The Li3V2（PO4）3/C composite cathode material was synthesized via sol-gel method using three different chelating agents （citric acid, salicylic acid and polyacrylic acid） at pH value of 3 or 7. The crystal structur...The Li3V2（PO4）3/C composite cathode material was synthesized via sol-gel method using three different chelating agents （citric acid, salicylic acid and polyacrylic acid） at pH value of 3 or 7. The crystal structure, morphology, specific surface area and electrochemical performance of the prepared samples were investigated by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, cyclic voltammetry （CV）, electrochemical impedance spectroscopy （EIS） and galvanostatic charge/discharge test. The results show that the effects of pH value on the performance of the prepared materials are greatly related to the chelating agents. With salicylic acid or polyacrylic acid as the chelating reagent, the structure, morphology and electrochemical performance of the samples are greatly influenced by the pH values. However, the structure of the materials with citric acid as the chelating agent does not change as pH value changes, and the materials own uniform particle size distribution and good electrochemical performance. It delivers an initial discharge capacity of 113.58 mA·h/g at 10C, remaining as high as 108.48 mA·h/g after 900 cycles, with a capacity retention of 95.51%.展开更多
The solvent extraction technology, was applied to recover Cu^2＋ and Ni^2＋ from plating wastewater.Lix984N was chosen as the extractant due to-its gooff extraction performance. The influence parame-ters were examlned...The solvent extraction technology, was applied to recover Cu^2＋ and Ni^2＋ from plating wastewater.Lix984N was chosen as the extractant due to-its gooff extraction performance. The influence parame-ters were examlned. The results show that the separation of Cu^2＋ and Ni＂ from sulphate medium can be realized by adjusting pH value with the help of Lix984N. For extracting Cu^2＋ and Ni^2＋, the optimal pH values are 4 and 10.5, and the maximal extraction percentages are 92.9% and 93.0%, respectively .With recovered Cu^2＋ and Ni^2＋ stripped in 170g.L^ -1 and 200 g.L^-1 H2SO4 medium, the stripping percentages of Cu^2＋ and Ni^2＋ are 92.9% and 93.0%, respectively. This method is simple and can be used to recover Cu^2＋ and Ni^2＋ from plating wastewater. And a flow sheet for separation of Cu^2＋ and Ni^2＋ is presented.展开更多
Extraction of copper and ammonia from Cu2+-NH3-Cl--H2O solution using laboratorialy synthesized sterically hindered β-diketone(4,4-dimethyl-1-(4-dodecylphenyl)-1,3-pentanedione) was studied.The effects of the copper ...Extraction of copper and ammonia from Cu2+-NH3-Cl--H2O solution using laboratorialy synthesized sterically hindered β-diketone(4,4-dimethyl-1-(4-dodecylphenyl)-1,3-pentanedione) was studied.The effects of the copper concentration,the total ammonia concentration,the initial pH in the aqueous phase,the phase ratio,and the temperature on copper extraction ratio and ammonia extraction in loaded organic phase were investigated using this sterically hindered β-diketone.Under the conditions of temperature 25℃,contact time of two phases 30 min,phase ratio 1-1,concentration of copper 3 g/L,concentration of total ammonia 3 mol/L,aqueous pH 8.43,and the concentration of β-diketone in organic phase 20%(volume fraction),ammonia in aqueous phase is much lower to be extracted by organic phase(just 14.5 mg/L),while the extraction rate of copper is 95.09%.展开更多
The present work is concerned with the voltammetric application of unmodified tricresyl phosphate carbon paste electrode （TCP-CPE） and in situ bismuth-film modified tricresyl phosphate-based carbon paste electrode ...The present work is concerned with the voltammetric application of unmodified tricresyl phosphate carbon paste electrode （TCP-CPE） and in situ bismuth-film modified tricresyl phosphate-based carbon paste electrode （BiF-TCP-CPE）. The TCP-CPE was examined with the main objective of using it for the differential pulse voltammetric analysis of some neonicotinoid insecticides in aqueous Britton-Robinson buffer solution pH 7.0 as supporting electrolyte. After comparing the performance of the TCP-CPE with that of silicone oil carbon paste electrode, quantitative analysis of imidacloprid, thiamethoxam and clothianidin was performed in model solutions and real samples （river water and commercial insecticide formulations）. The in situ prepared BiF-TCP-CPE was tested for a simultaneous detection of selected heavy metal ions （Cd^2＋ and Pb^2＋） at a μg/dm^3 concentration level, using square wave anodic stripping voltammetric technique. The influence of different electrochemical pretreatments of the working electrode on the bismuth deposition and analyte signals were investigated. Film formation was studied at untreated, pre-cathodized and pre-anodized TCP-CPEs in the acetic buffer solution pH 4.6, containing 1 μg/cm^3 Bi （III）.展开更多
基金Project(2007BAQ01055)supported by the National Key Technology R&D Program of ChinaProject(2011SCU11081)supported by the Sichuan University Funds for Young Scientists,ChinaProject(20120181120103)supported by Ph.D.Programs Foundation of the Ministry of Education of China
文摘The Li3V2（PO4）3/C composite cathode material was synthesized via sol-gel method using three different chelating agents （citric acid, salicylic acid and polyacrylic acid） at pH value of 3 or 7. The crystal structure, morphology, specific surface area and electrochemical performance of the prepared samples were investigated by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, cyclic voltammetry （CV）, electrochemical impedance spectroscopy （EIS） and galvanostatic charge/discharge test. The results show that the effects of pH value on the performance of the prepared materials are greatly related to the chelating agents. With salicylic acid or polyacrylic acid as the chelating reagent, the structure, morphology and electrochemical performance of the samples are greatly influenced by the pH values. However, the structure of the materials with citric acid as the chelating agent does not change as pH value changes, and the materials own uniform particle size distribution and good electrochemical performance. It delivers an initial discharge capacity of 113.58 mA·h/g at 10C, remaining as high as 108.48 mA·h/g after 900 cycles, with a capacity retention of 95.51%.
