A solution of 0.1 mol/L to 1.0 mol/L H2SO4 can dissolve alkali metals and alkaline earth metals which weaken an active site of SCR catalyst. The waste catalyst washed with 0.5 mol/L H2SO4 regained the best catalytic a...A solution of 0.1 mol/L to 1.0 mol/L H2SO4 can dissolve alkali metals and alkaline earth metals which weaken an active site of SCR catalyst. The waste catalyst washed with 0.5 mol/L H2SO4 regained the best catalytic activity. When a concentration of the sulfuric acid is less than 0.5 mol/L, sufficient cleaning effects cannot be obtained. In contrast, when the concentration is greater than 1.0 tool/L, the active components, vanadium and tungsten are undesirably eluted. The total BET surface of the catalyst regenerated by air lift loop reactor showed almost the same as that of fresh catalyst due to the removal of insoluble compounds which may be penetrated into pores of catalyst. The addition of a solution of 0.075 mol/L ammonium vanadate （NHnVO3） and 0.075 mol/L ammonium paratungstate （5（NH4）20· 12WO3-5H20） to 0.1 mol/L H2SO4 significantly increases the activity of the waste catalyst.展开更多
Epoxidation of cyclohexene to cyclohexene oxide was studied in a new type reactor—the ultrasound airlift loop reactor. The influences of ultrasound intensity, molar ratio of isobutyraldehyde to cyclohexene and oxy-ge...Epoxidation of cyclohexene to cyclohexene oxide was studied in a new type reactor—the ultrasound airlift loop reactor. The influences of ultrasound intensity, molar ratio of isobutyraldehyde to cyclohexene and oxy-gen gas flow rate on the conversion of cyclohexene and selectivity of cyclohexene oxide were investigated and dis-cussed, and the optimal operation condition was found, under which 95.2% conversion of cyclohexene and 90.7% selectivity of cyclohexene oxide were achieved. The ultrasonic airlift loop reactor utilizes the synergistic effect of sonochemsitry and higher oxygen transfer rate. Possible reaction mechanisms were outlined and the reason of ul-trasound promotion of epoxidation reactionwas analyzed.展开更多
Combined technology of SDS-CuO/TiO2 photocatalysis and sequencing batch reactor （SBR） were applied to treating dyestuff wastewater. Photocatalysis was carried out in a spiral up-flow type reactor as pre-treatment. S...Combined technology of SDS-CuO/TiO2 photocatalysis and sequencing batch reactor （SBR） were applied to treating dyestuff wastewater. Photocatalysis was carried out in a spiral up-flow type reactor as pre-treatment. SDS-CuO/TiO2 photocatalyst was prepared by modification of nano-TiO2 using CuO and sodium dodecyl sulfate （SDS）. Results show that the SDS-CuO/TiO2 photocatalyst contains two kinds of crystals, including TiO2 and CuO. The band gap of this photocatalyst is 1.56 eV, indicating that it can be excited by visible light （2〈794.87 nm）. And characterization also shows that there are alkyl groups on its surface. It takes 40 rain to improve the biodegradability of dyestuff wastewater. Five-day biochemical oxygen demand （BODs） and dehydrogenase activity （DHA） of wastewater reach the maximum value when dissolved oxygen is higher than 2.97 mg/L. SBR reactor was used to treat this biodegradability improved wastewater. Chemical oxygen demand （COD） and colority decline to 72 mg/L and 20 times, respectively, when the sludge loading is 0.179 kg（COD）/[kg（MLSS）＇d], dissolved oxygen is 4.09 mg/L and aeration time is 10 h.展开更多
基金Project(2009T100100602) supported by the Korea Institute of Energy Technology Evaluation and Planning,Korea
文摘A solution of 0.1 mol/L to 1.0 mol/L H2SO4 can dissolve alkali metals and alkaline earth metals which weaken an active site of SCR catalyst. The waste catalyst washed with 0.5 mol/L H2SO4 regained the best catalytic activity. When a concentration of the sulfuric acid is less than 0.5 mol/L, sufficient cleaning effects cannot be obtained. In contrast, when the concentration is greater than 1.0 tool/L, the active components, vanadium and tungsten are undesirably eluted. The total BET surface of the catalyst regenerated by air lift loop reactor showed almost the same as that of fresh catalyst due to the removal of insoluble compounds which may be penetrated into pores of catalyst. The addition of a solution of 0.075 mol/L ammonium vanadate （NHnVO3） and 0.075 mol/L ammonium paratungstate （5（NH4）20· 12WO3-5H20） to 0.1 mol/L H2SO4 significantly increases the activity of the waste catalyst.
基金Supported by Qinglan Project Foundation of Jiangsu Province and Doctoral Dissertation Innovate Foundation of Nanjing Uni-versity of Technology (No.BSCS200508).
文摘Epoxidation of cyclohexene to cyclohexene oxide was studied in a new type reactor—the ultrasound airlift loop reactor. The influences of ultrasound intensity, molar ratio of isobutyraldehyde to cyclohexene and oxy-gen gas flow rate on the conversion of cyclohexene and selectivity of cyclohexene oxide were investigated and dis-cussed, and the optimal operation condition was found, under which 95.2% conversion of cyclohexene and 90.7% selectivity of cyclohexene oxide were achieved. The ultrasonic airlift loop reactor utilizes the synergistic effect of sonochemsitry and higher oxygen transfer rate. Possible reaction mechanisms were outlined and the reason of ul-trasound promotion of epoxidation reactionwas analyzed.
基金Project(CDJZR11210009) supported by the Fundamental Research Funds for the Central Universities of China
文摘Combined technology of SDS-CuO/TiO2 photocatalysis and sequencing batch reactor （SBR） were applied to treating dyestuff wastewater. Photocatalysis was carried out in a spiral up-flow type reactor as pre-treatment. SDS-CuO/TiO2 photocatalyst was prepared by modification of nano-TiO2 using CuO and sodium dodecyl sulfate （SDS）. Results show that the SDS-CuO/TiO2 photocatalyst contains two kinds of crystals, including TiO2 and CuO. The band gap of this photocatalyst is 1.56 eV, indicating that it can be excited by visible light （2〈794.87 nm）. And characterization also shows that there are alkyl groups on its surface. It takes 40 rain to improve the biodegradability of dyestuff wastewater. Five-day biochemical oxygen demand （BODs） and dehydrogenase activity （DHA） of wastewater reach the maximum value when dissolved oxygen is higher than 2.97 mg/L. SBR reactor was used to treat this biodegradability improved wastewater. Chemical oxygen demand （COD） and colority decline to 72 mg/L and 20 times, respectively, when the sludge loading is 0.179 kg（COD）/[kg（MLSS）＇d], dissolved oxygen is 4.09 mg/L and aeration time is 10 h.