With no annealing treatment, cathodic polarization trends in 5083F A1 alloy revealed concentration polarization and activation polarization. However, the annealed specimens have lower current densities at corrosion pr...With no annealing treatment, cathodic polarization trends in 5083F A1 alloy revealed concentration polarization and activation polarization. However, the annealed specimens have lower current densities at corrosion protection potential compared to the non-annealed specimen. The results of SSRTs conducted in seawater at the applied potential range of-l.8 V to -0.5 V indicated that the maximum tensile strength, elongation, and time-to-fracture had high values at applied potentials of -0.7 to -1.4 V. The maximum tensile strength, elongation, and time-to-f？acture decreased when the potential values were beyond this range in either anodic or cathodic direction. In general, the increased shear lip caused by annealing treatment indicates elongation. Time-to-fracture would likely increase with elongation. Potentials between -0.5 V to -0.6 V were found to be in the region of stress corrosion cracking. The corrosion protection zone was determined to be -0.7 V to -J,4 V because these potential ranges produced good mechanical properties. Potential less than -1.4 V produced a fractured surface with a mixture of dimples （ductile fractures） and a quasi-cleavage pattern resulting from the effects of hydrogen gas.展开更多
Strongly acidic soils （pH 〈 5.0） are detrimental to tea （Camellia sinensis） production and quality. Little information exists on the ability of surface amendments to ameliorate subsoil acidity in the tea garden s...Strongly acidic soils （pH 〈 5.0） are detrimental to tea （Camellia sinensis） production and quality. Little information exists on the ability of surface amendments to ameliorate subsoil acidity in the tea garden soils. A 120-d glasshouse column leaching experiment was conducted using commonly available soil ameliorants. Alkaline slag （AS） and organic residues, pig manure （PM） and rapeseed cake （RC） differing in ash alkalinity and C/N ratio were incorporated alone and in combination into the surface （0-15 cm） of soil columns （10 cm internal diameter x 50 cm long） packed with soil from the acidic soil layer （15-30 cm） of an Ultisol （initial pH -- 4.4）. During the 120-d experiment, the soil columns were watered （about 127 mm over 9 applications） according to the long-term mean annual rainfall （1 143 mm） and the leachates were collected and analyzed. At the end of the experiment, soil columns were partitioned into various depths and the chemical properties of soil were measured. The PM with a higher C/N ratio increased subsoil pH, whereas the RC with a lower C/N ratio decreased subsoil pH. However, combined amendments had a greater ability to reduce subsoil acidity than either of the amendments alone. The increases in pH of the subsoil were mainly ascribed to decreased base cation concentrations and the decomposition of organic anions present in dissolved organic carbon （DOC） and immobilization of nitrate that had been leached down from the amended layer. A significant （P 〈 0.05） correlation between alkalinity production （reduced exchangeable acidity - N-cycle alkalinity） and alkalinity balance （net alkalinity production - N-cycle alkalinity） was observed at the end of the experiment. Additionally, combined amendments significantly increased （P ~ 0.05） subsoil cation concentrations and decreased subsoil A1 saturation （P 〈 0.05）. Combined applications of AS with organic amendments to surface soils are effective in reducing subsoil acidity in high-rainfall areas. Further investigations under field conditions and over longer timeframes are needed to fully understand their practical effectiveness in ameliorating acidity of deeper soil layers under naturally occurring leaching regimes.展开更多
文摘With no annealing treatment, cathodic polarization trends in 5083F A1 alloy revealed concentration polarization and activation polarization. However, the annealed specimens have lower current densities at corrosion protection potential compared to the non-annealed specimen. The results of SSRTs conducted in seawater at the applied potential range of-l.8 V to -0.5 V indicated that the maximum tensile strength, elongation, and time-to-fracture had high values at applied potentials of -0.7 to -1.4 V. The maximum tensile strength, elongation, and time-to-f？acture decreased when the potential values were beyond this range in either anodic or cathodic direction. In general, the increased shear lip caused by annealing treatment indicates elongation. Time-to-fracture would likely increase with elongation. Potentials between -0.5 V to -0.6 V were found to be in the region of stress corrosion cracking. The corrosion protection zone was determined to be -0.7 V to -J,4 V because these potential ranges produced good mechanical properties. Potential less than -1.4 V produced a fractured surface with a mixture of dimples （ductile fractures） and a quasi-cleavage pattern resulting from the effects of hydrogen gas.
基金This study was supported by the National Natural Science Foundation of China （No. 41401336）, the Na- tural Science Foundation of Jiangsu Province, China （No. BK20130105）, the State Key Laboratory of Soil and Sustainable Agriculture, Chinese Academy of Sci-ence （No. Y412201452）, and the Environmental Pro- tection Public Benefit Research Foundation of China （No. 201309036）. We thank the three anonymous refe- rees for their helpful comments.
文摘Strongly acidic soils （pH 〈 5.0） are detrimental to tea （Camellia sinensis） production and quality. Little information exists on the ability of surface amendments to ameliorate subsoil acidity in the tea garden soils. A 120-d glasshouse column leaching experiment was conducted using commonly available soil ameliorants. Alkaline slag （AS） and organic residues, pig manure （PM） and rapeseed cake （RC） differing in ash alkalinity and C/N ratio were incorporated alone and in combination into the surface （0-15 cm） of soil columns （10 cm internal diameter x 50 cm long） packed with soil from the acidic soil layer （15-30 cm） of an Ultisol （initial pH -- 4.4）. During the 120-d experiment, the soil columns were watered （about 127 mm over 9 applications） according to the long-term mean annual rainfall （1 143 mm） and the leachates were collected and analyzed. At the end of the experiment, soil columns were partitioned into various depths and the chemical properties of soil were measured. The PM with a higher C/N ratio increased subsoil pH, whereas the RC with a lower C/N ratio decreased subsoil pH. However, combined amendments had a greater ability to reduce subsoil acidity than either of the amendments alone. The increases in pH of the subsoil were mainly ascribed to decreased base cation concentrations and the decomposition of organic anions present in dissolved organic carbon （DOC） and immobilization of nitrate that had been leached down from the amended layer. A significant （P 〈 0.05） correlation between alkalinity production （reduced exchangeable acidity - N-cycle alkalinity） and alkalinity balance （net alkalinity production - N-cycle alkalinity） was observed at the end of the experiment. Additionally, combined amendments significantly increased （P ~ 0.05） subsoil cation concentrations and decreased subsoil A1 saturation （P 〈 0.05）. Combined applications of AS with organic amendments to surface soils are effective in reducing subsoil acidity in high-rainfall areas. Further investigations under field conditions and over longer timeframes are needed to fully understand their practical effectiveness in ameliorating acidity of deeper soil layers under naturally occurring leaching regimes.