The influence of pre-stretching on quench sensitive effect of high strength Al-Zn-Mg-Cu-Zr alloy AA 7085 sheet was investigated by tensile testing at room temperature,transmission electron microscopy(TEM)and different...The influence of pre-stretching on quench sensitive effect of high strength Al-Zn-Mg-Cu-Zr alloy AA 7085 sheet was investigated by tensile testing at room temperature,transmission electron microscopy(TEM)and differential scanning calorimetry(DSC).The water-cooled and aged alloy exhibits higher strength than the air-cooled and aged alloy;2.5%pre-stretching of tensile deformation exerts little effect on strength of water-cooled and aged alloy but increases that of air-cooled and aged one,and therefore the yield strength reduction rate due to slow quenching decreases from about 3.8%to about 1.0%,reducing quench sensitive effect.For the air-cooled alloy,pre-stretching increases the sizes ofη'strengthening precipitates but also increases their quantity and the ratio of diameter to thickness,resulting in enhanced strengthening and higher strength after aging.The reason has been discussed based on microstructure examination by TEM and DSC.展开更多
The fluorescence quenching effect of the conjugated polymers P1 and P2 (the molecular recognitions are twisted 2,2'-bipyridine (bpy) and planar 1,10-phenanthrolin(phen), respectively) films upon the addition of me...The fluorescence quenching effect of the conjugated polymers P1 and P2 (the molecular recognitions are twisted 2,2'-bipyridine (bpy) and planar 1,10-phenanthrolin(phen), respectively) films upon the addition of metal ions has been studied. And the results showed that P2 exhibited stronger fluorescence quenching ability upon the addition of both transition metal ions and main group metal ions compared with that of P1. The 20° twist angle between the two consecutive pyridine rings of bpy unit in the P1 main chain is the reason for the weaker fluorescence quenching ability compared with P2, in which the planar phen unit can chelate with metal ions relatively freely without the conformational transition. So P2 is a kind of material with better properties for solid film devices, such as sensors for metal ions recognition.展开更多
基金Project(AA17202007) supported by the Special Funding for Innovation-Driven Development of Guangxi Province,China。
文摘The influence of pre-stretching on quench sensitive effect of high strength Al-Zn-Mg-Cu-Zr alloy AA 7085 sheet was investigated by tensile testing at room temperature,transmission electron microscopy(TEM)and differential scanning calorimetry(DSC).The water-cooled and aged alloy exhibits higher strength than the air-cooled and aged alloy;2.5%pre-stretching of tensile deformation exerts little effect on strength of water-cooled and aged alloy but increases that of air-cooled and aged one,and therefore the yield strength reduction rate due to slow quenching decreases from about 3.8%to about 1.0%,reducing quench sensitive effect.For the air-cooled alloy,pre-stretching increases the sizes ofη'strengthening precipitates but also increases their quantity and the ratio of diameter to thickness,resulting in enhanced strengthening and higher strength after aging.The reason has been discussed based on microstructure examination by TEM and DSC.
文摘The fluorescence quenching effect of the conjugated polymers P1 and P2 (the molecular recognitions are twisted 2,2'-bipyridine (bpy) and planar 1,10-phenanthrolin(phen), respectively) films upon the addition of metal ions has been studied. And the results showed that P2 exhibited stronger fluorescence quenching ability upon the addition of both transition metal ions and main group metal ions compared with that of P1. The 20° twist angle between the two consecutive pyridine rings of bpy unit in the P1 main chain is the reason for the weaker fluorescence quenching ability compared with P2, in which the planar phen unit can chelate with metal ions relatively freely without the conformational transition. So P2 is a kind of material with better properties for solid film devices, such as sensors for metal ions recognition.