The title compound [N(CH 3) 4] 4 [H 5PMo 5V 9O 42 ] ·3.5H 2O was synthesized by hydrothermal method and its structure was determined with single crystal X ray analysis. The cluster anion is a bicapped Keggin poly...The title compound [N(CH 3) 4] 4 [H 5PMo 5V 9O 42 ] ·3.5H 2O was synthesized by hydrothermal method and its structure was determined with single crystal X ray analysis. The cluster anion is a bicapped Keggin polyanion, two vanadium atoms are distributed at two capping metal atom positions. The crystal is monoclinic, space group C2/c with a=1.284 8(4) nm, b=2.366 4(4) nm, c=2.113 6(4) nm, β= 90.69(2)° , V=6.425(4) nm 3, Z=4, D c=2.07 g\5cm -3 , R=0.066, R w=0.069, S=1.33, \{(Δ/σ) max =\}0 04, \{(Δρ) max =\}91 e·nm -3 .展开更多
A new three-dimensional copper dithiocarbamate-copper iodide coordination polymer [Cu(Me2dtc)2(CuI)3]n (Me2dtc=N,N-dimethyldithiocarbamate) was synthesized by reactions of Cu(OAc)2,NaI and Na(Me2dtc) in DMF solution,c...A new three-dimensional copper dithiocarbamate-copper iodide coordination polymer [Cu(Me2dtc)2(CuI)3]n (Me2dtc=N,N-dimethyldithiocarbamate) was synthesized by reactions of Cu(OAc)2,NaI and Na(Me2dtc) in DMF solution,characterized by elemental analysis,IR spectrum,and single-crystal X-ray diffraction. The crystal belongs to the monoclinic system,space group C2/c with a=1.293 89(17) nm,b=1.077 61(11) nm,c=1.456 05(17) nm,β=115.585 (4)°,V=1.831 1 (4) nm3,Z=4,Dc=3.175 g·cm-3,Mr=875.28,λ (Mo Kα)=0.071 073 nm,μ=10.082 mm-1,F(000)=1 604,the final R=0.029 5 and wR=0.081 7. A total of 2 083 unique reflections were collected,of which 1 918 with I>2σ(I) were observed. The Cu atoms are Cu(Ⅰ)/Cu(Ⅱ) mixed-valence and they have two different coordinate geometries,namely planar square and tetrahedron. This three-dimensional structure consists of individual Cu(Me2dtc)2 molecules linking together CuI polymeric chains which run parallel to the [001] direction vis Cu-S bonds.展开更多
文摘The title compound [N(CH 3) 4] 4 [H 5PMo 5V 9O 42 ] ·3.5H 2O was synthesized by hydrothermal method and its structure was determined with single crystal X ray analysis. The cluster anion is a bicapped Keggin polyanion, two vanadium atoms are distributed at two capping metal atom positions. The crystal is monoclinic, space group C2/c with a=1.284 8(4) nm, b=2.366 4(4) nm, c=2.113 6(4) nm, β= 90.69(2)° , V=6.425(4) nm 3, Z=4, D c=2.07 g\5cm -3 , R=0.066, R w=0.069, S=1.33, \{(Δ/σ) max =\}0 04, \{(Δρ) max =\}91 e·nm -3 .
文摘A new three-dimensional copper dithiocarbamate-copper iodide coordination polymer [Cu(Me2dtc)2(CuI)3]n (Me2dtc=N,N-dimethyldithiocarbamate) was synthesized by reactions of Cu(OAc)2,NaI and Na(Me2dtc) in DMF solution,characterized by elemental analysis,IR spectrum,and single-crystal X-ray diffraction. The crystal belongs to the monoclinic system,space group C2/c with a=1.293 89(17) nm,b=1.077 61(11) nm,c=1.456 05(17) nm,β=115.585 (4)°,V=1.831 1 (4) nm3,Z=4,Dc=3.175 g·cm-3,Mr=875.28,λ (Mo Kα)=0.071 073 nm,μ=10.082 mm-1,F(000)=1 604,the final R=0.029 5 and wR=0.081 7. A total of 2 083 unique reflections were collected,of which 1 918 with I>2σ(I) were observed. The Cu atoms are Cu(Ⅰ)/Cu(Ⅱ) mixed-valence and they have two different coordinate geometries,namely planar square and tetrahedron. This three-dimensional structure consists of individual Cu(Me2dtc)2 molecules linking together CuI polymeric chains which run parallel to the [001] direction vis Cu-S bonds.
文摘以MnO2,Ca(OH)2和La(OH)3为反应原料,在惰性气氛、低温(500℃)熔融KOH体系中合成了具有菱形钙钛矿结构Ca,K共掺杂的La0.64Ca0.25K0.11MnO3纳米材料,并对Mn的价态及磁学性能等进行了讨论.X射线光电子能谱(XPS)分析结果表明,La0.64Ca0.25K0.11MnO3纳米材料中的Mn具有三重混合价态,其零场冷却低温磁化率曲线表现出顺磁-铁磁转变,居里温度(Tc)为280 K.