叙述了铅蓄电池板栅的特点及其功能,介绍了几种常见材料的铅蓄电池板栅以及部分最新的板栅材料,并重点阐述了泡沫铅板栅的特点与性能;综述了国内外板栅材料的发展状况,并展望了铅电池板栅材料的发展方向及其市场前景。

真空渗流法制备的通孔泡沫铝的吸声性能

研究了真空渗流法制备的通孔泡沫铝的吸声性能、通孔泡沫铝的孔结构参数及厚度对通孔泡沫铝吸声性能的影响。试验结果表明 ,真空渗流法制备的通孔泡沫铝具有较大的吸声系数 ,而且随孔径减小或孔隙率、厚度增加 。

铅酸电池轻量化板栅的失效机理

为了提高铅酸电池的能量密度和寿命,发展轻量化的板栅以取代比重大的铅板栅,具有重要的实际意义。铅酸电池用轻量化板栅的失效主要是由板栅在电化学环境下腐蚀所引起的。因此,板栅在酸性条件下抗电化学腐蚀的能力对铅酸电池的性能和寿命有很大的影响。笔者总结了轻质金属板栅、轻质合金板栅和铅炭板栅的发展状况,以及其用于铅酸电池时的失效机理,并论述了板栅失效对铅酸电池机械强度和寿命的影响。为了促进耐腐蚀的轻量化板栅的研发,还提出了几个未来可能的研发方向。

铅酸电池极板制备方法的研究进展

本文针对传统铅酸电池极板铅密度大、利用率低、极板容易腐蚀坍塌等常见问题,介绍几种比较有开发价值的制备铅酸蓄电池极板的方法,着重总结各个制备方法的流程工艺,从提高电池的重量比能量,循环寿命和充放电能力等方面,讨论了各种方法制备的电池的性能,对它们的制备方法的发展进行概述及展望,并提出了一种铝材料的拉网式基板结构。