基金Supported by the National Key Technologies Research and Development Program of China during the 1 lth Five-Year Plan Period （2007BAB22B01） and the Young Science Foundation of Jiangxi Province Education Office （GJJ11124）.
文摘The solvent extraction technology, was applied to recover Cu^2＋ and Ni^2＋ from plating wastewater.Lix984N was chosen as the extractant due to-its gooff extraction performance. The influence parame-ters were examlned. The results show that the separation of Cu^2＋ and Ni＂ from sulphate medium can be realized by adjusting pH value with the help of Lix984N. For extracting Cu^2＋ and Ni^2＋, the optimal pH values are 4 and 10.5, and the maximal extraction percentages are 92.9% and 93.0%, respectively .With recovered Cu^2＋ and Ni^2＋ stripped in 170g.L^ -1 and 200 g.L^-1 H2SO4 medium, the stripping percentages of Cu^2＋ and Ni^2＋ are 92.9% and 93.0%, respectively. This method is simple and can be used to recover Cu^2＋ and Ni^2＋ from plating wastewater. And a flow sheet for separation of Cu^2＋ and Ni^2＋ is presented.
基金Project(2007CB613601) supported by the National Basic Research Program of ChinaProject(NCET-08) supported by Program for New Century Excellent Talents in University, China
文摘Extraction of copper and ammonia from Cu2+-NH3-Cl--H2O solution using laboratorialy synthesized sterically hindered β-diketone(4,4-dimethyl-1-(4-dodecylphenyl)-1,3-pentanedione) was studied.The effects of the copper concentration,the total ammonia concentration,the initial pH in the aqueous phase,the phase ratio,and the temperature on copper extraction ratio and ammonia extraction in loaded organic phase were investigated using this sterically hindered β-diketone.Under the conditions of temperature 25℃,contact time of two phases 30 min,phase ratio 1-1,concentration of copper 3 g/L,concentration of total ammonia 3 mol/L,aqueous pH 8.43,and the concentration of β-diketone in organic phase 20%(volume fraction),ammonia in aqueous phase is much lower to be extracted by organic phase(just 14.5 mg/L),while the extraction rate of copper is 95.09%.
文摘The present work is concerned with the voltammetric application of unmodified tricresyl phosphate carbon paste electrode （TCP-CPE） and in situ bismuth-film modified tricresyl phosphate-based carbon paste electrode （BiF-TCP-CPE）. The TCP-CPE was examined with the main objective of using it for the differential pulse voltammetric analysis of some neonicotinoid insecticides in aqueous Britton-Robinson buffer solution pH 7.0 as supporting electrolyte. After comparing the performance of the TCP-CPE with that of silicone oil carbon paste electrode, quantitative analysis of imidacloprid, thiamethoxam and clothianidin was performed in model solutions and real samples （river water and commercial insecticide formulations）. The in situ prepared BiF-TCP-CPE was tested for a simultaneous detection of selected heavy metal ions （Cd^2＋ and Pb^2＋） at a μg/dm^3 concentration level, using square wave anodic stripping voltammetric technique. The influence of different electrochemical pretreatments of the working electrode on the bismuth deposition and analyte signals were investigated. Film formation was studied at untreated, pre-cathodized and pre-anodized TCP-CPEs in the acetic buffer solution pH 4.6, containing 1 μg/cm^3 Bi （III）.