Ti-47Al-2Nb-2Cr-0.4(W, Mo) (mole fraction, %) alloy ingot fabricated using vacuum consumable melting was containerless near-isothermally forged, and the high temperature forgeability, microstructure and tensile pr...Ti-47Al-2Nb-2Cr-0.4(W, Mo) (mole fraction, %) alloy ingot fabricated using vacuum consumable melting was containerless near-isothermally forged, and the high temperature forgeability, microstructure and tensile properties were investigated. The results show that the TiAl ingot exhibits good heat workability during containerless near-isothermally forging process, and there are not evident cracks on the surface of as-forged TiAl pancake with a total deformation degree of 60%. The microstructure of the TiAl ingot appears to be typical nearly-lamellar(NL), comprising a great amount of lamellar colonies (α2+γ) and a few equiaxed γ grains. After near-isothermally forging, the as-forged pancake shows primarily fine equiaxed γ grains with an average grain size of 20 μm and some broken lamellar pieces, and some bent lamellas still exist in the hard-deformation zone. Tensile tests at room temperature show that ultimate tensile strength increases from 433 MPa to 573 MPa after forging due to grain refinement effect.展开更多
Based on the EAM potential, a molecular dynamics study on the tensile properties of ultrathin nickel nanowires in the (100〉 orientation with diameters of 3.94, 4.95 and 5.99 nm was presented at different temperature...Based on the EAM potential, a molecular dynamics study on the tensile properties of ultrathin nickel nanowires in the (100〉 orientation with diameters of 3.94, 4.95 and 5.99 nm was presented at different temperatures and strain rates. The temperature and strain rate dependences of tensile properties were investigated. The simulation results show that the elastic modulus and the yield strength are gradually decreasing with the increase of temperature, while with the increase of the strain rate, the stress--strain curves fluctuate more intensely and the ultrathin nickel nanowires rupture at one smaller and smaller strain. At an ideal temperature of 0.01 K, the yield strength of the nanowires drops rapidly with the increase of strain rate, and at other temperatures the strain rate has a little influence on the elastic modulus and the yield strength. Finally, the effects of size on the tensile properties of ultrathin nickel nanowires were briefly discussed.展开更多
The effects of Ca and Sr addition on the microstructure and creep properties of Mg-4Al-2Sn alloys were examined. Tensile tests at 25 ℃ and 200 ℃ and creep tests at 150 ℃ and 200 ℃ were carried out to estimate the ...The effects of Ca and Sr addition on the microstructure and creep properties of Mg-4Al-2Sn alloys were examined. Tensile tests at 25 ℃ and 200 ℃ and creep tests at 150 ℃ and 200 ℃ were carried out to estimate the room temperature and high temperature mechanical properties of these alloys. The microstrueture of the Mg-4Al-2Sn alloy showed dendritic a-Mg, Mg17Al12 and Mg2Sn phases. The latter two phases precipitated along the grain boundaries. The addition of Ca and Sr resulted in the formation of ternary CaMgSn and SrMgSn phases within the grain. The grain size was reduced slightly with the addition of Sr and Ca. The tensile strength was decreased by the addition of Ca and Sr at room temperature. However, the high temperature tensile strength was increased. The creep strength was improved by the addition of Ca and Sr.展开更多
At temperatures ranging from 760 to 1100 °C, the tensile properties of a nickel-based third generation single crystal superalloy DD9 with [100],[120] and [110] orientations were studied. The microstructures and f...At temperatures ranging from 760 to 1100 °C, the tensile properties of a nickel-based third generation single crystal superalloy DD9 with [100],[120] and [110] orientations were studied. The microstructures and fracture surfaces were observed by OM, SEM and TEM. Results show that the tensile strength of [100] specimen is higher than that of [120] and [110] specimens at 760 and 850 °C;while at the temperatures higher than 980 °C, the tensile strength of all specimens has little difference. The fracture mechanisms of [100],[120] and [110] specimens are the same at 760 and 980 °C. At 1100 °C, the fracture surfaces of [100] and [120] specimens are characterized by dimple features;while [110] specimen shows mixed quasi-cleavage and dimple featured fracture surfaces. At 760 °C, obvious superlattice stacking faults (SSFs) are observed only in [100] specimen;while at 1100 °C, the dislocation configurations of all specimens are similar. The difference in the number of potential active slip systems in [100],[120] and [110] specimens during the tensile deformation process is the main reason for the transverse tensile anisotropy.展开更多
