In this paper,1-butyl-3-methylimidazole tetrafluoroborate([BMIM]BF4)is used as corrosion inhibitor.Polyacrylonitrile(PAN)is used to load the corrosion inhibitor.PAN/[BMIM]BF4 hybrid nanofibers are successfullysynthesi...In this paper,1-butyl-3-methylimidazole tetrafluoroborate([BMIM]BF4)is used as corrosion inhibitor.Polyacrylonitrile(PAN)is used to load the corrosion inhibitor.PAN/[BMIM]BF4 hybrid nanofibers are successfullysynthesized by electrospinning technology.The alkyd varnish is coated on the fiber membrane to prepare a compositecoating,and then a series of tests are carried out on the self-healing and anticorrosive performance of the compositecoating.It is observed by scanning electron microscope that the fiber morphology is stable and there is no bead-likestructure.The composition of the composite fiber is analyzed by Fourier infrared spectroscopy,and it is confirmed thatthe hybrid nanofiber was successfully prepared.3D laser confocal scanning microscope was used to observe thecorrosion morphology and profile of the carbon steel.The composite coating shows good self-healing performance.[BMIM]BF4 can form a protective film on the surface of the bare carbon steel substrate through physical adsorption orchemical adsorption in an alkaline environment.Electrochemical impedance spectroscopy was tested and analyzed.It isfound that the maximum corrosion inhibition efficiency of the coating is 88.5%in 3.5 wt.%alkaline NaCl solution.Compared with the blank coating without nanofibers,the composite fiber varnish composite coating exhibits good selfhealingand anti-corrosion properties.展开更多
A Schiff base(a compound containing a C=N bond)induced anodic Ca−P coating was prepared on AZ31 Mg alloy in a mixed solution of CaCl_(2) and KH_(2)PO_(4) at 60℃ in the presence of glucose and L-cysteine.The microstru...A Schiff base(a compound containing a C=N bond)induced anodic Ca−P coating was prepared on AZ31 Mg alloy in a mixed solution of CaCl_(2) and KH_(2)PO_(4) at 60℃ in the presence of glucose and L-cysteine.The microstructure and chemical composition of the coatings were characterized using FE-SEM,FT-IR,XRD,and XPS.The in vitro degradation resistance of the coated samples was evaluated via potentiodynamic polarization(PDP),electrochemical impedance spectroscopy(EIS),and hydrogen evolution test.The experimental results show that the Ca−PSchiff base coating is composed of CaHPO_(4)(DCPA)and hydroxyapatite(HA),whereas HA is not present in the Ca−P coating.The Ca−P_(Schiff base) coating thickness is about 2 times that of Ca−P coating(Ca−P coating:(9.13±4.20)μm and Ca−P_(Schiff base):(18.13±5.78)μm).The corrosion current density of the Ca−P_(Schiff base) coating is two orders of magnitude lower than that of the Ca−P coating.The formation mechanism of the Ca−P_(Schiff base) is proposed.展开更多
基金Projects(42076039,42106042)supported by the National Natural Science Foundation of ChinaProject(202165004)supported by the Fundamental Research Funds for the Central Universities,ChinaProject(JC12022106)supported by 2022 Innovation Project for Young Scientific and Technological Talents in Basic Science Research,China。
文摘In this paper,1-butyl-3-methylimidazole tetrafluoroborate([BMIM]BF4)is used as corrosion inhibitor.Polyacrylonitrile(PAN)is used to load the corrosion inhibitor.PAN/[BMIM]BF4 hybrid nanofibers are successfullysynthesized by electrospinning technology.The alkyd varnish is coated on the fiber membrane to prepare a compositecoating,and then a series of tests are carried out on the self-healing and anticorrosive performance of the compositecoating.It is observed by scanning electron microscope that the fiber morphology is stable and there is no bead-likestructure.The composition of the composite fiber is analyzed by Fourier infrared spectroscopy,and it is confirmed thatthe hybrid nanofiber was successfully prepared.3D laser confocal scanning microscope was used to observe thecorrosion morphology and profile of the carbon steel.The composite coating shows good self-healing performance.[BMIM]BF4 can form a protective film on the surface of the bare carbon steel substrate through physical adsorption orchemical adsorption in an alkaline environment.Electrochemical impedance spectroscopy was tested and analyzed.It isfound that the maximum corrosion inhibition efficiency of the coating is 88.5%in 3.5 wt.%alkaline NaCl solution.Compared with the blank coating without nanofibers,the composite fiber varnish composite coating exhibits good selfhealingand anti-corrosion properties.
基金supported by the National Natural Science Foundation of China(No.52071191)the Open Foundation of Hubei Key Laboratory of Advanced Technology for Automotive Components,China(No.XDQCKF2021006)。
文摘A Schiff base(a compound containing a C=N bond)induced anodic Ca−P coating was prepared on AZ31 Mg alloy in a mixed solution of CaCl_(2) and KH_(2)PO_(4) at 60℃ in the presence of glucose and L-cysteine.The microstructure and chemical composition of the coatings were characterized using FE-SEM,FT-IR,XRD,and XPS.The in vitro degradation resistance of the coated samples was evaluated via potentiodynamic polarization(PDP),electrochemical impedance spectroscopy(EIS),and hydrogen evolution test.The experimental results show that the Ca−PSchiff base coating is composed of CaHPO_(4)(DCPA)and hydroxyapatite(HA),whereas HA is not present in the Ca−P coating.The Ca−P_(Schiff base) coating thickness is about 2 times that of Ca−P coating(Ca−P coating:(9.13±4.20)μm and Ca−P_(Schiff base):(18.13±5.78)μm).The corrosion current density of the Ca−P_(Schiff base) coating is two orders of magnitude lower than that of the Ca−P coating.The formation mechanism of the Ca−P_(Schiff base) is proposed.