The effects of pouring temperature,vibration frequency,and the number of curves in a serpentine channel,on themicrostructure and mechanical properties of Al-30%Si alloy processed by rheo-diecasting(RDC)were investigat...The effects of pouring temperature,vibration frequency,and the number of curves in a serpentine channel,on themicrostructure and mechanical properties of Al-30%Si alloy processed by rheo-diecasting(RDC)were investigated.The semisolidAl-30%Si alloy slurry was prepared by vibration serpentine channel pouring(VSCP)process in the RDC process.The results showthat the pouring temperature,the vibration frequency,and the number of the curves strongly affect the microstructure and mechanicalproperties of Al-30%Si alloy.Under experimental conditions of a pouring temperature of850°C,a twelve-curve copper channel anda vibration frequency of80Hz,the primary Si grains are refined into fine compact grains with average grain size of about24.6μm inthe RDC samples assisted with VSCP.Moreover,the ultimate tensile strength(UTS),elongation and hardness of the RDC sample are296MPa,0.87%and HB155,respectively.It is concluded that the VSCP process can effectively refine the primary Si grains.Therefinement of primary Si grains is the major cause for the improvement of the mechanical properties of the RDC sample.展开更多
基金Project(5077400) supported by the National Natural Science Foundation of China
文摘The effects of pouring temperature,vibration frequency,and the number of curves in a serpentine channel,on themicrostructure and mechanical properties of Al-30%Si alloy processed by rheo-diecasting(RDC)were investigated.The semisolidAl-30%Si alloy slurry was prepared by vibration serpentine channel pouring(VSCP)process in the RDC process.The results showthat the pouring temperature,the vibration frequency,and the number of the curves strongly affect the microstructure and mechanicalproperties of Al-30%Si alloy.Under experimental conditions of a pouring temperature of850°C,a twelve-curve copper channel anda vibration frequency of80Hz,the primary Si grains are refined into fine compact grains with average grain size of about24.6μm inthe RDC samples assisted with VSCP.Moreover,the ultimate tensile strength(UTS),elongation and hardness of the RDC sample are296MPa,0.87%and HB155,respectively.It is concluded that the VSCP process can effectively refine the primary Si grains.Therefinement of primary Si grains is the major cause for the improvement of the mechanical properties of the RDC sample.