High temperature tensile properties and microstructure evolutions of twin-roll-cast AZ31B magnesium alloy were investigated over a strain rate range from 10-3 to 1 s-1.It is suggested that the dominant deformation mec...High temperature tensile properties and microstructure evolutions of twin-roll-cast AZ31B magnesium alloy were investigated over a strain rate range from 10-3 to 1 s-1.It is suggested that the dominant deformation mechanism in the lower strain rate regimes is dislocation creep controlled by grain boundary diffusion at lower temperature and by lattice diffusion at higher temperatures,respectively.Furthermore,dislocation glide and twinning are dominant deformation mechanisms at higher strain-rate.The processing map,the effective diffusion coefficient and activation energy map of the alloy were established.The relations of microstructure evolutions to the transition temperature of dominant diffusion process,the activation energy platform and the occurrence of the full dynamic recrystallization with the maximum peak efficiency were analyzed.It is revealed that the optimum conditions for thermo-mechanical processing of the alloy are at a temperature range from 553 to 593 K,and a strain rate range from 7×10-3 to 2×10-3 s-1.展开更多
Temperature distribution and weld bead profiles of constant current and pulsed current gas tungsten arc welded aluminium alloy joints were compared. The effects of pulsed current welding on tensile properties, hardnes...Temperature distribution and weld bead profiles of constant current and pulsed current gas tungsten arc welded aluminium alloy joints were compared. The effects of pulsed current welding on tensile properties, hardness profiles, microstructural features and residual stress distribution of aluminium alloy joints were reported. The use of pulsed current technique is found to improve the tensile properties of the weld compared with continuous current welding due to grain refinement occurring in the fusion zone.展开更多
The phase precipitation behavior and tensile properties of an as-cast Ni-based alloy,IN617B alloy,after solution heat treatment and long-term aging treatment were investigated.Ti(C,N),M6C and M23C6 are the primary pre...The phase precipitation behavior and tensile properties of an as-cast Ni-based alloy,IN617B alloy,after solution heat treatment and long-term aging treatment were investigated.Ti(C,N),M6C and M23C6 are the primary precipitates in as-cast microstructure.After solution heat treatment,most of carbides dissolve into the matrix except a few fine Ti(C,N)within grains.During long-term aging at 700°C,the phase precipitation behaviors of the alloy are characterized as follows:(1)M23C6 carbides at grain boundaries(GBs)transform from film-like shape to cellular shape and gradually coarsen due to the decrease of the surface energy and element aggregation to GBs;(2)M23C6 carbides within grains have a bar-like morphology with a preferential growth direction[110]and have a cube-on-cube coherent orientation relationship with the matrixγ;(3)γ?particles inhibit the coarsening of M23C6 within grains by constraining the diffusion of formation elements.Furthermore,the tensile strength of the alloy obviously increases,but the ductility significantly decreases after the aging for 5000 h.The alloy has a relatively stable microstructure which guarantees the excellent tensile properties during long-term aging.展开更多
