润滑油对制冷系统的影响

讨论了润滑油与制冷剂的互溶对制冷系统性能的影响。润滑油与制冷剂的热物理性质相差很大,因而进入循环后必然会引起制冷剂流动、换热系数和压降的变化。分析了制冷剂在制冷系统各部件内循环流动时,含油量对系统性能的影响及机理。总体来讲,少量的润滑油对系统的制冷效果是有利的,但含油量过大则会降低制冷量,并对系统产生许多不利的影响。

煤矿机电设备的使用、维护、保养与计划检修

本文从煤矿机电设备的选型、工作环境、工作条件、设备的效能、润滑制、包机制及设备的维护、保养与计划检修等对设备的合理使用和日常管理进行了探讨并结合实际提出了一些改进措施。

Parametric analysis of mixed lubrication characteristics in work zone of strip rolling

A theoretical model for mixed lubrication with more accurate contact length has been developed based on the average volume flow model and asperity flattening model,and the lubricant volume flow rate and outlet speed ratio are determined by integrating differential equations based on rolling parameters.The lubrication characteristics at the roll-strip interface with different surface roughness,rolling speed,reduction and lubricant viscosity are analyzed respectively.Additionally,the average volume flow rates of lubricant under different rolling conditions are calculated and used to explain the change rule of lubrication characteristics.The developed scheme is able to determine the total pressure,lubricant pressure,film thickness and real contact area at any point within the work zone.The prediction and analysis of mixed lubrication characteristics at the interface is meaningful to better control the surface quality and optimize the rolling process.

Effects of Corrosion Inhibitors on Lubrication Performance of Rolling Oil for Copper Foil

The 2,5-bis（ethyldisulfanyl）-l,3,4-thiadiazole （T561）, benzotriazole （BTA）,1-N, N-bis （2-ethylhexyl） aminomethyl-4-methyl-lh-benzotriazole （IRGAMET39） and I-IN, N-bis （2-ethylhexyl） aminomethyl] methyl benzotriazole （TT- LX） have been evaluated as corrosion inhibitors used in rolling oil for cold rolling of copper foil. The MRS-10A four-ball friction and wear tests have been carried out to compare their tribological properties, and the lubricating performance of rolling oils has been studied through rolling experiments. The oil sample containing IRGAMET 39 has the same PB value as that one containing T561, with the coefficient of friction increased by 35.6% and wear scar diameter decreased by 4%. The minimum rolling gauge has been studied after rolling lubrication, but the results show that inhibitors have no effect on it. Scanning electron microscopy （SEM） and energy dispersive spectrometry （EDS） analyses have indicated that the inhibitor is adsorbed on the copper surface to prevent copper from being corroded easily. In addition, the LEXT OLS4000 laser confocal microscopy has been used to observe the foil surface which shows that the streaks of foil surface are clear, the scratches are shallow and the surface failure is improved effectively.

Dynamic wetting of rolling oil on aluminum surfaces

Static and dynamic contact angles of stock oil and its solutions with additives（fatty acid, fatty alcohol, fatty methyl ester usually used in rolling aluminum） were measured on aluminum surface （Alloy 1145） by sessile drop technique on an OCA35 dynamic contact angle tester. The effect of additive on the drop spreading was investigated as well. It is shown that the drop spreads very quickly in the first 500 ms after the lubricant contacts with the aluminum surface, and then does slowly later. The dynamic contact angle decreases exponentially with time. In contrast to the stock oil, although addition of polarity additive of long chain alkyl into stock oil is able to decrease the surface tension of solutions, it weakens the wetting dynamic, which results fi＇om the adsorption at the expanding solid/liquid interface. Among the same long chain polarity organic compounds used, dynamic wetting decreases in the order of fatty acid, fatty alcohol and fatty ester. The blend of fatty alcohol and fatty methyl ester can improve the oil wetting dynamics and promote the lubricant spreading.

Research on the Relationship between Molecular Activity of Additives and Lubricating Performance of Aluminum Rolling Oil

In this paper,an ab initio,local density functional(LDF)method was used to explore the relationship between the molecular properties of additives and the lubricating performance of aluminum rolling oil.The structural properties of butyl stearate,dodecanol,docosanol,and methyl dodecanoate were studied according to the density functional theory.The calculated data showed that the atoms in or around the functional groups might be likely the reacting sites.Because of the different functional groups and structure of ester and alcohol,two types of complex additives,dodecanol and butyl stearate,methyl dodecanoate and butyl stearate,respectively,were chosen for studying their tribological properties and performing aluminum cold rolling experiments.The test results agreed with the calculated results very well.The complex ester,viz.methyl dodecanoate and butyl stearate,had the best lubricating performance with a friction coefficient of 0.084 1 and a permissive-rolling thickness of 0.040 mm as compared with that of dodecanol-butyl stearate-base oil formulation.

