Using a ball-milling technique,polymorphous iron particles were prepared by changing only the liquid-solid ratioλ.Effects of λon their morphology,structure,conductivity,and electromagnetic properties were studied.Th...Using a ball-milling technique,polymorphous iron particles were prepared by changing only the liquid-solid ratioλ.Effects of λon their morphology,structure,conductivity,and electromagnetic properties were studied.The results show that an increase ofλfrom 0 to 0.25 causes a nonlinear decrease of the conductivity in the ranges of 88.50-2.25 S cm-1 and a regular variation of the electromagnetic parameters,corresponding to the as-obtained iron particles.This is ascribed to a combination of the increased shape anisotropy and the decreased fresh surface with active atoms deriving from the weakened welding-on action and the enhanced micro-malleation action in the ball-milling process.Hereinto,the iron flakes formed at wet-milling with λ=0.08-0.25 have lower conductivity,higher permittivity and permeability,and more excellent absorption property compared with the irregular iron particles obtained at dry-milling withλ=0.It is a consequence of the synergistic effect of dielectric relaxation loss,exchange energy and conductance loss originating from the flake-shape structures.This indicates that the morphology,structure,conductivity,and electromagnetic properties of the products can be effectively controlled by changingλ.展开更多
基金supported in part by Natural Scientific Foundation of Zhejiang Province(Project Nos.Y4100022 and Y4100074)New Bud Talents Grant from Zhejiang Province,Science and Technology Projects from Jinhua City(Grant No.2010A12066)+1 种基金Doctoral Startup Foundation from Zhejiang Normal University(Grant No.ZC304009094)Open Lab Project and the 12th Research Task from Zhejiang Normal University
文摘Using a ball-milling technique,polymorphous iron particles were prepared by changing only the liquid-solid ratioλ.Effects of λon their morphology,structure,conductivity,and electromagnetic properties were studied.The results show that an increase ofλfrom 0 to 0.25 causes a nonlinear decrease of the conductivity in the ranges of 88.50-2.25 S cm-1 and a regular variation of the electromagnetic parameters,corresponding to the as-obtained iron particles.This is ascribed to a combination of the increased shape anisotropy and the decreased fresh surface with active atoms deriving from the weakened welding-on action and the enhanced micro-malleation action in the ball-milling process.Hereinto,the iron flakes formed at wet-milling with λ=0.08-0.25 have lower conductivity,higher permittivity and permeability,and more excellent absorption property compared with the irregular iron particles obtained at dry-milling withλ=0.It is a consequence of the synergistic effect of dielectric relaxation loss,exchange energy and conductance loss originating from the flake-shape structures.This indicates that the morphology,structure,conductivity,and electromagnetic properties of the products can be effectively controlled by changingλ.