Tensile properties of as-deformed 2A50 aluminum alloy were investigated in the high temperature solid and semi-solid states. The results show that temperature has almost no effect on the maximum tensile stress between...Tensile properties of as-deformed 2A50 aluminum alloy were investigated in the high temperature solid and semi-solid states. The results show that temperature has almost no effect on the maximum tensile stress between 500 ℃ and 530 ℃, and the maximum tensile stress decreases rapidly when the temperature is above 532 ℃. The ductility decreases with increasing temperature and has an obvious fall when the temperature is above solidus temperature. This alloy almost has no ductility above 537 ℃, and cannot sustain tensile stress above 550℃. A brittle temperature range in which this alloy is prone to form microcracks was derived. The relation between microstructure, fraction solid and tensile properties were also investigated by examining the metallograph and fracture surface morphology of tested specimens, which could provide reference for forecasting the microcracks in this alloy occurring in semi-solid processing.展开更多
Co-based superalloys such as FSX-414 have been recently used in gas turbine first stage nozzles. During service, nozzles are exposed to low cycle fatigue, which can lead to cracking of these components. The cracks on ...Co-based superalloys such as FSX-414 have been recently used in gas turbine first stage nozzles. During service, nozzles are exposed to low cycle fatigue, which can lead to cracking of these components. The cracks on these nozzles are usually welded with ttmgsten arc welding (TIG) using Co-based filler metals. In this paper, the effect of TIG on the tensile and low cycle fatigue properties of Co-based superalloy FSX-414 was studied at 950℃. The experimental results show that the yield and ultimate tensile stresses of welded and unwelded specimens are comparable to each other. But toughness of welded specimens is lower than that of unwelded ones. The low cycle fatigue properties of FSX-414 were studied at a strain rate of 3.3×10^-4 s^-1, strain ratio R=-1 (R=emin/emax) and Aet (total strain change) from 0.8% to 2%. In welded specimens, at high strain cycling, the nucleation and growth of cracks occur in the welded zone. But at Aet=0.8%, fracture occurs in the same zones of unwelded specimens. The results show that the total fatigue lives of the welded specimens are shorter than those of unwelded ones. In all of the low cycle fatigue tests, softening phenomena are observed.展开更多
Underwater friction stir welding of 2219 aluminum alloy was carried out in order to further improve the joint performances by varying welding temperature history.The results indicated that the tensile strength of the ...Underwater friction stir welding of 2219 aluminum alloy was carried out in order to further improve the joint performances by varying welding temperature history.The results indicated that the tensile strength of the joint can be improved from 324 MPa by external water cooling action in normal to 341 MPa.However,the plasticity of the joint is deteriorated.The underwater joint tends to fracture at the interface between the weld nugget zone and the thermal mechanically affected zone on the advancing side during tensile test,which is significantly different from the normal joint.展开更多
The aims of the present work are to evaluate the overaging behaviour of the investigated Cu-enriched alloy and to assess its mechanical behaviour,in terms of the tensile and fatigue strength,at room temperature and at...The aims of the present work are to evaluate the overaging behaviour of the investigated Cu-enriched alloy and to assess its mechanical behaviour,in terms of the tensile and fatigue strength,at room temperature and at 200℃,and to correlate the mechanical performance with its microstructure,in particular with the secondary dendrite arm spacing(SDAS).The mechanical tests carried out on the overaged alloy at 200℃ indicate that the addition of about 1.3 wt.%Cu to the A357 alloy enables to maintain ultimate tensile strength and yield strength values close to 210 and 200 MPa,respectively,and fatigue strength at about 100 MPa.Compared to the quaternary(Al−Si−Cu−Mg)alloy C355,the A357−Cu alloy has greater mechanical properties at room temperature and comparable mechanical behaviour in the overaged condition at 200℃.The microstructural analyses highlight that SDAS affects the mechanical behaviour of the peak-aged A357−Cu alloy at room temperature,while its influence is negligible on the tensile and fatigue properties of the overaged alloy at 200℃.展开更多