Die wall lubricated warm compaction behavior of non-lubricant admixed iron powders

The phenomena of die wall lubricated warm compaction of non-lubricant admixed iron powders were researched, and its mechanism of densification was discussed. Water atomized powder obtained from the Wuhan Iron and Steel Corporation was used. With compacting and sintering, compared with cold compaction, the density of warm compacted samples increases by 0.07 - 0. 22 g/cm^3 at the same pressed pressure. The maximum achievable green density of warm compacted samples is 7.12 g/cm^3 at 120℃, and the maximum sintered density is 7.18 g/cm^3 at 80℃. Compared with cold compaction, the ejection force of warm compaction is smaller; the maximum discrep- ancy is about 7 kN. The warm compacted mechanism of densification of iron powders can be obtained： heating the powder contributes to improving plastic deformation of powder particles, and accelerating the mutual filling and rearrangement of powder particles.

Investigation on Relationship between Lubricating Performance and Stability of Emulsion for Cold Strip Rolling

The influence of the ratio and content of emulsifiers on the stability of anion emulsions for cold strip rolling was investigated in this paper. The present study also investigated the effects of HLB （hydrophile-lipophile balance） value and emulsifier content on the stability of no-ionic emulsions. Based on the effects of different stabilities and different concentrations of emulsions on the adsorptivity and friction coefficients, good lubricating performance was obtained when the amount of the separated oil and soap （SOS） accounted for 2.5%. The wearing scar of the steel balls also indicated the improvements in tribological properties after using the emulsion. Thus, the preparation of emulsion should be regulated according to different rolling conditions.

Research on Lubrication Behaviors and Mechanism of Nano-Copper Used in Emulsions for Strip Cold Rolling

In this paper,nano-Cu particles with an average size of smaller than 20 nm were dispersed under ultrasonic agitation in emulsions for cold rolling of steel strips.The tribological properties of the cold rolling emulsion doped with nano-Cu particles were evaluated by using a four-ball machine,and the worn surfaces of the steel balls were checked by an optical microscope.A JC2000C1 wetting angle tester was also applied to study the variation in the emulsion's wetting performance when nano-Cu particles were incorporated.Furthermore,the lubricity of the emulsion doped with nano-Cu for steel strip cold rolling was evaluated on a four-high rolling mill for comparison with the emulsion without using nano-Cu particles.Test results indicated that nano-Cu particles as the additive used in cold rolling emulsion were able to improve the wetting property,friction-reducing,anti-wear,and extreme pressure performance of the base stock significantly.At the same time,nano-Cu particles also showed good lubricity to the cold-rolled steel strips.Namely,the cold-rolled steel strips under the lubrication of the cold rolling emulsion containing nano-Cu particles had considerably decreased the after-rolling thickness and achieved excellent surface quality as well.Finally,the lubrication mechanism of nano-Cu particles in the emulsion for cold rolling of steel strips was discussed.

Friction Characteristics of Space Lubricating Oil No.4129 in Rolling and Sliding Contact

The friction coefficients between the surfaces of a ball and a disc lubricated by a space lubricating oil No.4129 were measured at various operating conditions on a ball-disc friction test rig. Friction characteristic curves were obtained under sliding and rolling movements at point contact. A new model for calculation of the friction coefficient was presented. The results show that the bigger the load is, the larger the friction coefficient becomes. The rolling speed ranging from 1 m/s to10 m/s has an important effect on the friction coefficient. The friction coefficient increases with the increase in sliding speed and the decrease in rolling speed. The linear variation region of the friction coefficient versus the sliding speed at high rolling speed is wider than that at low rolling speed. The model for calculation of the friction coefficient is accurate for engineering use.

Development and Lubricating Properties of Rolling Oil for Stainless Steel Cold Rolling

Appropriate base oils and homologous additives such as extreme pressure and anti-wear agents,oiliness agents and antioxidants were selected,and experiments testing the compatibility performance between additive,base oil and other components were carried out to develop the SK and SD series of rolling oils for cold rolling of stainless steel.The developed oils were used in the stainless steel cold rolling lubrication experiments,and were successfully applied in the actual cold rolling operation of stainless steel.Compared with a foreign product,the tribological properties,the thermal oxidation stability,and the rolling lubrication performance of the developed stainless steel cold rolling oils were studied.Test results showed that the tribological properties of the thereby developed rolling oils and the reference one were almost at the same level,and to some extent the performance of rolling was even better than the foreign product,at the same time the stainless steel sheet could retain its well annealed performance.Meanwhile,within a certain range,the lubrication of the rolling oil became better as its viscosity increased at the same level of saponification value,which could provide a lower friction coefficient,so that a higher maximum reduction ratio of the rolled piece through a constant roll gap and a minimum thickness could be secured.Also,similar phenomena appeared as the saponification value increased at a same viscosity level of the rolling oils.

