The response and failure of magnesium alloy AZ31 specimens subjected to different pre-loaded-stress levels and heating rates were investigated with a Gleeble-1500 thermo-mechanical material testing system.It is found ...The response and failure of magnesium alloy AZ31 specimens subjected to different pre-loaded-stress levels and heating rates were investigated with a Gleeble-1500 thermo-mechanical material testing system.It is found that the increases of either pre-loaded stresses or heating-rates decrease the failure temperatures of the specimens.The metallographs of the tested specimens were also observed.It is shown that the high heating-rate may cause stronger local thermal inconsistency,which remarkably increases the microdefects and reduces the macroscopic mechanical properties of the material.展开更多
基金Projects(10872221,50621403)supported by the National Natural Science Foundation of China
文摘The response and failure of magnesium alloy AZ31 specimens subjected to different pre-loaded-stress levels and heating rates were investigated with a Gleeble-1500 thermo-mechanical material testing system.It is found that the increases of either pre-loaded stresses or heating-rates decrease the failure temperatures of the specimens.The metallographs of the tested specimens were also observed.It is shown that the high heating-rate may cause stronger local thermal inconsistency,which remarkably increases the microdefects and reduces the macroscopic mechanical properties of the material.