The structural evolution of dislocation network is closely related to y' rafting and tensile properties. In this work, the effects of strain rate and temperature on the structural evolution of interface dislocatio...The structural evolution of dislocation network is closely related to y' rafting and tensile properties. In this work, the effects of strain rate and temperature on the structural evolution of interface dislocation network in Ni-based superalloys are studied by molecular dynamics simulations. The correlation between the evolution of dislocation network and tensile properties is also explored. The results indicate that the dislocation network shows different degrees of deformation and damage at various strain rates and temperatures. The ),' rafting depends on the damage structure of dislocation network at various strain rates and tem- peratures. Moreover, the tensile properties of interface in Ni-based superalloys are closely related to the evolution of disloca- tion network and dislocation motion mechanisms.展开更多
基金Project (2011CB605505) supported by the National Basic Research Program of ChinaProject (2008AA03A233) supported by the National High-Tech Research and Development Program of China
文摘Ti-47Al-2Nb-2Cr-0.4(W, Mo) (mole fraction, %) alloy ingot fabricated using vacuum consumable melting was containerless near-isothermally forged, and the high temperature forgeability, microstructure and tensile properties were investigated. The results show that the TiAl ingot exhibits good heat workability during containerless near-isothermally forging process, and there are not evident cracks on the surface of as-forged TiAl pancake with a total deformation degree of 60%. The microstructure of the TiAl ingot appears to be typical nearly-lamellar(NL), comprising a great amount of lamellar colonies (α2+γ) and a few equiaxed γ grains. After near-isothermally forging, the as-forged pancake shows primarily fine equiaxed γ grains with an average grain size of 20 μm and some broken lamellar pieces, and some bent lamellas still exist in the hard-deformation zone. Tensile tests at room temperature show that ultimate tensile strength increases from 433 MPa to 573 MPa after forging due to grain refinement effect.
基金Project(51205302)supported by the National Natural Science Foundation of ChinaProject(2013JM7017)supported by the Natural Science Basic Research Plan in Shanxi Province of ChinaProject(K5051304006)supported by the Fundamental Research Funds for the Central Universities,China
文摘Based on the EAM potential, a molecular dynamics study on the tensile properties of ultrathin nickel nanowires in the (100〉 orientation with diameters of 3.94, 4.95 and 5.99 nm was presented at different temperatures and strain rates. The temperature and strain rate dependences of tensile properties were investigated. The simulation results show that the elastic modulus and the yield strength are gradually decreasing with the increase of temperature, while with the increase of the strain rate, the stress--strain curves fluctuate more intensely and the ultrathin nickel nanowires rupture at one smaller and smaller strain. At an ideal temperature of 0.01 K, the yield strength of the nanowires drops rapidly with the increase of strain rate, and at other temperatures the strain rate has a little influence on the elastic modulus and the yield strength. Finally, the effects of size on the tensile properties of ultrathin nickel nanowires were briefly discussed.
基金supported by a grant from the Metals Bank by the Ministry of Knowledge Economy and a grant-in-aid for the National Core Research Center Program (No.R15-2006-022-02001-0)
文摘The effects of Ca and Sr addition on the microstructure and creep properties of Mg-4Al-2Sn alloys were examined. Tensile tests at 25 ℃ and 200 ℃ and creep tests at 150 ℃ and 200 ℃ were carried out to estimate the room temperature and high temperature mechanical properties of these alloys. The microstrueture of the Mg-4Al-2Sn alloy showed dendritic a-Mg, Mg17Al12 and Mg2Sn phases. The latter two phases precipitated along the grain boundaries. The addition of Ca and Sr resulted in the formation of ternary CaMgSn and SrMgSn phases within the grain. The grain size was reduced slightly with the addition of Sr and Ca. The tensile strength was decreased by the addition of Ca and Sr at room temperature. However, the high temperature tensile strength was increased. The creep strength was improved by the addition of Ca and Sr.