Scalable preparation of functionalized graphite nanoplatelets via magnetic grinding as lubricity-enhanced additive

Graphite nanoplatelets were prepared by a novel magnetic-grinding method using self-made equipments. Under a variant magnetic field, magnetic needles collided at a high rotating speed and exfoliated pristine graphite into graphite nanoplatelets with high efficiency. The obtained graphite nanoplatelets are highly crystalline, and the thickness is less than 10 nm. Moreover, the surface area could reached 738.1 m^2/g with a grinding time of 4 h. Silanized graphite nanoplatelets can disperse well in SG 15W-40 engine oil and serve as lubricant additive. Tribological results indicate that the friction coefficient and wear-scar of the friction pairs are lower than 76% and 41%, respectively, by adding 1.5‰(mass fraction) of silanized graphite nanoplatelets. Notably, the functionalized graphite nanoplatelets can realize large-scale production and commercial application.

Effects of copper-coated MoS_(2) on friction performance of bronze-graphite-MoS_(2) self-lubricating materials

Two kinds of bronze-graphite-MoS_(2) self-lubricating materials with copper-coated MoS_(2) and uncoated MoS_(2) were prepared by powder metallurgy.Friction and wear experiments were carried out under 4 N and 10 N loads respectively,and the effects of copper-coated MoS_(2) on the friction performances of the materials were studied.Results showed that the way of copper-coated on the surface of MoS_(2) could reinforce the bonding between MoS_(2) and matrix,and inhibited the formation of MoO_(2).Moreover,both materials formed a MoS_(2) lubricating film on the surface during the friction process.While the lubricating film formed after copper coating on MoS_(2) was thicker and had uneven morphology,it was more conducive to improving the friction performance of the material.Compared with conventional materials,the wear rate of copper-coated materials was reduced by one order of magnitude,and the friction coefficient was also reduced by 22.44% and 22.53%,respectively,when sliding under 4 N and 10 N loads.It shows that copper-coated MoS_(2)can improve friction properties of bronze-graphite-MoS_(2)self-lubricating materials furtherly.

Effect of applied load on transition behavior of wear mechanism in Cu-15Ni-8Sn alloy under oil lubrication

Tribological behavior of Cu-15Ni-8Sn(mass fraction, %) alloy against GCr15 ring under various loads was investigated on a ring-on-block tester in oil lubrication. The results showed that the wear rate increased slowly from 1.7×10^(-7) to 9.8× 10^(-7) mm^3/mm under the load lower than 300 N, and then increased dramatically to the climax of 216×10^(-7) mm^3/mm under the load over 300 N, which indicated the transition of wear mechanism with the increase of applied load. The wear mechanism mainly was plastic deformation and abrasive wear under the load less than 300 N. As the applied load was more than 300 N, the wear mechanism of Cu-15Ni-8Sn alloy primarily was delamination wear. Besides, the transition can also be confirmed from the different morphologies of worn surface, subsurface and wear debris. It is distinctly indicated that the appearance of flaky debris at the applied load over 300 N may be a critical point for the change of wear mechanism.

Study on Low-Temperature Traction Behavior of a Space Lubricating Oil No.4116

The traction behavior of space lubricating oil No. 4116 was measured and analyzed at various oil inlet temperatures below 0 ℃ and various rolling speeds under normal loads by a test rig simulating the operating conditions of space bearings. A traction coefficient calculation model was presented. The rheological property and rheological parameters of the lubricant at a low oil inlet temperature were analyzed based on the Tevaarwerk-Johnson model. The results showed that the lubricating oil No. 4116 was sensitive to the rolling speed and had lower sensitivity to the normal load. This lubricating oil is more suitable for applications under high speed when it is used below 0 ℃. It behaves as an elastic-plastic fluid operating below 0 ℃. Both the average limiting shear stress and the average elastic shear modulus have a negative correlation with the rolling speed and oil inlet temperature and have a positive correlation with the normal load.

莱钢1500mm热带轧机工艺润滑系统的开发与应用

介绍了在莱钢集团板带厂1 500 mm热连轧线开发的热轧工艺润滑系统组成及良好的应用效果。应用热轧工艺润滑后,可以降低轧辊磨损20%～40%,轧制力降低10%～20%,轧机主电机电流亦相应降低,实现节能降耗,效益显著;同时改善带钢表面质量,效果明显。另外本系统具有创新点:国内唯一采用喷嘴小孔径技术,吨钢油耗量指标国内领先;在控制系统中设置了独有的喷嘴清洗防堵塞技术。