文摘At temperatures ranging from 760 to 1100 °C, the tensile properties of a nickel-based third generation single crystal superalloy DD9 with [100],[120] and [110] orientations were studied. The microstructures and fracture surfaces were observed by OM, SEM and TEM. Results show that the tensile strength of [100] specimen is higher than that of [120] and [110] specimens at 760 and 850 °C;while at the temperatures higher than 980 °C, the tensile strength of all specimens has little difference. The fracture mechanisms of [100],[120] and [110] specimens are the same at 760 and 980 °C. At 1100 °C, the fracture surfaces of [100] and [120] specimens are characterized by dimple features;while [110] specimen shows mixed quasi-cleavage and dimple featured fracture surfaces. At 760 °C, obvious superlattice stacking faults (SSFs) are observed only in [100] specimen;while at 1100 °C, the dislocation configurations of all specimens are similar. The difference in the number of potential active slip systems in [100],[120] and [110] specimens during the tensile deformation process is the main reason for the transverse tensile anisotropy.
基金Project(3093024) supported by the Natural Science Foundation of Beijing, China Project(2007XM035) supported by the Science Foundation of Beijing Jiaotong University
文摘High temperature tensile properties and microstructure evolutions of twin-roll-cast AZ31B magnesium alloy were investigated over a strain rate range from 10-3 to 1 s-1.It is suggested that the dominant deformation mechanism in the lower strain rate regimes is dislocation creep controlled by grain boundary diffusion at lower temperature and by lattice diffusion at higher temperatures,respectively.Furthermore,dislocation glide and twinning are dominant deformation mechanisms at higher strain-rate.The processing map,the effective diffusion coefficient and activation energy map of the alloy were established.The relations of microstructure evolutions to the transition temperature of dominant diffusion process,the activation energy platform and the occurrence of the full dynamic recrystallization with the maximum peak efficiency were analyzed.It is revealed that the optimum conditions for thermo-mechanical processing of the alloy are at a temperature range from 553 to 593 K,and a strain rate range from 7×10-3 to 2×10-3 s-1.
文摘Temperature distribution and weld bead profiles of constant current and pulsed current gas tungsten arc welded aluminium alloy joints were compared. The effects of pulsed current welding on tensile properties, hardness profiles, microstructural features and residual stress distribution of aluminium alloy joints were reported. The use of pulsed current technique is found to improve the tensile properties of the weld compared with continuous current welding due to grain refinement occurring in the fusion zone.
基金Project(51571191)supported by the National Natural Science Foundation of ChinaProject(NY 20150102)supported by the National Energy Administration Program of China
文摘The phase precipitation behavior and tensile properties of an as-cast Ni-based alloy,IN617B alloy,after solution heat treatment and long-term aging treatment were investigated.Ti(C,N),M6C and M23C6 are the primary precipitates in as-cast microstructure.After solution heat treatment,most of carbides dissolve into the matrix except a few fine Ti(C,N)within grains.During long-term aging at 700°C,the phase precipitation behaviors of the alloy are characterized as follows:(1)M23C6 carbides at grain boundaries(GBs)transform from film-like shape to cellular shape and gradually coarsen due to the decrease of the surface energy and element aggregation to GBs;(2)M23C6 carbides within grains have a bar-like morphology with a preferential growth direction[110]and have a cube-on-cube coherent orientation relationship with the matrixγ;(3)γ?particles inhibit the coarsening of M23C6 within grains by constraining the diffusion of formation elements.Furthermore,the tensile strength of the alloy obviously increases,but the ductility significantly decreases after the aging for 5000 h.The alloy has a relatively stable microstructure which guarantees the excellent tensile properties during long-term aging.
基金Projects(50774026, 50875059) supported by the National Natural Science Foundation of ChinaProject(20070420023) supported by the China Postdoctoral Science FoundationProject(2008AA03A239) supported by the National High-tech Research and Development Program of China
文摘Tensile properties of as-deformed 2A50 aluminum alloy were investigated in the high temperature solid and semi-solid states. The results show that temperature has almost no effect on the maximum tensile stress between 500 ℃ and 530 ℃, and the maximum tensile stress decreases rapidly when the temperature is above 532 ℃. The ductility decreases with increasing temperature and has an obvious fall when the temperature is above solidus temperature. This alloy almost has no ductility above 537 ℃, and cannot sustain tensile stress above 550℃. A brittle temperature range in which this alloy is prone to form microcracks was derived. The relation between microstructure, fraction solid and tensile properties were also investigated by examining the metallograph and fracture surface morphology of tested specimens, which could provide reference for forecasting the microcracks in this alloy occurring in semi-solid processing.
文摘Co-based superalloys such as FSX-414 have been recently used in gas turbine first stage nozzles. During service, nozzles are exposed to low cycle fatigue, which can lead to cracking of these components. The cracks on these nozzles are usually welded with ttmgsten arc welding (TIG) using Co-based filler metals. In this paper, the effect of TIG on the tensile and low cycle fatigue properties of Co-based superalloy FSX-414 was studied at 950℃. The experimental results show that the yield and ultimate tensile stresses of welded and unwelded specimens are comparable to each other. But toughness of welded specimens is lower than that of unwelded ones. The low cycle fatigue properties of FSX-414 were studied at a strain rate of 3.3×10^-4 s^-1, strain ratio R=-1 (R=emin/emax) and Aet (total strain change) from 0.8% to 2%. In welded specimens, at high strain cycling, the nucleation and growth of cracks occur in the welded zone. But at Aet=0.8%, fracture occurs in the same zones of unwelded specimens. The results show that the total fatigue lives of the welded specimens are shorter than those of unwelded ones. In all of the low cycle fatigue tests, softening phenomena are observed.
基金Project (2010CB731704) supported by the National Basic Research Program of ChinaProject (2006BAF04B09) supported by the NationalKey Technology Research and Development Program of ChinaProject supported by the Program of Excellent Team in Harbin Instituteof Technology,China
文摘Underwater friction stir welding of 2219 aluminum alloy was carried out in order to further improve the joint performances by varying welding temperature history.The results indicated that the tensile strength of the joint can be improved from 324 MPa by external water cooling action in normal to 341 MPa.However,the plasticity of the joint is deteriorated.The underwater joint tends to fracture at the interface between the weld nugget zone and the thermal mechanically affected zone on the advancing side during tensile test,which is significantly different from the normal joint.
文摘The aims of the present work are to evaluate the overaging behaviour of the investigated Cu-enriched alloy and to assess its mechanical behaviour,in terms of the tensile and fatigue strength,at room temperature and at 200℃,and to correlate the mechanical performance with its microstructure,in particular with the secondary dendrite arm spacing(SDAS).The mechanical tests carried out on the overaged alloy at 200℃ indicate that the addition of about 1.3 wt.%Cu to the A357 alloy enables to maintain ultimate tensile strength and yield strength values close to 210 and 200 MPa,respectively,and fatigue strength at about 100 MPa.Compared to the quaternary(Al−Si−Cu−Mg)alloy C355,the A357−Cu alloy has greater mechanical properties at room temperature and comparable mechanical behaviour in the overaged condition at 200℃.The microstructural analyses highlight that SDAS affects the mechanical behaviour of the peak-aged A357−Cu alloy at room temperature,while its influence is negligible on the tensile and fatigue properties of the overaged alloy at 200℃.
基金supported by the National Natural Science Foundation of China (Grant Nos. 11072026 and 11102139)the Fundamental Research Funds for the Central Universities (Grant No. 2009JBZ015)China Postdoctoral Science Foundation (Grant No. 20110491205)
文摘The structural evolution of dislocation network is closely related to y' rafting and tensile properties. In this work, the effects of strain rate and temperature on the structural evolution of interface dislocation network in Ni-based superalloys are studied by molecular dynamics simulations. The correlation between the evolution of dislocation network and tensile properties is also explored. The results indicate that the dislocation network shows different degrees of deformation and damage at various strain rates and temperatures. The ),' rafting depends on the damage structure of dislocation network at various strain rates and tem- peratures. Moreover, the tensile properties of interface in Ni-based superalloys are closely related to the evolution of disloca- tion network and dislocation motion mechanisms.